RBS, TEM and SEM Characterization of Gold Nanoclusters in TiO2(110)

2003 ◽  
Vol 792 ◽  
Author(s):  
V. Shutthanandan ◽  
Y. Zhang ◽  
C. M. Wang ◽  
J. S. Young ◽  
L. Saraf ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Room Temperature ◽  
Rutherford Backscattering Spectrometry ◽  
Gold Nanoclusters ◽  
Subsequent Annealing ◽  
Transmission Electron ◽  
Scanning Electron

ABSTRACTNucleation of gold nanoclusters in TiO2(110) single crystal using ion implantation and subsequent annealing were studied by Rutherford backscattering spectrometry /channeling (RBS/C), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Approximately 1000 Au2+/nm2 were implanted at room temperature in TiO2(110) substrates. TEM and SEM measurements reveal that rounded nanoclusters were formed during the implantation. In contrast, subsequent annealing in air for 10 hours at 1275 K promoted the formation of faceted (rectangular shaped) Au nanostructures in TiO2. RBS channeling measurements further reveled that Au atoms randomly occupied the host TiO2 lattice during the implantation. However, it appears that some Au atoms moved to the Ti lattice positions after annealing.

Hydrothermal Synthesis and Characterization of BiFeO3 Polyhedral Crystallites

2012 ◽  
Vol 174-177 ◽  
pp. 508-511
Author(s):  
Lin Lin Yang ◽  
Yong Gang Wang ◽  
Yu Jiang Wang ◽  
Xiao Feng Wang
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Synthesis And Characterization ◽  
X Ray Diffraction ◽  
Xrd Pattern ◽  
X Ray ◽  
Transmission Electron ◽  
Scanning Electron

BiFeO3 polyhedrons had been successfully synthesized via a hydrothermal method. The as-prepared products were characterized by power X-ray diffraction (XRD) pattern, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The possible mechanisms for the formation of BiFeO3 polyhedrons were discussed. Though comparison experiments, it was found that the kind of precursor played a key role on the morphology control of BiFeO3 crystals.

Novel Methods for Preparation and Surface Treatment of Nano-CaCO3

2013 ◽  
Vol 750-752 ◽  
pp. 336-339
Author(s):  
Fa Chao Wu ◽  
Teng Fei Shen
Keyword(s):  
Electron Microscopy ◽  
Heat Treatment ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Particle Size ◽  
Fourier Transform ◽  
Room Temperature ◽  
Transmission Electron ◽  
Reduce Energy Consumption ◽  
Scanning Electron

In this work, CaCO3 nanoparticles have been synthesized via heat-treatment of a new precursor. Effect of calcinations temperature on particle size has been investigated. The products were characterized by Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). nanoCaCO3 was modified using chloroform as solvent and fatty acid as modifier atroom temperature. The advantage of this modification is that it can be proceed at room temperature and it can reduce energy consumption.

Study and characterization of the carbon-based nanoparticles obtained from PET

2013 ◽  
Vol 1549 ◽  
pp. 149-154
Author(s):  
Alena Borisovna Kharissova ◽  
Edgar de Casas Ortiz ◽  
Oxana V. Kharissova ◽  
Ubaldo Ortiz Mendez ◽  
Boris I. Kharisov
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Raman Spectroscopy ◽  
Normal Pressure ◽  
Transmission Electron ◽  
Polymer Type ◽  
Scanning Electron ◽  
Carbon Based

ABSTRACTMaterial like PET {polyethylene terephthalate (C10H8O4)n} are usually thrown away present in glasses of refreshments, water bottles between others which are hard to be degraded. However, this material can be recycled and used to acquire nanostructures. During this investigation the objective was to obtain nanoparticles and carbon based nanostructures from the polymer type PET by means of microwave irradiation at the temperature of 260°C at normal pressure and at 600 psi in the presence of acids, ethylene glycol and by means of calcinations. The obtained nanoparticles of ultrananocrystalline diamonds were studied by means of scanning electron microscopy (SEM), high-resolution transmission electron microscopy (TEM), and Raman spectroscopy.

Fabrication of a vertically aligned carbon nanotube electrode and its modification by nanostructured MnO2 for supercapacitors

2009 ◽  
Vol 81 (12) ◽  
pp. 2317-2325 ◽  
Author(s):  
Wei-De Zhang ◽  
Jin Chen
Keyword(s):  
Electron Microscopy ◽  
Carbon Nanotubes ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Room Temperature ◽  
Transmission Electron ◽  
Multi Walled Carbon Nanotubes ◽  
Vertically Aligned ◽  
Walled Carbon Nanotubes ◽  
Scanning Electron

Strongly bonded arrays of vertically aligned, multi-walled carbon nanotubes (MWNTs) have been successfully grown on Ta foils, and provide a convenient basis for fabricating electrodes with high conductivity and stability. The MWNT arrays were further coated by nanostructured MnO2 through reacting with KMnO4 solution at room temperature. The morphology of the MnO2/MWNT nanocomposite was characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). It was found that the MnO2 is a beehive-like nanostructure that is homogeneously and densely coated on the surface of the MWNTs. The capacitance of the MWNT electrode was significantly increased from 0.14 to 6.81 mF cm–2 after being modified with nanostructured MnO2, that is, the mass-specific capacitance of the bare and MnO2-modified MWNTs was about 33 and 446 F g–1, respectively. The MnO2/MWNT nanocomposite on Ta foils could be potential for developing a supercapacitor.

Growth Mechanism and Characterization of Porous CuS Microspheres

2012 ◽  
Vol 568 ◽  
pp. 348-351
Author(s):  
Shuang Xu ◽  
Nuan Song ◽  
Chang Li Qiu ◽  
Yao Ping Zhang ◽  
Jian Feng Wang
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Growth Mechanism ◽  
Experimental Results ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Scanning Electron

In this paper, a facile method was presented to fabricate CuS porous microspheres, which were formed by the intergrowth of CuS polycrystalline nanoslices. The obtained sample has been characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), selected area electronic diffraction (SAED), and scanning electron microscopy (SEM). On the basis of the experimental results, we proposed a self-assemble mechanism to elucidate the formation of CuS nanoslice structure.

Low-Voltage Scanning Electron Microscopy Investigation of Polymers

1988 ◽  
Vol 46 ◽  
pp. 220-221
Author(s):  
V. K. Berry
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Low Voltage ◽  
Morphological Characterization ◽  
Transmission Electron ◽  
Conducting Materials ◽  
Voltage Scanning ◽  
Scanning Electron

The morphological characterization of any polymer blend plays an important part in the development of a new blend system because the properties of blends are dictated by phase morphology which is dependent upon the chemistry and the processing conditions. Light microscopy, scanning electron microscopy and transmission electron microscopy are the most commonly used microscopical techniques for morphological characterization. Transmission electron microscopy techniques provide the best resolution (≈ 0.3 nm) but are limited in the size of sample area and require elaborate sample preparation procedures. Surface charging and beam damage problems have been some of the drawbacks of conventional scanning electron microscopy with non-conducting materials like polymers.The use of low accelerating voltage scanning electron microscopy (LVSEM) in the characterization of polymers and other non-conducting materials is beginning to be recognized.

A Facile Approach to Synthesis and Modification of Nano-Alumina

2013 ◽  
Vol 774-776 ◽  
pp. 646-649
Author(s):  
Teng Fei Shen ◽  
Ying Juan Sun
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Particle Size ◽  
Fourier Transform ◽  
Room Temperature ◽  
Transmission Electron ◽  
Nano Alumina ◽  
Reduce Energy Consumption ◽  
Scanning Electron

In this work, nanoAlumina particles (nanoAl2O3) have been synthesized via solid state reaction. Effect of quantity of surfactant on particle size has been investigated. nanoAl2O3 was modified using chloroform as solvent and fatty acid as modifier at room temperature. The advantage of this modification is that it can be proceed at room temperature and it can reduce energy consumption. The products were characterized by Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM).