scholarly journals Effect of Powder Size on Microstructure and Mechanical Properties of 2A12Al Compacts Fabricated by Hot Isostatic Pressing

2018 ◽  
Vol 2018 ◽  
pp. 1-7 ◽  
Author(s):  
Xina Huang ◽  
Lihui Lang ◽  
Gang Wang ◽  
Sergei Alexandrov
Keyword(s):  
Mechanical Properties ◽  
Alloy Powder ◽  
Powder Compact ◽  
Hot Isostatic Pressing ◽  
Powder Size ◽  
Microstructure And Mechanical Properties ◽  
Powder Particles ◽  
Aluminum Alloy Powder ◽  
Precipitated Phases ◽  
Dense Powder

This paper studied the effects of powder size on densification, microstructure, and mechanical properties of the hot isostatic-pressed 2A12 aluminum alloy powder compact. The results show that the near-fully dense powder compact can be successfully achieved and the smaller the powder is, the higher the relative density is. In addition, as the powder size decreases, the precipitated phases in the powder compact change from continuously point-like distribution at the junctions among powder particles to the concentrated distribution at the three-way intersections. Compared with the large powder, the tensile strength, yield strength, and elongation of the compact with the small powder were improved by 14%, 30.8%, and 48.6%, respectively.

scholarly journals Effect of Sintering Temperature on Microstructure and Mechanical Properties of Hot-Pressed Fe/FeAl2O4 Composite

Crystals ◽  
2021 ◽  
Vol 11 (4) ◽  
pp. 422
Author(s):  
Kuai Zhang ◽  
Yungang Li ◽  
Hongyan Yan ◽  
Chuang Wang ◽  
Hui Li ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Bending Strength ◽  
Sintering Temperature ◽  
Raw Materials ◽  
Hot Press ◽  
Microstructure And Mechanical Properties ◽  
Powder Particles ◽  
Hot Press Sintering ◽  
Sintering Method

An Fe/FeAl2O4 composite was prepared with Fe-Fe2O3-Al2O3 powder by a hot press sintering method. The mass ratio was 6:1:2, sintering pressure was 30 MPa, and holding time was 120 min. The raw materials for the powder particles were respectively 1 µm (Fe), 0.5 µm (Fe2O3), and 1 µm (Al2O3) in diameter. The effect of sintering temperature on the microstructure and mechanical properties of Fe/FeAl2O4 composite was studied. The results showed that Fe/FeAl2O4 composite was formed by in situ reaction at 1300 °C–1500 °C. With the increased sintering temperature, the microstructure and mechanical properties of the Fe/FeAl2O4 composite showed a change law that initially became better and then became worse. The best microstructure and optimal mechanical properties were obtained at 1400 °C. At this temperature, the grain size of Fe and FeAl2O4 phases in Fe/FeAl2O4 composite was uniform, the relative density was 96.7%, and the Vickers hardness and bending strength were 1.88 GPa and 280.0 MPa, respectively. The wettability between Fe and FeAl2O4 was enhanced with increased sintering temperature. And then the densification process was accelerated. Finally, the microstructure and mechanical properties of the Fe/FeAl2O4 composite were improved.

scholarly journals Microstructure and Mechanical Properties of 14Cr-ODS Steels with Zr Addition

2019 ◽  
Vol 38 (2019) ◽  
pp. 404-410 ◽  
Author(s):  
Weijuan Li ◽  
Haijian Xu ◽  
Xiaochun Sha ◽  
Jingsong Meng ◽  
Zhaodong Wang
Keyword(s):  
Mechanical Properties ◽  
Hot Isostatic Pressing ◽  
Oxide Dispersion Strengthened ◽  
Nominal Composition ◽  
Ods Steel ◽  
Zr Addition ◽  
Microstructure And Mechanical Properties ◽  
The Matrix ◽  
Ods Steels ◽  
The Impact

AbstractIn this study, oxide dispersion strengthened (ODS) ferritic steels with nominal composition of Fe–14Cr–2W–0.35Y2O3 (14Cr non Zr-ODS) and Fe–14Cr–2W–0.3Zr–0.35Y2O3 (14Cr–Zr-ODS) were fabricated by mechanical alloying (MA) and hot isostatic pressing (HIP) technique to explore the impact of Zr addition on the microstructure and mechanical properties of 14Cr-ODS steels. Microstructure characterization revealed that Zr addition led to the formation of finer oxides, which was identified as Y4Zr3O12, with denser dispersion in the matrix. The ultimate tensile strength (UTS) of the non Zr-ODS steel is about 1201 MPa, but UTS of the Zr-ODS steel increases to1372 MPa, indicating the enhancement of mechanical properties by Zr addition.