Understanding Water Ingress in Scanning Acoustic Microscopy and a Method to Observe Defects that are Open to the Surface

2019 ◽  
Author(s):  
Adam Benak ◽  
Roger Devaney
Keyword(s):  
Acoustic Microscopy ◽  
Physical Analysis ◽  
Scanning Acoustic Microscopy ◽  
Sound Waves ◽  
Electronic Components ◽  
Water Ingress ◽  
Ultrasonic Sound ◽  
Plastic Components ◽  
Important Test

Abstract Scanning Acoustic Microscopy (SAM) is a very important tool in the evaluation of molded plastic electronic components. SAM is used to non-destructively determine the configuration and quality of components using ultrasonic sound waves and consequently is an important test step in the screening, Destructive Physical Analysis (DPA) or Failure Analysis (FA) of plastic components. SAM is performed in a water bath so if internal defects are open to the surface of the device they can fill with water and become invisible to SAM.

Counterfeit Parts Recognition and Detection for Failure Analysts

2010 ◽  
Author(s):  
Katherine V. Whittington
Keyword(s):  
Thermal Cycle ◽  
Visual Inspection ◽  
Acoustic Microscopy ◽  
Scanning Acoustic Microscopy ◽  
3D Measurement ◽  
X Ray ◽  
Wide Range ◽  
Electronic Parts ◽  
Testing Awareness

Abstract The electronics supply chain is being increasingly infiltrated by non-authentic, counterfeit electronic parts, whose use poses a great risk to the integrity and quality of critical hardware. There is a wide range of counterfeit parts such as leads and body molds. The failure analyst has many tools that can be used to investigate counterfeit parts. The key is to follow an investigative path that makes sense for each scenario. External visual inspection is called for whenever the source of supply is questionable. Other methods include use of solvents, 3D measurement, X-ray fluorescence, C-mode scanning acoustic microscopy, thermal cycle testing, burn-in technique, and electrical testing. Awareness, vigilance, and effective investigations are the best defense against the threat of counterfeit parts.

scholarly journals Possibilities of using scanning acoustic microscopy to analyze incompatibilities in braze welded joints

2019 ◽  
Vol 91 (10) ◽  
pp. 7-15
Author(s):  
Tomasz Piwowarczyk ◽  
Marcin Korzeniowski ◽  
Dawid Majewski
Keyword(s):  
Aluminum Alloys ◽  
Welded Joints ◽  
Acoustic Microscopy ◽  
Scanning Acoustic Microscopy ◽  
Ultrasonic Techniques ◽  
Titanium Grade ◽  
Non Destructive

This article explores the possibilities of using non-destructive ultrasonic techniques to analyze the quality of lapped braze-welded joints. The tests were performed for 4 material groups (DC03+ZE steel and X5CrNi18-19 steel, aluminum alloys AW-5754 and AW-6061, titanium Grade 2 and copper Cu-ETP). As part of the work, additional materials and joint processes and its parameters were selected (TIG, MIG, laser). The quality of joints was monitored using scanning acoustic microscopy. Based on the A-scan andC-scan images, potential joints imperfections were determined. The possibilities of using advanced ultrasonic techniques to analyze the quality of braze joints was assessed.

Imaging of packaging-related problems in electronic components by scanning acoustic microscopy

1989 ◽  
Vol 5 (4) ◽  
pp. 299-307
Author(s):  
K. J. Wilson ◽  
R. R. Sutherland ◽  
I. D. E. Videlo ◽  
B. Wakefield
Keyword(s):  
Acoustic Microscopy ◽  
Scanning Acoustic Microscopy ◽  
Electronic Components

Failure Analysis of Broken Stitch Bonds in TSSOP Packages Using Scanning Acoustic Microscopy (SAM) and Time Domain Reflectometry (TDR)

2004 ◽  
Author(s):  
Bilal Abd-AlRahman ◽  
Corey Lewis ◽  
Todd Simons
Keyword(s):  
Failure Analysis ◽  
Mechanical Stress ◽  
Time Domain ◽  
Open Circuit ◽  
Time Domain Reflectometry ◽  
Acoustic Microscopy ◽  
Scanning Acoustic Microscopy ◽  
Root Cause ◽  
Analysis Application

Abstract A failure analysis application utilizing scanning acoustic microscopy (SAM) and time domain reflectometry (TDR) for failure analysis has been developed to isolate broken stitch bonds in thin shrink small outline package (TSSOP) devices. Open circuit failures have occurred in this package due to excessive bending of the leads during assembly. The tools and their specific application to this technique as well as the limitations of C-SAM, TDR and radiographic analyses are discussed. By coupling C-SAM and TDR, a failure analyst can confidently determine whether the cause of an open circuit in a TSSOP package is located at the stitch bond. The root cause of the failure was determined to be abnormal mechanical stress placed on the pins during the lead forming operation. While C-SAM and TDR had proven useful in the analysis of TSSOP packages, it can potentially be expanded to other wire-bonded packages.

Stacked Die Analysis Using C-mode Scanning Acoustic Microscope

2005 ◽  
Author(s):  
Li Na ◽  
Jawed Khan ◽  
Lonnie Adams
Keyword(s):  
Data Acquisition ◽  
Image Interpretation ◽  
Acoustic Microscopy ◽  
Scanning Acoustic Microscopy ◽  
Acoustic Microscope ◽  
Analysis Mode ◽  
Scanning Acoustic Microscope

Abstract For stacked die package delamination inspection using C-mode acoustic microscope, traditional interface and thorough scan techniques cannot give enough of information when the delamination occurs in multi-interfaces, and echoes from adjacent interfaces are not sufficiently separated from each other. A thinner thickness in the stacked-die package could complicate C-mode scanning acoustic microscopy (CSAM) analysis and sometimes may lead to false interpretations. The first objective of this paper is to briefly explain the CSAM mechanism. Based on that, some of the drawbacks of current settings in detecting the delamination for stacked-die packages are presented. The last objective is to introduce quantitative B-scan analysis mode (Q-BAM) and Zip-Slice technologies in order to better understand and improve the reliability of detecting the delamination in stacked-die packages. Therefore, a large portion of this paper focuses on the Q-BAM and Zip-Slice data acquisition and image interpretation.

Failure and Stress Analysis of Cu TSVs Using GHz-Scanning Acoustic Microscopy and Scanning Infrared Polariscopy

2015 ◽  
Author(s):  
Ingrid De Wolf ◽  
Ahmad Khaled ◽  
Martin Herms ◽  
Matthias Wagner ◽  
Tatjana Djuric ◽  
...  
Keyword(s):  
Failure Analysis ◽  
Stress Analysis ◽  
Rayleigh Waves ◽  
Acoustic Microscopy ◽  
Scanning Acoustic Microscopy ◽  
Through Silicon Vias ◽  
Stress Anisotropy ◽  
Silicon Vias ◽  
Ic Technology ◽  
Detection Of Defects

Abstract This paper discusses the application of two different techniques for failure analysis of Cu through-silicon vias (TSVs), used in 3D stacked-IC technology. The first technique is GHz Scanning Acoustic Microscopy (GHz- SAM), which not only allows detection of defects like voids, cracks and delamination, but also the visualization of Rayleigh waves. GHz-SAM can provide information on voids, delamination and possibly stress near the TSVs. The second is a reflection-based photoelastic technique (SIREX), which is shown to be very sensitive to stress anisotropy in the Si near TSVs and as such also to any defect affecting this stress, such as delamination and large voids.