AbstractA saturable absorber is a building block for integrated ultrafast photonics and passive optical circuits. However, options currently available suffer from the bottlenecks of the necessity for fine control of the material preparation, large optical losses, and compatibility. This paper presents a complementary metal–oxide–semiconductor (CMOS)-compatible alternative based on an epsilon-near-zero (ENZ) medium, in which the real part of the dielectric constant vanishes. Excellent nonlinear optical modulations, including low linear optical losses, low bleaching threshold, moderate optical amplitude modulation, and high modulation speed of indium tin oxide (ITO) in its ENZ region are achieved. The use of ITO as an intracavity saturable absorber for optical switches of integrated waveguide chip lasers at 1.9 μm has been realized. A stable mode-locked waveguide laser with a repetition rate of 6.4 GHz and an average output power of 28.6 mW is achieved via carefully adjusting the intracavity three-surface interferometer (TSI). This work may pave the way for integrated photonics and electro-optics using a CMOS-compatible ENZ medium.

Download Full-text

Synthesis of Photosensitive Organic-Inorganic Hybrid Polymers via Anhydrous Sol-Gel Process for Integrated Optics

MRS Proceedings ◽

10.1557/proc-780-y4.11 ◽

2003 ◽

Vol 780 ◽

Cited By ~ 2

Author(s):

Xinshi Luo ◽

Congji Zha ◽

Barry Luther-Davies

Keyword(s):

Low Cost ◽

Sol Gel ◽

Optical Loss ◽

Hybrid Polymer ◽

Optical Losses ◽

Hybrid Polymers ◽

Inorganic Hybrid ◽

Wide Range ◽

Integrated Optical ◽

Sol Gel Process

AbstractPhotosensitive organic-inorganic hybrid polymers were synthesised for integrated optical and optoelectronic devices by a non-hydrous sol-gel process of hydrolysis/condensation of 3-methacryloxypropyltrimethoxysilane (MPS), diphenyldimethoxysilane (DPhDMS), and zirconium isopropoxide (TPZ) with boric acid under anhydrous conditions. The methacryl groups of MPS are UVpolymerizable, which are suitable for low cost fabrication of waveguides with a “UV write/develop” process. The incorporation of DPhDMS and TPZ was found useful in reducing the optical loss and in enhancing the thermostability of the polymer. The refractive index of the hybrid polymer is tuneable from 1.4950 to 1.5360 by variation of the ratio among MPS, DPhDMS and TPZ. Optical characterisation showed that the material has low optical losses at the telecommunications windows (0.16 dB/cm at 1310 nm and 0.4 dB/cm at 1550nm). The hybrid polymer also showed a low birefringence (1.2×10-4), a large thermo-optic (TO) coefficient (-2.77 ×10-4), and an outstanding linearity of dn/dT in a wide range of temperature (from 25 °C to 200 °C). Waveguides forming ability for the hybrid polymer with UV imprinting was also demonstrated.