Evaluation of Short Term Creep-Rupture Strength of High Temperature P122 Boiler Material

2003 ◽  
Author(s):  
John Pumwa
Keyword(s):  
High Temperature ◽  
Fracture Mode ◽  
Life Prediction ◽  
Rupture Strength ◽  
Creep Rupture ◽  
Creep Rupture Strength ◽  
Short Term ◽  
Boiler Material ◽  
Term Creep ◽  
Short Term Creep

The complex thermal-mechanical loading of power-generating plant components usually comprises of creep, high-cycle and low-cycle fatigue which are thermally induced by start-ups, load changes and shut-downs, producing instationary temperature gradients and hence creating strain as well as stress fields. In order to select the correct materials for these hostile environmental conditions, it is vitally important to understand the behaviour of mechanical properties such as creep rupture properties of these materials. This paper reports the results of standard creep rupture tests of P122 (HCM12A or 12Cr-1.8W-1.5Cu) high temperature boiler material. P122 is one of the latest developed materials for high temperature environments, which has the potential to be successful in hostile environments. The tests were conducted at temperatures ranging from 550°C to 700°C at 50°C intervals with stress levels ranging from 80–400 MPa using a locally made creep rupture testing machine. The results are found to have stable creep-rupture strength at short term creep stage for over 800-hours at elevated temperatures. Creep life prediction from Larson-Miller relationship was also carried out and the accuracy of life prediction is demonstrated. Moreover, the fracture mode assessments strongly revealed a typical ductile transgranular fracture mode with dimples and voids.

KUBOTA ALLOY KHR35C

Alloy Digest ◽  
1999 ◽  
Vol 48 (7) ◽  
Keyword(s):  
High Temperature ◽  
Physical Properties ◽  
Tensile Properties ◽  
Rupture Strength ◽  
Creep Rupture ◽  
Creep Rupture Strength ◽  
Temperature Performance

Abstract Kubota alloy KHR35C is similar to HP alloy with the addition of niobium to increase its creep-rupture strength. Typical applications include components and assemblies for severe carburizing environments, such as ethylene pyrolysis coils. This datasheet provides information on composition, physical properties, elasticity, and tensile properties as well as creep. It also includes information on high temperature performance as well as casting and joining. Filing Code: SS-753. Producer or source: Kubota Metal Corporation.

A Postassessment Test of 100,000 h Creep Rupture Strength of Grade 91 Steel at 600 °C

2017 ◽  
Vol 139 (5) ◽  
Author(s):  
K. Maruyama ◽  
N. Sekido ◽  
K. Yoshimi
Keyword(s):  
Rupture Strength ◽  
Creep Rupture ◽  
Creep Rupture Strength ◽  
Data Points ◽  
Predicted Values ◽  
Grade 91 ◽  
Term Creep ◽  
Term Data ◽  
Grade 91 Steel

Predictions as to 105 h creep rupture strength of grade 91 steel have been made recently. The predicted values are examined with long-term creep rupture data of the steel. Three creep rupture databases were used in the predictions: data of tube products of grade 91 steel reported in National Institute for Materials Science (NIMS) Creep Data Sheet (NIMS T91 database), data of T91 steel collected in Japan, and data of grade 91 steel collected by an American Society of Mechanical Engineers (ASME) code committee. Short-term creep rupture data points were discarded by the following criteria for minimizing overestimation of the strength: selecting long-term data points with low activation energy (multiregion analysis), selecting data points crept at stresses lower than a half of proof stress (σ0.2/2 criterion), and selecting data points longer than 1000 h (cutoff time of 1000 h). In the case of NIMS T91 database, a time–temperature parameter (TTP) analysis of a dataset selected by multiregion analysis can properly describe the long-term data points and gives the creep rupture strength of 68 MPa at 600 °C. However, TTP analyses of datasets selected by σ0.2/2 criterion and cutoff time of 1000 h from the same database overestimate the data points and predict the strength over 80 MPa. Datasets selected by the same criterion from the three databases provide similar values of the strength. The different criteria for data selection have more substantial effects on predicted values of the strength of the steel than difference of the databases.

scholarly journals Effect of Cobalt and Boron on Long-term Creep Rupture Strength of 12Cr Cast Steels

2010 ◽  
Vol 96 (10) ◽  
pp. 620-628 ◽  
Author(s):  
Masahiko Arai ◽  
Kentaro Asakura ◽  
Hiroyuki Doi ◽  
Hirotsugu Kawanaka ◽  
Toshihiko Koseki ◽  
...  
Keyword(s):  
Rupture Strength ◽  
Creep Rupture ◽  
Creep Rupture Strength ◽  
Cast Steels ◽  
Term Creep

Prediction of Breakdown Transition of Creep Strength in Advanced High Cr Ferritic Steels by Hardness Measurement of Aged Structures at High Temperature

2007 ◽  
Vol 345-346 ◽  
pp. 553-556 ◽  
Author(s):  
Hassan Ghassemi Armaki ◽  
Kouichi Maruyama ◽  
Mitsuru Yoshizawa ◽  
Masaaki Igarashi
Keyword(s):  
Power Plants ◽  
Rupture Strength ◽  
Hardness Measurement ◽  
Creep Rupture ◽  
Ferritic Steels ◽  
Creep Rupture Strength ◽  
Cr Concentration ◽  
Reduction Of Area ◽  
Term Creep

Recent researches have shown the premature breakdown of creep rupture strength in long term creep region of advanced high Cr ferritic steels. As safe operation of power plants becomes a serious problem we should be able to detect and predict the breakdown transition of creep rupture strength. Some methods for detecting the breakdown transition have been presented till now like the measurement of reduction of area after creep rupture and particle size of laves phase. However it will be more economic if we make use of non-destructive tests, for example, hardness testing. In this paper 3 types of ferritic steels with different Cr concentration have been studied. The results suggest that the hardness of aged structures is constant independently of exposure time in short term region, whereas the hardness breaks down in long term region. The boundary of breakdown in hardness coincides with that of breakdown in creep rupture strength.

Progress in the Design of an Improved High-Temperature 1 Percent CrMoV Rotor Steel

1990 ◽  
Vol 112 (1) ◽  
pp. 99-115 ◽  
Author(s):  
R. L. Bodnar ◽  
J. R. Michael ◽  
S. S. Hansen ◽  
R. I. Jaffee
Keyword(s):  
Tensile Strength ◽  
High Temperature ◽  
Room Temperature ◽  
Rupture Strength ◽  
Temper Embrittlement ◽  
Creep Rupture ◽  
Rotor Steel ◽  
Creep Rupture Strength ◽  
Austenitizing Temperature ◽  
Creep Ductility

Silicon-deoxidized, tempered bainitic 1 percent CrMoV steel is currently used extensively for high-temperature steam turbine rotor forgings operating at temperatures up to 565°C due to its excellent creep rupture properties and relative economy. There is impetus to improve the creep rupture strength of this steel while maintaining its current toughness level and vice versa. The excellent creep rupture ductility of the low Si version of this steel allows the use of a higher austenitizing temperature or tensile strength level for improving creep rupture strength without loss in creep ductility or toughness. When the tensile strength of this steel is increased from 785 to 854 MPa, the creep rupture strength exceeds that of the more expensive martensitic 12CrMoVCbN steel currently used for high-temperature rotor applications where additional creep rupture strength is required. The toughness of 1 percent CrMoV steel is improved by lowering the bainite start (Bs) temperature in a “superclean” base composition which is essentially free of Mn, Si, P, S, Sb, As and Sn. The Bs temperature can be lowered through the addition of alloying elements (i.e., C, Ni, Cr, and Mo) and/or increasing the cooling rate from the austenitizing temperature. Using these techniques, the 50 percent FATT can be lowered from approximately 100°C to below room temperature, which provides the opportunity to eliminate the special precautionary procedures currently used in the startup and shutdown of steam turbines. The most promising steels in terms of creep rupture and toughness properties contain 2.5 percent Ni and 0.04 percent Cb (for austenite grain refinement and enhanced tempering resistance). In general, the creep rupture strength of the superclean steels equals or exceeds that of the standard 1 percent CrMoV steel. In addition, the superclean steels have not been found to be susceptible to temper embrittlement, nor do they alter the room temperature fatigue crack propagation characteristics of the standard 1 percent CrMoV steel. These new steels may also find application in combination high-temperature-low-temperature rotors and gas turbine rotors.

Evaluation of Long-Term Creep Strength of Welded Joints of ASME Grades 91, 92 and 122 Type Steels

2012 ◽  
Author(s):  
Masatsugu Yaguchi ◽  
Takuaki Matsumura ◽  
Katsuaki Hoshino
Keyword(s):  
Creep Strength ◽  
Welded Joints ◽  
Rupture Strength ◽  
Reduction Factor ◽  
Creep Rupture ◽  
Creep Rupture Strength ◽  
Strength Reduction Factor ◽  
Rupture Data ◽  
Term Creep

Creep rupture data of welded joints of ASME Grades 91, 92 and 122 type steels have been collected and long-term creep rupture strength of the materials has been evaluated. Similar study was conducted by the SHC Committee in 2004 and 2005, therefore, the evaluation of the creep rupture strength was conducted with emphasis on the long-term creep rupture data obtained after the previous study, in addition to discussion of the effects of product form, welding procedure and test temperature etc. on the creep strength. Almost the same results were obtained on the welded joint of Grade 92 as the previous study, however, the master creep life equations for the welded joints of Grades 91 and 122 were lower than the previous results, especially in the case of Grade 122. Furthermore, the creep strength reduction factor obtained from 100,000 hours creep strength of welded joints and base metal was given as a function of temperature.

Assessment of Creep Rupture Strength for New Martensitic 9% Cr Steels

2007 ◽  
Author(s):  
Walter Bendick ◽  
Jean Gabrel ◽  
Bruno Vandenberghe
Keyword(s):  
Power Plants ◽  
Rupture Strength ◽  
Strength Properties ◽  
Creep Rupture ◽  
Assessment Procedure ◽  
Creep Rupture Strength ◽  
Raw Data ◽  
Cr Steels ◽  
Term Creep

The application of new heat resistant steels in power plants requires reliable long term creep rupture strength values as basis for design. Modern martensitic 9% Cr-steels have complex microstructures that change with service exposure. That is why extrapolations of long term strength properties will be most difficult. Due to new long term test results, re-assessments became necessary for grades 911 and 92. Different methods have been used. Good agreement was obtained between a graphical and the numerical ISO 6303 method. In both cases a two-step assessment procedure was used. First the raw data was prepared in a suitable way, which was followed by mathematical averaging procedures. For comparison a Larson-Miller analysis on the raw data was performed, too. The results turned out to be too optimistic at temperatures higher than 575°C (1050°F). It is shown that a suitable preparation of data can improve the Larson-Miller assessment. As a result of the new assessments the design values had to be reduced for both grades. With respect to previous assessments the new values are up to almost 10% lower. In the case of grade 92 the difference from the former ASME values are even higher. Consequences concerning design and service operation are discussed.

scholarly journals Microstructural Evolution and Short-Term Creep Rupture of the Simulated HAZ in T92 Steel Normalized at Different Temperatures

Metals ◽  
2019 ◽  
Vol 9 (12) ◽  
pp. 1310 ◽  
Author(s):  
Tai-Jung Wu ◽  
Chien-Chun Liao ◽  
Tai-Cheng Chen ◽  
Ren-Kae Shiue ◽  
Leu-Wen Tsay
Keyword(s):  
Grain Boundaries ◽  
Elevated Temperatures ◽  
Creep Rupture ◽  
Infrared Heating ◽  
Short Term ◽  
Creep Tests ◽  
Steel Tubes ◽  
Austenite Grain ◽  
Term Creep ◽  
Short Term Creep

T92 steel tubes have been widely applied in advanced supercritical boilers to replace Gr.91 tubes. Simulated samples with microstructures similar to those present in the heat-affected zone (HAZ) of a T92 steel weld were subjected to short-term creep tests in the study. T92 steel tubes were normalized at either 1213 K (L) or 1333 K (H) for 1 h, followed by tempering (T) at 1033 K for 2 h. After the normalizing and tempering treatments, the HT samples comprised finer precipitates but in greater numbers along the prior austenite grain boundaries (PAGBs) and martensite lath boundaries, as compared with those of the LT samples. The HAZ microstructures in the T92 steel welds were simulated by using an infrared heating system, which included over-tempering (OT, below AC1) and partial transformation (PT, slightly below AC3) zones. Martensite laths in the OT sample were more likely to be replaced by numerous cellular structures or subgrains together with spherodized carbides mainly located at the lath and austenite grain boundaries. Furthermore, coarser but fewer carbides were found along the refined lath and grain boundaries in the PT samples, in comparison with other samples in each group. Short-term creep tests showed that the PT samples were more likely to fracture than other samples in each group. Moreover, under the same testing conditions, the microstructures of T92 steel were more stable and resistant to degradation than those of T91 steel after welding or loading at elevated temperatures. Such events were responsible for higher creep resistance of the simulated T92 samples than that of the simulated T91 samples under the same creep-rupture conditions.