Influence of Complex SiF62− Ions on the PEO Coatings Formed on Mg–Al6–Zn1 Alloy for Enhanced Wear and Corrosion Protection
The present study was carried out to explore the effect of SiF62− incorporation and concentration on the plasma electrolytic oxidation (PEO) coatings formed on AZ61 Mg alloy. The coatings were prepared using electrolyte solution with various concentration of Na2SiF6 (0.0–0.7 g/L). Highly compact coatings with minimum porosity were obtained for an optimum concentration of Na2SiF6 ~0.3 g/L added into the electrolyte. The highest corrosion resistance, ~2.04 × 105 Ω·cm2, was obtained for 0.3 g/L of Na2SiF6, in addition to its superior anti-wear properties. However, it was found from the scanning electron microscope (SEM) image analysis that increasing concentration above 0.3 g/L, could cause severe breakdown in the inner layers, and thus the said coatings could not withstand effectively against wear and corrosion.