In high-strength steel hot forming, under the heating and quenching interaction, the material is oxidized and de-carbonized in the surface layer, forming a gradual change microstructure composed of ferrite, ferrite and martensite mixture and full martensite layers from surface to interior. The experiment enunciation: Form the table to ferrite, ferrite and martensite hybrid organization, completely martensite gradual change microstructure,and make the strength and rigidity of material one by one in order lower from inside to surface, ductility one by one in order increment in 22MnB5 for hot forming;Changes depends on the hot forming process temperature and the control of reheating furnace gas content protection, when oxygen levels of 5% protective gas, can better prevent oxidation and decarburization;Boron segregation in the grain boundary, solid solution strengthening, is a major cause of strength increase in ;The gradual change microstructure in outer big elongation properties, make the structure of the peak force is relatively flat, to reduce the peak impact force of structure, keep the structure of high energy absorption capacity;With lower temperature, the material yield strength rise rapidly,when the temperature is 650 °C, the yield strength at 950 °C was more than 3 times as much.
Supra-Ductile and High-Strength Manganese-TRIP/TWIP Steels for High Energy Absorption Purposes.