Adhesive strength of the coating significantly affects the lifetime of the coating. However, it is still inevitable for the coating, even with strong adhesive strength, to peel off from the substrate after working for a while. In this work, fatigue and wear behaviors were employed to analyze the effect on the mechanics of coating and contribute to a fundamental understanding of peeling of the coating. A small-size Co-cemented tungsten carbide drill bit was selected as the examined substrate to fabricate the diamond coating. Roughening pretreatment with a diamond slurry combined with ultrasonic vibration was performed for the substrate surface to enhance adhesive strength. Meanwhile, a diamond coating without roughening pretreatment was also fabricated for comparison. The lifetime and quality of the coating were evaluated by the drilling test. Although the diamond coating could grow on the substrates with and without roughening pretreatment, the diamond coating with roughening pretreatment possessed a higher lifetime and stronger wear resistance than that without roughening pretreatment. We found that both substrates with and without roughening pretreatment exhibited a coarse surface, whereas the roughening pretreatment could remove the original machined surface of the substrate and thus make the near surface with numerous integrated crystalline grains become the new topmost surface. This increased the contact area and surface energy of the interface, leading to the improvement of adhesive strength. Finally, fatigue strength and contact mechanics were studied to trace the changes in the stress of the diamond coating in the whole process of drilling from a theoretical point of view. We suggest that fatigue strength and contact mechanics may play vital roles on the durability and peeling of the coating.
Influence of Adhesive Strength, Fatigue Strength and Contact Mechanics on the Drilling Performance of Diamond Coating