MECHANICAL PROPERTIES AND HIGH TEMPERATURE OXIDATION BEHAVIOR OF Ti–Al COATING REINFORCED BY NITRIDES ON Ti–6Al–4V ALLOY

2016 ◽  
Vol 23 (05) ◽  
pp. 1650031
Author(s):  
JINGJIE DAI ◽  
HUIJUN YU ◽  
JIYUN ZHU ◽  
FEI WENG ◽  
CHUANZHONG CHEN
Keyword(s):  
Mechanical Properties ◽  
Titanium Alloy ◽  
High Temperature ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Oxidation Behavior ◽  
Mass Gain ◽  
Temperature Oxidation ◽  
High Temperature Oxidation Behavior ◽  
Al Coating

Ti–Al alloyed coating reinforced by nitrides was fabricated by laser surface alloying technique to improve mechanical properties and high temperature oxidation resistance of Ti–6Al–4V titanium alloy. Microstructures, mechanical properties and high temperature oxidation behavior of the alloyed coating were analyzed. The results show that the alloyed coating consisted of Ti3Al, TiAl2, TiN and Ti2AlN phases. Nitrides with different morphologies were dispersed in the alloyed coating. The maximum microhardness of the alloyed coating was 906[Formula: see text]HV. The friction coefficients of the alloyed coating at room temperature and high temperature were both one-fourth of the substrate. Mass gain of the alloyed coating oxidized at 800[Formula: see text]C for 1000[Formula: see text]h in static air was [Formula: see text][Formula: see text]mg/mm2, which was 1/35th of the substrate. No obvious spallation was observed for the alloyed coating after oxidation. The alloyed coating exhibited excellent mechanical properties and long-term high temperature oxidation resistance, which improved surface properties of Ti–6Al–4V titanium alloy significantly.

High-Temperature Oxidation Behavior of Cu-Si-Y Alloys

2013 ◽  
Vol 32 (4) ◽  
pp. 397-403
Author(s):  
Qun Liu ◽  
Guangyan Fu ◽  
Yong Su ◽  
Zhigang Zhang ◽  
Qi Xiong
Keyword(s):  
Grain Size ◽  
High Temperature ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Oxidation Behavior ◽  
Mass Gain ◽  
Alloying Elements ◽  
Experimental Conditions ◽  
Temperature Oxidation ◽  
High Temperature Oxidation Behavior

AbstractThe effect of rare-earth element Y on high-temperature oxidation behavior of Cu-Si alloys at 973 and 1073 K in 0.1 MPa flowing pure O2 has been investigated. Results show at the two temperatures the mass gain of the alloys with different compositions follows the following sequence, Cu-3Si-1.0Y > Cu-3Si-0Y > Cu-3Si-0.5Y alloy. As the Y content increases, the grain size of the alloys decreases, which accelerates the diffusion rate of the alloying elements in the alloys and oxygen under the experimental conditions, increases the ratio of short-path diffusion, and promotes the formation of SiO2 and Y2O3. The three alloys do not form continuous oxide scales of SiO2 or Y2O3, but their rapid formation and dispersed distribution due to the grain-size reduction may also hinder the diffusion of alloying elements and oxygen, which is beneficial to improve the oxidation resistance of the Y-containing alloys. Thereby, the Cu-3Si-0.5Y alloy has good oxidation resistance. The Cu-3Si-1.0Y alloy exhibits largest mass gain among the three alloys, which is due to the fact that in the alloy with higher Y contend and finer grain size, more amount of Y2O3 is more quickly formed, whose mass occupy a more proportion in the whole mass gain of the alloy.

ENHANCING HIGH-TEMPERATURE OXIDATION RESISTANCE OF TITANIUM ALLOY WITH KF110-B4C-Ag THROUGH LASER TECHNOLOGY

2021 ◽  
Author(s):  
ZHAO ZHANG ◽  
JIANING LI ◽  
ZHIYUN YE ◽  
CAINIAN JING ◽  
MENG WANG ◽  
...  
Keyword(s):  
Titanium Alloy ◽  
High Temperature ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Mass Gain ◽  
Temperature Oxidation ◽  
Laser Technology ◽  
X Ray ◽  
Ta15 Titanium Alloy ◽  
Oxidation Resistant

In this paper, the high-temperature oxidation resistant coating on the TA15 titanium alloy by laser cladding (LC) of the KF110-B4C-Ag mixed powders was analyzed in detail. The scanning electron microscope (SEM) and energy dispersive X-ray spectrometer (EDS) images indicated that a good metallurgy bond between the fabricated coating/TA15 was formed; also the fine/compact microstructure was produced after a cladding process. The oxidation mass gain of TA15 was higher than that of the coating after LC process, which were 3.72 and 0.91[Formula: see text]mg[Formula: see text]cm[Formula: see text], respectively, at 60[Formula: see text]h, greatly enhancing the high temperature oxidation resistance.

scholarly journals High Temperature Oxidation Behavior of Selective Laser Melting Manufactured IN 625

Metals ◽  
2020 ◽  
Vol 10 (5) ◽  
pp. 668 ◽  
Author(s):  
Mihaela Raluca Condruz ◽  
Gheorghe Matache ◽  
Alexandru Paraschiv ◽  
Teodor Badea ◽  
Viorel Badilita
Keyword(s):  
High Temperature ◽  
Oxide Scale ◽  
Selective Laser Melting ◽  
High Temperature Oxidation ◽  
Oxidation Behavior ◽  
Complex Oxide ◽  
Mass Gain ◽  
Laser Melting ◽  
Temperature Oxidation ◽  
High Temperature Oxidation Behavior

The high-temperature oxidation behavior of selective laser melting (SLM) manufactured IN 625 was studied over 96 h of exposure at 900 °C and 1050 °C in air. An extensive analysis was performed to characterize the oxide scale formed and its evolution during the 96 h, including mass gain analysis, EDS, XRD, and morphological analysis of the oxide scale. The mass gain rate of the bare material increases rapidly during the first 8 h of temperature holding and diminishes at higher holding periods for both oxidation temperatures. High-temperature exposure for short periods (24 h) follows a parabolic law and promotes the precipitation of δ phase, Ni-rich intermetallics, and carbides. Within the first 24 h of exposure at 900 °C, a Cr2O3 and a (Ni, Fe)Cr2O4 spinel scale were formed, while at a higher temperature, a more complex oxide was registered, consisting of (Ni, Fe)Cr2O4, Cr2O3, and rutile-type oxides. Prolonged exposure of IN 625 at 900 °C induces the preservation of the Cr2O3 scale and the dissolution of carbides. Other phases and intermetallics, such as γ, δ phases, and MoNi4 are still present. The exposure for 96 h at 1050 °C led to the dissolution of all intermetallics, while the same complex oxide scale was formed.

scholarly journals The Effects of Grain Size and Twins Density on High Temperature Oxidation Behavior of Nickel-Based Superalloy GH738

Materials ◽  
2020 ◽  
Vol 13 (18) ◽  
pp. 4166
Author(s):  
Wenbin Ma ◽  
Hongyun Luo ◽  
Xiaoguang Yang
Keyword(s):  
Grain Size ◽  
High Temperature ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Oxidation Behavior ◽  
Crystal Defects ◽  
Temperature Oxidation ◽  
Nickel Based Superalloy ◽  
High Temperature Oxidation Behavior ◽  
Nano Grains

In the present study, surface treatment techniques such as room temperature machining (RTM) and low temperature burnishing (LTB) processing have been used to improve the microstructure of GH738 superalloy. Nano-grains and nano-twins are obtained on the top surface of RTM and LTB specimens. It is found that although the grain size of RTM and LTB specimens is almost the same, different types of nano-twins have been produced. Moreover, the effect of RTM and LTB processing on high temperature oxidation behavior of nickel-based superalloy GH738 at 700 °C is investigated. The result shows that LTB specimen has the best high temperature oxidation resistance owing to the formation of nano-grains and higher twins density, which induce to form a continuous protective Al2O3 layer at the interface between outer oxide layer and matrix. It is observed that this layer inhibits the inward diffusion of O and outward diffusion of Ti and significantly improves oxidation resistance of LTB specimen. Furthermore, the effects of nano-grains and crystal defects on the diffusion mechanism of elements are clarified during the high temperature oxidation test.

Sign in / Sign up

Export Citation Format

Share Document