scholarly journals Impact of Temperature on Low-Cycle Fatigue Characteristics of the HR6W Alloy

Materials ◽  
2021 ◽  
Vol 14 (22) ◽  
pp. 6741
Author(s):  
Grzegorz Junak ◽  
Anżelina Marek ◽  
Michał Paduchowicz
Keyword(s):  
Fatigue Life ◽  
Room Temperature ◽  
Low Cycle Fatigue ◽  
Fatigue Tests ◽  
Total Strain ◽  
Cycle Fatigue ◽  
Fatigue Characteristics

This paper presents the results of tests conducted on the HR6W (23Cr-45Ni-6W-Nb-Ti-B) alloy under low-cycle fatigue at room temperature and at 650 °C. Fatigue tests were carried out at constant values of the total strain ranges. The alloy under low-cycle fatigue showed cyclic strengthening both at room temperature and at 650 °C. The degree of HR6W strengthening described by coefficient n’ was higher at higher temperatures. At the same time, its fatigue life Nf at room temperature was, depending on the range of total strain adopted in the tests, several times higher than observed at 650 °C.

High Temperature Low Cycle Fatigue Characteristics of Grit Blasted Polycrystalline Ni-Base Superalloy

2015 ◽  
Vol 665 ◽  
pp. 73-76 ◽  
Author(s):  
Ivo Šulák ◽  
Karel Obrtlík ◽  
Ladislav Čelko
Keyword(s):  
Fatigue Life ◽  
Strain Amplitude ◽  
Low Cycle Fatigue ◽  
Total Strain ◽  
Material Surface ◽  
Total Strain Amplitude ◽  
Cycle Fatigue ◽  
Stress Strain ◽  
Fatigue Characteristics ◽  
Base Superalloy

The present work is focused on the study of low cycle fatigue behavior of grit blasted nickel-base superalloy Inconel 713LC (IN 713LC). Grit blasting parameters are obtained. Button end specimens of IN 713LC in as-received condition and with grit blasted surface were fatigued under strain control with constant total strain amplitude in symmetrical cycle at 900 °C in air. Hardening/softening curves, cyclic stress-strain curve and fatigue life data of both materials were obtained. Both materials exhibit the same stress-strain response. It has not been observed any improvement or reduction of low cycle fatigue life in representation of total strain amplitude versus number of cycles to failure of grit blasted material in comparison with as-received material. Surface relief and fracture surface were observed in SEM. The little effect of surface treatment on fatigue characteristics is discussed.

Low Cycle Fatigue Testing of Ball Grid Array Solder Joints under Mixed-Mode Loading Conditions

2004 ◽  
Vol 127 (3) ◽  
pp. 237-244 ◽  
Author(s):  
Tae-Sang Park ◽  
Soon-Bok Lee
Keyword(s):  
Fatigue Life ◽  
Mixed Mode ◽  
Room Temperature ◽  
Solder Joints ◽  
Low Cycle Fatigue ◽  
Ball Grid Array ◽  
Fatigue Tests ◽  
Test Method ◽  
Cycle Fatigue ◽  
Mixed Mode Loading

To give a proper and accurate estimation of the fatigue life of ball grid array (BGA) solder joints, a mechanical fatigue test method under mixed-mode loading is proposed. Experiments were conducted with 63Sn∕37Pb and Sn∕3.5Ag∕0.75Cu solder joints in room temperature. The mechanical low cycle fatigue tests were performed under several loading angles. The loading angle is controlled by several grips which have specific surface angle to the loading direction. Constant displacement controlled tests are performed using a micro-mechanical test apparatus. It was found that the normal deformation significantly affects the fatigue life of the solder joint. Throughout the whole test conditions at room temperature, Sn∕3.5Ag∕0.75Cu solder alloy had longer fatigue life than 63Sn∕37Pb alloy. Failure patterns of the fatigue tests were observed and discussed. A morrow energy model was examined and found to be a proper low cycle fatigue model for solder joints under mixed mode loading condition.

Low Cycle Fatigue of GX12CrMoVNbN9 -1 Cast Steel at 600°C Temperature

2011 ◽  
Vol 396-398 ◽  
pp. 326-329 ◽  
Author(s):  
Grzegorz Golański ◽  
Krzysztof Werner ◽  
Stanisław Mroziński
Keyword(s):  
Heat Treatment ◽  
Fatigue Life ◽  
Low Cycle Fatigue ◽  
Cast Steel ◽  
Fatigue Tests ◽  
Total Strain ◽  
Cycle Fatigue ◽  
The Given ◽  
Cycles To Failure ◽  
Stabilization Period

The paper treats of the low cycle fatigue (LCF) behaviour of GX12CrMoVNbN9-1 (GP91) cast steel after heat treatment. Fatigue tests at the temperature of 600oC within the scope of small amount of cycles to failure were carried out for five levels of controlled amplitude of total strain εac = 0.25, 0.30, 0.35, 0.50 and 0.60 %. The investigated cast steel within the scope of low cycle fatigue life reveals a three-stage course of changes in strength and strain. In the given scope of low cycle fatigue for GP91 cast steel, cyclic weakening was observed without the occurrence of stabilization period of its properties.

scholarly journals Fatigue Testing of Wearable Sensing Technologies: Issues and Opportunities

Materials ◽  
2021 ◽  
Vol 14 (15) ◽  
pp. 4070
Author(s):  
Andrea Karen Persons ◽  
John E. Ball ◽  
Charles Freeman ◽  
David M. Macias ◽  
Chartrisa LaShan Simpson ◽  
...  
Keyword(s):  
Fatigue Life ◽  
Prediction Models ◽  
Fatigue Testing ◽  
Low Cycle Fatigue ◽  
Wearable Sensors ◽  
Fatigue Tests ◽  
Proof Of Concept ◽  
Cycle Fatigue ◽  
Wearable Sensing ◽  
Failure Data

Standards for the fatigue testing of wearable sensing technologies are lacking. The majority of published fatigue tests for wearable sensors are performed on proof-of-concept stretch sensors fabricated from a variety of materials. Due to their flexibility and stretchability, polymers are often used in the fabrication of wearable sensors. Other materials, including textiles, carbon nanotubes, graphene, and conductive metals or inks, may be used in conjunction with polymers to fabricate wearable sensors. Depending on the combination of the materials used, the fatigue behaviors of wearable sensors can vary. Additionally, fatigue testing methodologies for the sensors also vary, with most tests focusing only on the low-cycle fatigue (LCF) regime, and few sensors are cycled until failure or runout are achieved. Fatigue life predictions of wearable sensors are also lacking. These issues make direct comparisons of wearable sensors difficult. To facilitate direct comparisons of wearable sensors and to move proof-of-concept sensors from “bench to bedside,” fatigue testing standards should be established. Further, both high-cycle fatigue (HCF) and failure data are needed to determine the appropriateness in the use, modification, development, and validation of fatigue life prediction models and to further the understanding of how cracks initiate and propagate in wearable sensing technologies.

LOW CYCLE FATIGUE BEHAVIOR AND LIFE PREDICTION OF A CAST COBALT-BASED SUPERALLOY

2012 ◽  
Vol 06 ◽  
pp. 251-256
Author(s):  
HO-YOUNG YANG ◽  
JAE-HOON KIM ◽  
KEUN-BONG YOO
Keyword(s):  
Fatigue Life ◽  
Strain Energy ◽  
Life Prediction ◽  
Prediction Models ◽  
Low Cycle Fatigue ◽  
Fatigue Behavior ◽  
Total Strain ◽  
Cycle Fatigue ◽  
Total Strain Range ◽  
Different Temperatures

Co -base superalloys have been applied in the stationary components of gas turbine owing to their excellent high temperature properties. Low cycle fatigue data on ECY-768 reported in a companion paper were used to evaluate fatigue life prediction models. In this study, low cycle fatigue tests are performed as the variables of total strain range and temperatures. The relations between plastic and total strain energy densities and number of cycles to failure are examined in order to predict the low cycle fatigue life of Cobalt-based super alloy at different temperatures. The fatigue lives is evaluated using predicted by Coffin-Manson method and strain energy methods is compared with the measured fatigue lives at different temperatures. The microstructure observing was performed for how affect able to low-cycle fatigue life by increasing the temperature.

scholarly journals High-Strength Reinforcing Steel Bars: Low Cycle Fatigue Behavior Using RGB Methodology

2021 ◽  
Vol 15 (1) ◽  
Author(s):  
Jorge E. Egger ◽  
Fabian R. Rojas ◽  
Leonardo M. Massone
Keyword(s):  
Fatigue Life ◽  
Strain Amplitude ◽  
Low Cycle Fatigue ◽  
High Strength ◽  
Image Correlation ◽  
Total Strain ◽  
Total Strain Amplitude ◽  
Reinforcing Steel ◽  
Cycle Fatigue ◽  
Steel Bars

AbstractLow cycle fatigue life of high-strength reinforcing steel bars (ASTM A706 Grade 80), using photogrammetry by RGB methodology is evaluated. Fatigue tests are performed on specimens under constant axial displacement with total strain amplitudes ranging from 0.01 to 0.05. The experimental observations indicate that buckling of high-strength reinforcing bars results in a damaging degradation of their fatigue life performance as the slenderness ratio increases, including an early rebar failure as the total strain amplitude increases since it achieves the plastic range faster. In addition to this, the results show that the ratio of the ultimate tensile strength to yield strength satisfies the minimum of 1.25 specified in ASTM A706 for reinforcement. On the other hand, the RGB methodology indicates that the axial strains measured by photogrammetry provide more accurate data since the registered results by the traditional experimental setup do not detect second-order effects, such as slippage or lengthening of the specimens within the clamps. Moreover, the RGB filter is faster than digital image correlation (DIC) because the RGB methodology requires a fewer computational cost than DIC algorithms. The RGB methodology allows to reduce the total strain amplitude up to 45% compared to the results obtained by the traditional setup. Finally, models relating total strain amplitude with half-cycles to failure and total strain amplitude with total energy dissipated for multiple slenderness ratios (L/d of 5, 10, and 15) are obtained.

Low Cycle Fatigue Properties of FGH720Li Superalloy

2021 ◽  
Vol 1035 ◽  
pp. 292-296
Author(s):  
Zi Chao Peng ◽  
Jun Ying Sheng ◽  
Xu Qing Wang ◽  
Yue Tang
Keyword(s):  
Fatigue Life ◽  
Powder Metallurgy ◽  
Applied Stress ◽  
Low Cycle Fatigue ◽  
Influencing Factor ◽  
Fatigue Tests ◽  
Fatigue Properties ◽  
Nickel Base Superalloy ◽  
Loading Frequency ◽  
Cycle Fatigue

Low cycle fatigue (LCF) properties of a powder metallurgy(PM) nickel base superalloy FGH720Li were systematically studied in this work, including smooth LCF and notched LCF tested at various temperatures and different stress. The relationship between the fatigue life and applied stress was analyzed both for smooth fatigue and notch fatigue tests. The effects of loading frequency and stress ratio on LCF behavior were also studied. As an important influencing factor of the fatigue life in powder metallurgy superalloy, the effect of inclusions on LCF life was also investigated. The results showed that the fatigue properties of FGH720Li alloy was excellent, when tested at the temperature of 450°C and applied stress of 1230MPa, the fatigue life could exceed 5×104 cycles. When tested at 650°C and 1150MPa, the average fatigue life was still beyond 2×105 cycles.

Effect of Surface Finish and Loading Conditions on the Low Cycle Fatigue Life of Stainless Steel Welded Piping in PWR Environment

2013 ◽  
Author(s):  
Yuichi Fukuta ◽  
Yuichiro Nomura ◽  
Seiji Asada
Keyword(s):  
Stainless Steel ◽  
Fatigue Life ◽  
Austenitic Stainless Steel ◽  
Surface Finish ◽  
Loading Condition ◽  
Low Cycle Fatigue ◽  
Complex Loading ◽  
Fatigue Tests ◽  
Cycle Fatigue ◽  
Effect Of Surface

NUREG/CR-6909 of USA and JSME of Japan proposed new rules for evaluating environmental effects in fatigue analyses of reactors components. These rules were established from a lot of fatigue data with polished specimens under simple loading condition. The effects of surface finish or complex loading condition were reported in some papers, but these data were obtained with the simple shaped specimens. In order to evaluate the effects of surface finish and loading condition and to confirm the applicability of the proposed rules to actual components, Low Cycle Fatigue tests are performed in PWR environment with the specimens cut from 316 austenitic stainless steel welded piping. The pipes are machined to have three levels of surface finish condition and the load pattern simulating the thermal stress is applied to specimens. In this study, the effect of surface finish on fatigue life is included to be small for 316 austenitic stainless steel welded piping. Considering the insensitive region in the current evaluation rule, predicted accuracy is increased and possibility of improving the current rule is indicated.

Low Cycle Fatigue of Nuclear Pipe Components

1974 ◽  
Vol 96 (3) ◽  
pp. 171-176 ◽  
Author(s):  
J. D. Heald ◽  
E. Kiss
Keyword(s):  
Stainless Steel ◽  
Fatigue Life ◽  
Room Temperature ◽  
Fatigue Testing ◽  
Low Cycle Fatigue ◽  
304 Stainless Steel ◽  
Code Design ◽  
Hydraulic Pressure ◽  
Cycle Fatigue ◽  
Cyclic Bending

This paper presents the results of low-cycle fatigue testing and analysis of 26 piping components and butt-welded sections. The test specimens were fabricated from Type-304 stainless steel and carbon steel, materials which are typically used in the primary piping of light water nuclear reactors. Components included 6-in. elbows, tees, and girth butt-welded straight sections. Fatigue testing consisted of subjecting the specimens to deflection-controlled cyclic bending with the objective of simulating system thermal expansion type loading. Tests were conducted at room temperature and 550 deg F, with specimens at room temperature subjected to 1050 psi constant internal hydraulic pressure in addition to cyclic bending. In two tests at room temperature, however, stainless steel elbows were subjected to combined simultaneous cyclic internal pressure and cyclic bending. Predictions of the fatigue life of each of the specimens tested have been made according to the procedures specified in NB-3650 of Section III[1] in order to assess the code design margin. For the purpose of the assessment, predicted fatigue life is compared to actual fatigue life which is defined as the number of fatigue cycles producing complete through-wall crack growth (leakage). Results of this assessment show that the present code fatigue rules are adequately conservative.

Sign in / Sign up

Export Citation Format

Share Document