Keywords: vanadium pentoxide；carbon black；reduction and nitridation；vanadium nitrogen alloy. Abstract. The V2O5 extracted from low vanadium shale and carbon black are used as raw materials to prepare briquetting samples through mixing, grinding and pressing. The samples are prereduced, final reduced and nitrated to produce vanadium nitrogen alloy with high nitrogen content. Thermodynamic analysis and experiment results show that：（1）In order to avoid V2O5 volatilization loss during reduction, the briquetting samples should be pre-reduced for 4 hours below the melting point 670°C of V2O5, which can transform V2O5 into low valence vanadium oxide.（2）During V2O5 being self-reduction under N2 atmosphere, if the final reduction temperature is below 1271°C, the VN is preferential formation; if more than 1271°C, the reduced product forms V4C3.（3）To make a product with high nitrogen and low carbon content, the final reduction and nitride temperature should be controlled below 1300°C.
One-Step Synthesis of Microporous Carbon Monoliths Derived from Biomass with High Nitrogen Doping Content for Highly Selective CO2 Capture