scholarly journals Effect of PWHT on the Microstructure and Mechanical Properties of Friction Stir Welded DP780 Steel

Metals ◽  
2021 ◽  
Vol 11 (7) ◽  
pp. 1097
Author(s):  
Umer Masood Chaudry ◽  
Seung-Chang Han ◽  
Fathia Alkelae ◽  
Tea-Sung Jun
Keyword(s):  
Mechanical Properties ◽  
Annealing Temperature ◽  
Tensile Elongation ◽  
Image Correlation ◽  
Frictional Heat ◽  
Uniaxial Tensile ◽  
Uniaxial Tensile Test ◽  
Friction Stir ◽  
Microstructure And Mechanical Properties ◽  
Dp780 Steel

In the present study, the effect of post-weld heat treatment (PWHT) on the microstructure and mechanical properties of friction stir welded (FSW) DP780 steel sheets was investigated. FSW was carried out at a constant tool rotation speed of 400 rpm and different welding speeds (200 mm/min and 400 min/min). A defect free weld was witnessed for both of the welding conditions. The mutual effect of severe plastic deformation and frictional heat generation by pin rotation during the FSW process resulted in grain refinement due to dynamic recrystallization in the stir zone (SZ) and thermo-mechanically affected zone (TMAZ). Lower tensile elongation and higher yield and ultimate tensile strengths were recorded for welded-samples as compared to the base material (BM) DP780 steel. The joints were subsequently annealed at various temperatures at 450–650 °C for 1 h. At higher annealing temperature, the work hardening rate of joints gradually decreased and subsequently failed in the softened heat-affected zone (HAZ) during the uniaxial tensile test. Reduction in yield strength and tensile strength was found in all PWHT conditions, though improvement in elongation was achieved by annealing at 550 °C. The digital image correlation analysis showed that an inhomogeneous strain distribution occurred in the FSWed samples, and the strain was particularly highly localized in the advancing side of interface zone. The nanoindentation measurements covering the FSWed joint were consistent with an increase of the annealing temperature. The various grains size in the BM, TMAZ, and SZ is the main factor monitoring the hardness distribution in these zones and the observed discrepancies in mechanical properties.

Characterization and Evaluation of Mechanical Properties and Residual Stress in Aluminum-Magnesium Alloys Welded by the FSW Process

2020 ◽  
Vol 1012 ◽  
pp. 349-353
Author(s):  
D.B. Colaço ◽  
M.A. Ribeiro ◽  
T.M. Maciel ◽  
R.H.F. de Melo
Keyword(s):  
Mechanical Properties ◽  
Residual Stress ◽  
Residual Stresses ◽  
Welding Process ◽  
Bending Test ◽  
Uniaxial Tensile ◽  
Uniaxial Tensile Test ◽  
Friction Stir ◽  
Aluminum Magnesium Alloys

The demand for lighter materials with suitable mechanical properties and a high resistance to corrosion has been increasing in the industries. Therefore, aluminum appears as an alternative due to its set of properties. The aim of this work was to evaluate residual stress levels and mechanical properties of welded joints of Aluminum-Magnesium alloy AA 5083-O using the Friction Stir Welding process. For mechanical characterization were performed a uniaxial tensile test, Vickers hardness, bending test and, finally, the determination of residual stresses. It was concluded that welding by FSW process with an angle of inclination of the tool at 3o, established better results due to better mixing of materials. The best results of tensile strength and a lower level of residual stresses were obtained using a tool rotation speed of 340 RPM with welding advance speed of 180 mm/min and 70 mm/min.

Effect of Continuous Annealing Temperature on Microstructure and Mechanical Properties of a High Strength Cold-Rolled DP980 Steel

2016 ◽  
Vol 879 ◽  
pp. 2144-2149
Author(s):  
Kai Zhou ◽  
Ying Zou ◽  
Yun Bo Xu ◽  
Zhi Ping Hu ◽  
Xiao Dong Tan ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Annealing Temperature ◽  
Volume Fraction ◽  
Uniaxial Tensile ◽  
Continuous Annealing ◽  
Moderate Increase ◽  
Fracture Elongation ◽  
Microstructure And Mechanical Properties ◽  
Cold Rolled

Continuous annealing processes were applied to a 980MPa cold-rolled dual phase steel (Fe-0.11C-2.5Mn-0.5Si-0.4Cr) and the effect of continuous annealing temperature on microstructure and mechanical properties was investigated. The microstructures were observed and analyzed by optical microscopy (OM), scanning electron microscopy (SEM), electron probe micro-analyzer (EPMA) and transmission electron microscopy (TEM). The mechanical properties were measured by uniaxial tensile tests. The results revealed that the steel is composed of a certain percentage of ferrite, martensite and perhaps a small amount of retained austenite as well. As the annealing temperature increased, the volume fraction of martensite reached to 67% from 48% and the morphology translated to lath-like from M/A island. As a consequence, the ultimate tensile strength (UTS) and yield strength had a moderate increase from 1070 to 1110 MPa and 580 to 640 MPa, respectively. Meanwhile, the fracture elongation rose to the maximum 12.6% firstly and then decreased to about 9.0%. The optimizing mechanical properties with UTS up to 1090 MPa, yield ratio about 0.54 and fracture elongation about 13% could be obtained at the annealing temperature of 790°C for 120s.

Use of Micro Tensile Test Samples in Determining the Remnant Life of Pressure Vessel Steels

2007 ◽  
Vol 7-8 ◽  
pp. 187-194 ◽  
Author(s):  
Rafal M. Molak ◽  
M. Kartal ◽  
Zbigniew Pakiela ◽  
W. Manaj ◽  
Mark Turski ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Test ◽  
Elevated Temperatures ◽  
Collaborative Study ◽  
Correlation Method ◽  
Uniaxial Stress ◽  
Operating Conditions ◽  
Image Correlation ◽  
Uniaxial Tensile ◽  
Uniaxial Tensile Test

The aim of this collaborative study was to measure mechanical properties of 14MoV67-3 steel taken from small sections of material machined in-situ from an operating high pressure collector pipe after different operating lifetimes (from 0h to 186 000h) at elevated temperatures (540°C). Conventional methods of measuring mechanical properties of materials, such as the uniaxial tensile test require relatively large test samples. This can create difficulties when the amount of material available for testing is limited. One way of measuring mechanical properties from small quantities of material is using micro tensile test samples. In this work, micro-samples with a total length of 7.22mm were used. Digital Image Correlation method (DIC) was employed for the strain measurements in a uniaxial tensile test. This paper shows that there is measurable difference in the yield, ultimate tensile strength and elongation to failure as a function of the plant operating conditions. This work demonstrates, therefore, a ‘semi-invasive’ method of determining uniaxial stress-strain behaviour from plant components.

scholarly journals Microstructure and Mechanical Properties of Novel Quasibinary Al-Cu-Yb and Al-Cu-Gd Alloys

Metals ◽  
2021 ◽  
Vol 11 (3) ◽  
pp. 476
Author(s):  
Sayed Amer ◽  
Ruslan Barkov ◽  
Andrey Pozdniakov
Keyword(s):  
Mechanical Properties ◽  
Tensile Properties ◽  
Mechanism Of Action ◽  
Annealing Temperature ◽  
Eutectic Reaction ◽  
Solidification Process ◽  
Annealed State ◽  
Microstructure And Mechanical Properties ◽  
Cold Rolled ◽  
Hot Rolled

Microstructure of Al-Cu-Yb and Al-Cu-Gd alloys at casting, hot-rolled -cold-rolled and annealed state were observed; the effect of annealing on the microstructure was studied, as were the mechanical properties and forming properties of the alloys, and the mechanism of action was explored. Analysis of the solidification process showed that the primary Al solidification is followed by the eutectic reaction. The second Al8Cu4Yb and Al8Cu4Gd phases play an important role as recrystallization inhibitor. The Al3Yb or (Al, Cu)17Yb2 phase inclusions are present in the Al-Cu-Yb alloy at the boundary between the eutectic and aluminum dendrites. The recrystallization starting temperature of the alloys is in the range of 250–350 °C after rolling with previous quenching at 590 and 605 °C for Al-Cu-Yb and Al-Cu-Gd, respectively. The hardness and tensile properties of Al-Cu-Yb and Al-Cu-Gd as-rolled alloys are reduced by increasing the annealing temperature and time. The as-rolled alloys have high mechanical properties: YS = 303 MPa, UTS = 327 MPa and El. = 3.2% for Al-Cu-Yb alloy, while YS = 290 MPa, UTS = 315 MPa and El. = 2.1% for Al-Cu-Gd alloy.

Sign in / Sign up

Export Citation Format

Share Document