Macrostructure, microstructure and mechanical properties evolution during 8Cr4Mo4V steel roller bearing inner ring forging process

2020 ◽  
Vol 798 ◽  
pp. 140196
Author(s):  
Hongwei Jiang ◽  
Yanran Song ◽  
Yucheng Wu ◽  
Debin Shan ◽  
Yingying Zong
Metals ◽  
2020 ◽  
Vol 10 (3) ◽  
pp. 385
Author(s):  
Yushi Qi ◽  
Heng Wang ◽  
Lili Chen ◽  
Hongming Zhang ◽  
Gang Chen ◽  
...  

A ZK61-Y magnesium (Mg) alloy wheel hub was prepared via liquid forging—isothermal forging process. The effects of Y-element contents on the microstructure and mechanical properties of liquid forging blanks were investigated. The formation order of the second phase was I-phase (Mg3Zn6Y) → W-phase (Mg3Zn3Y2) → Z-phase (Mg12ZnY) with the increase of the Y-element content. Meanwhile, the I-phase and Z-phase formed in the liquid forging process were beneficial to the grain refinement. The numerical simulation of the isothermal forging process was carried out to analyze the effects of forming temperature on the temperature and stress field in the forming parts using the software Deform-3D. Isothermal forging experiments and post heat treatments were conducted. The influence of isothermal forging temperature, heat treatment temperature and preservation time on the microstructure and mechanical properties of the forming parts were also studied. The dynamic recrystallization (DRX), second-phase hardening, and work hardening account for the improvement of properties after the isothermal forging process. The forming part forged at 380 °C displayed the outstanding properties. The elongation, yield strength, and ultimate tensile strength were 18.5%, 150 MPa and 315 MPa, respectively. The samples displayed an increased elongation and decreased strength after heat treatments. The 520 °C—1 h sample possessed the best mechanical properties, the elongation was 25.5%, the yield stress was 125 MPa and the ultimate tensile strength was 282 MPa. This can be ascribed to the recrystallization and the elimination of working hardening. Meanwhile, the second phase transformation (I-phase → W-phase → Mg2Y + MgZn2), dissolution, and decomposition can be observed, as well.


2017 ◽  
Vol 898 ◽  
pp. 592-597
Author(s):  
Zhen Qiang Wang ◽  
Bo Long Li ◽  
Tong Bo Wang ◽  
Zuo Ren Nie

A new high-temperature titanium alloy containing erbium was designed and fabricated. The influence of α+β forging process and β forging process on microstructure and mechanical properties of the alloy was studied. The microstructure, mechanical properties and fracture morphologies of the new high-temperature titanium alloy after different forging processes were characterized. The results showed that the forging process significantly affected the microstructure of the alloy. The alloy exhibits nearly equiaxed microstructure and lamellar microstructure after α+β and β forging, respectively. In addition, there were Er-rich phases in both forged alloys. The alloy with nearly equiaxed microstructure acquired a satisfactory comprehensive performance. However, the alloy with lamellar microstructure had higher strength and less plasticity. The tensile fracture of the alloy after α + β forging had more dimples, while cleavage plane was obvious in the alloy after β forging. Owing to the addition of erbium and the formation of Er-rich phases, forged alloys possess excellent strength. The Er-rich phase might be the main reason for the fracture.


2016 ◽  
Vol 850 ◽  
pp. 762-767
Author(s):  
Shun Cheng Wang ◽  
Dong Fu Song ◽  
Jing Xu ◽  
Kai Hong Zheng

In the present investigation the casting-forging integrated technology was adopted to manufacture Al-1.1Mg-0.6Si-0.4Cu alloy automobile brake calipers. The effect of forging pressure on the microstructure and mechanical properties of Al-1.1Mg-0.6Si-0.4Cu alloy calipers were studied. The results showed that the shrinkage porosities and cracks in the Al-1.1Mg-0.6Si-0.4Cu alloy calipers could be removed by the forging process. The ultimate tensile strength and elongation of Al-1.1Mg-0.6Si-0.4Cu alloy calipers increased with the increase of forging pressure. When the forging pressure was 120 MPa, the ultimate tensile strength and elongation of Al-1.1Mg-0.6Si-0.4Cu alloy calipers with T6 heat treatment were 365.3 MPa and 11.5%, which were improved by 22.8% and 38.2%, respectively compared with that of Al-1.1Mg-0.6Si-0.4Cu alloy calipers without forging. The tensile fracture images revealed that the fracture modes of Al-1.1Mg-0.6Si-0.4Cu alloy calipers were more ductile at higher forging pressure.


2010 ◽  
Vol 146-147 ◽  
pp. 1415-1418
Author(s):  
Ronɡ Hua Zhang ◽  
Yon Gan Zhang ◽  
Bao Hong Zhu

In this paper, the Al-8.5Fe-1.3V-1.7Si alloy was fabricated by spray forming and forging processes. The microstructure and mechanical properties of the alloy were investigated by means of metallographic, scanning electron microscope and tensile test. The results indicate that spray formed Al-8.5Fe-1.3V-1.7Si alloy after pressing plus can forging processes displays excellent microstructure and characterization.