Al3Zr Precipitation Behaviour in a Melt-Spun Al-0.2Cu-1.2Mg-0.5Zr Alloy

Author(s):  
C G Jiao ◽  
M Aindow ◽  
G F Yu ◽  
M G Yan
Author(s):  
L. A. Bendersky ◽  
W. J. Boettinger

Rapid solidification produces a wide variety of sub-micron scale microstructure. Generally, the microstructure depends on the imposed melt undercooling and heat extraction rate. The microstructure can vary strongly not only due to processing parameters changes but also during the process itself, as a result of recalescence. Hence, careful examination of different locations in rapidly solidified products should be performed. Additionally, post-solidification solid-state reactions can alter the microstructure.The objective of the present work is to demonstrate the strong microstructural changes in different regions of melt-spun ribbon for three different alloys. The locations of the analyzed structures were near the wheel side (W) and near the center (C) of the ribbons. The TEM specimens were prepared by selective electropolishing or ion milling.


Author(s):  
G. M. Michal ◽  
T. K. Glasgow ◽  
T. J. Moore

Large additions of B to Fe-Ni alloys can lead to the formation of an amorphous structure, if the alloy is rapidly cooled from the liquid state to room temperature. Isothermal aging of such structures at elevated temperatures causes crystallization to occur. Commonly such crystallization pro ceeds by the nucleation and growth of spherulites which are spherical crystalline bodies of radiating crystal fibers. Spherulite features were found in the present study in a rapidly solidified alloy that was fully crysstalline as-cast. This alloy was part of a program to develop an austenitic steel for elevated temperature applications by strengthening it with TiB2. The alloy contained a relatively large percentage of B, not to induce an amorphous structure, but only as a consequence of trying to obtain a large volume fracture of TiB2 in the completely processed alloy. The observation of spherulitic features in this alloy is described herein. Utilization of the large range of useful magnifications obtainable in a modern TEM, when a suitably thinned foil is available, was a key element in this analysis.


1985 ◽  
Vol 46 (C8) ◽  
pp. C8-533-C8-537
Author(s):  
J. Chevrier ◽  
P. Sainfort ◽  
P. Germi ◽  
D. Pavuna

1988 ◽  
Vol 49 (C8) ◽  
pp. C8-655-C8-656 ◽  
Author(s):  
A. Handstein ◽  
J. Schneider ◽  
U. Heinecke ◽  
R. Grössinger ◽  
H. Sassik

2016 ◽  
pp. 3287-3297
Author(s):  
Tarek El Ashram ◽  
Ana P. Carapeto ◽  
Ana M. Botelho do Rego

Tin-bismuth alloy ribbons were produced using melt-spinning technique. The two main surfaces (in contact with the rotating wheel and exposed to the air) were characterized with Optical Microscopy and AFM, revealing that the surface exposed to the air is duller (due to a long-range heterogeneity) than the opposite surface. Also the XPS chemical composition revealed many differences between them both on the corrosion extension and on the total relative amounts of tin and bismuth. For instance, for the specific case of an alloy with a composition Bi-4 wt % Sn, the XPS atomic ratios Sn/Bi are 1.1 and 3.7 for the surface in contact with the rotating wheel and for the one exposed to air, respectively, showing, additionally, that a large segregation of tin at the surface exists (nominal ratio should be 0.073). This segregation was interpreted as the result of the electrochemical process yielding the corrosion products.


1999 ◽  
Vol 577 ◽  
Author(s):  
A. Gavrin ◽  
C. Sellers ◽  
S.H. Liouw

ABSTRACTWe have used Magnetic Force Microscopy (MFM) to study the magnetic domain structures of melt-spun Nd-Fe-B ribbons. The ribbons are commercial products (Magnequench International, Inc. MQP-B and MQP-B+) with a thickness of approximately 20 microns. These materials have identical composition, Nd12.18B5.36Fe76.99Co5.46, but differ in quenching conditions. In order to study the distribution of domain sizes through the ribbon thickness, we have prepared cross-sectional samples in epoxy mounts. In order to avoid artifacts due to tip-sample interactions, we have used high coercivity CoPt coated MFM tips. Our studies show domain sizes typically ranging from 50-200 nm in diameter. This is in agreement with studies of similar materials in which domains were investigated in the plane of the ribbon. We also find that these products differ substantially in mean domain size and in the uniformity of the domain sizes as measured across the ribbon. While the B+ material shows nearly uniform domain sizes throughout the cross section, the B material shows considerably larger domains on one surface, followed by a region in which the domains are smaller than average. This structure is presumably due to the differing quench conditions. The region of coarse domains varies in thickness, disappearing in some areas, and reaching a maximum thickness of 2.75 µm in others. We also describe bulk magnetic measurements, and suggest that.


2007 ◽  
Vol 141 (3) ◽  
pp. 121-125 ◽  
Author(s):  
L.J. Huang ◽  
G.Y. Liang ◽  
Z.B. Sun ◽  
Y.F. Zhou ◽  
D.C. Wu

2021 ◽  
Vol 62 (9-10) ◽  
pp. 566-571
Author(s):  
A. V. Protasov ◽  
A. G. Popov ◽  
V. S. Gaviko ◽  
P. B. Terent’ev ◽  
Tiangli Zhang