In order to study the microstructure of Fe – Ga alloy, Fe 85 Ga 15 ribbons prepared with different wheel velocity were studied by high resolution X-ray diffraction (HRXRD) and extend X-ray absorption fine structure (EXAFS). HRXRD patterns showed that only disordered A 2 phase was observed in as-cast Fe 85 Ga 15 alloy. A modified- DO 3 phase was detected in all of the melt spun samples. The HRXRD associated with EXAFS results indicated that Ga atoms were located as second-nearest neighbor along [100] orientation. A little DO 3 phase was found in ribbons annealed at 1000°C under 0.06 MPa Ar atmosphere. The result of magnetostriction measurement revealed that in the ribbon prepared with higher wheel velocity, more modified- DO 3 phase will enhance the magnetostriction. DO 3 phase in the annealed sample will deteriorate the magnetostrictive properties of Fe – Ga ribbons.
High-resolution synchrotron radiation X-ray absorption of Si K-edge have been employed to investigate 6H-, 4H- and 3C-SiC. Detailed analyses of the extended x-ray absorption fine structure are taken by using the IFEFFIT program, and significant results on the atomic bonding are obtained from these comparative studies. The x-ray absorption near-edge structures of the Si K-edge are investigated, and the electronic structure of 3C-, 4H- and 6H-SiC are studied. In order to investigate the angular dependence, the x-ray absorption near-edge spectra were operated at 55o and 90o of the angle between the surface and the X-ray direction.
High resolution spectrometer for extended x-ray absorption fine structure measurements in the 6 keV to 15 keV energy range