Effect of Au/Pd bilayer metallization on solder/Cu interfacial reaction and growth kinetics of Cu Sn intermetallic compounds during solid-state aging

2017 ◽  
Vol 319 ◽  
pp. 55-60 ◽  
Author(s):  
Chien-Lung Liang ◽  
Kwang-Lung Lin ◽  
Po-Jen Cheng
Keyword(s):  
Solid State ◽  
Intermetallic Compounds ◽  
Interfacial Reaction ◽  
Growth Kinetics ◽  
Kinetics Of

Enhanced Growth Kinetics of Intermetallic Compounds between Bi-Containing Sn-3.5Ag Solders and Cu Substrate during Aging

2005 ◽  
Vol 475-479 ◽  
pp. 2627-2630
Author(s):  
Soon Tae Kim ◽  
Joo Youl Huh
Keyword(s):  
Growth Rate ◽  
Intermetallic Compounds ◽  
Solder Alloy ◽  
Interfacial Reaction ◽  
Growth Kinetics ◽  
Cu Substrate ◽  
Reaction Barrier ◽  
Cu3sn Layer ◽  
Cu6sn5 Layer ◽  
Kinetics Of

The effect of adding Bi to a eutectic Sn-3.5Ag solder alloy on the growth kinetics of the intermetallic compounds (IMCs) in solder/Cu joints was examined at the aging temperatures of 130°C, 150°C and 180°C. At 150°C and 180°C, the growth rate of the Cu6Sn5 layer was significantly enhanced, but that of the Cu3Sn layer was rather reduced with increasing Bi content up to 12 wt.%. At 130°C, however, both the η and ε layers appeared to grow faster as the Bi content in the solder was increased to 12 wt.%. These results suggest that the accumulation of Bi ahead of the Cu6Sn5 layers can affect not only the interfacial reaction barrier but also the local thermodynamics at the interface between the Cu6Sn5 layer and the solder.