scholarly journals Plasma Spheroidisation of Irregular Ti6Al4V Powder for Powder Bed Fusion

Metals ◽  
2021 ◽  
Vol 11 (11) ◽  
pp. 1763
Author(s):  
Nthateng Nkhasi ◽  
Willie du Preez ◽  
Hertzog Bissett
Keyword(s):  
Particle Size ◽  
Additive Manufacturing ◽  
Particle Size Distribution ◽  
Size Distribution ◽  
Metal Powder ◽  
Weight Ratio ◽  
High Strength ◽  
Powder Bed Fusion ◽  
Metal Powders ◽  
Powder Bed

Metal powders suitable for use in powder bed additive manufacturing processes should ideally be spherical, dense, chemically pure and of a specified particle size distribution. Ti6Al4V is commonly used in the aerospace, medical and automotive industries due to its high strength-to-weight ratio and excellent corrosion resistance properties. Interstitial impurities in titanium alloys have an impact upon mechanical properties, particularly oxygen, nitrogen, hydrogen and carbon. The plasma spheroidisation process can be used to spheroidise metal powder consisting of irregularly shaped particles. In this study, the plasma spheroidisation of metal powder was performed on Ti6Al4V powder consisting of irregularly shaped particles. The properties of the powder relevant for powder bed fusion that were determined included the particle size distribution, morphology, particle porosity and chemical composition. Conclusions were drawn regarding the viability of using this process to produce powder suitable for additive manufacturing.

scholarly journals Effect of Particle Size Distribution on Laser Powder Bed Fusion Manufacturability of Copper

2021 ◽  
Author(s):  
Massimiliano Bonesso ◽  
Pietro Rebesan ◽  
Claudio Gennari ◽  
Simone Mancin ◽  
Razvan Dima ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Particle Size ◽  
Particle Size Distribution ◽  
Size Distribution ◽  
Physical And Mechanical Properties ◽  
Powder Bed Fusion ◽  
Laser Powder Bed Fusion ◽  
Powder Bed ◽  
Cooling Channels ◽  
Scan Speed

AbstractOne of the major benefits of the Laser Powder Bed Fusion (LPBF) technology is the possibility of fabrication of complex geometries and features in only one-step of production. In the case of heat exchangers in particular, this is very convenient for the fabrication of conformal cooling channels which can improve the performance of the heat transfer capability. Yet, obtaining dense copper parts printed via LPBF presents two major problems: the high reflectivity of 1 μm (the wavelength of commonly used laser sources) and the high thermal conductivity of copper that limits the maximum local temperature that can be attained. This leads to the formation of porous parts.In this contribution, the influence of the particle size distribution of the powder on the physical and mechanical properties of parts produced via LPBF is studied. Three copper powders lots with different particle size distributions are used in this study. The effect on densification from two laser scan parameters (scan speed and hatching distance) and the influence of contours scans on the lateral surface roughness is reported. Subsequently, samples manufactured with the optimal process parameters are tested for thermal and mechanical properties evaluation.

SIEVING OF POWDERS ADDITIVE AND POWDER MANUFACTURINGS (review)

2020 ◽  
pp. 11-20
Author(s):  
A.E. Knyazev ◽  
◽  
A.V. Vostrikov ◽  
Keyword(s):  
Particle Size ◽  
Particle Size Distribution ◽  
Size Distribution ◽  
Metal Powder ◽  
Metal Powders ◽  
Technological Properties ◽  
Factors Affecting ◽  
Ultrasonic Cleaning

Considers the features of powders obtained by various methods, their technological properties in relation to additive and granular manufacturing. The sequence of operations upon receipt of metal powder compositions is presented. The factors affecting the process of vibration sieving of metal powders and granules are described. The features and advantages of vibratory sieving on horizontally arranged circular sieves using ultrasonic cleaning to obtain specified trajectories of motion are shown. Criteria for evaluating the sieving efficiency are given and explanations are given for determining the particle size distribution of powders and granules.

scholarly journals Reuse of Grade 23 Ti6Al4V Powder during the Laser-Based Powder Bed Fusion Process

Metals ◽  
2020 ◽  
Vol 10 (12) ◽  
pp. 1700
Author(s):  
Ryan Harkin ◽  
Hao Wu ◽  
Sagar Nikam ◽  
Justin Quinn ◽  
Shaun McFadden
Keyword(s):  
Particle Size ◽  
Particle Size Distribution ◽  
Size Distribution ◽  
Compositional Analysis ◽  
Powder Bed Fusion ◽  
Property Variation ◽  
Powder Bed ◽  
Melt Pool ◽  
Powder Particles ◽  
Powder Recycling

Titanium alloy powder used for laser-based powder bed fusion (L-PBF) process is costly. One of the solutions is the inclusion of a powder recycling strategy, allowing unused or exposed powder particles to be recuperated post manufacture, replenished and used for future builds. However, during a L-PBF process, powder particles are exposed to high levels of concentrated energy from the laser. Particularly those in close proximity to the melt pool, leading to the formation of spatter and agglomerated particles. These particles can settle onto the powder bed, which can then influence the particle size distribution and layer uniformity. This study analysed extra-low interstitial (ELI) Ti6Al4V (Grade 23) powder when subjected to nine recycle iterations, tracking powder property variation across the successive recycling stages. Characterisation included chemical composition focusing upon O, N, and H content, particle size distribution, morphology and tapped and bulk densities. On review of the compositional analysis, the oxygen content exceeded the 0.13% limit for the ELI grade after 8 recycles, resulting in the degradation from Grade 23 level.

scholarly journals Evaluation of Inconel 718 Metallic Powder to Optimize the Reuse of Powder and to Improve the Performance and Sustainability of the Laser Powder Bed Fusion (LPBF) Process

Materials ◽  
2021 ◽  
Vol 14 (6) ◽  
pp. 1538
Author(s):  
Konrad Gruber ◽  
Irina Smolina ◽  
Marcin Kasprowicz ◽  
Tomasz Kurzynowski
Keyword(s):  
Particle Size ◽  
Particle Size Distribution ◽  
Size Distribution ◽  
Inconel 718 ◽  
Chemical Properties ◽  
Powder Bed Fusion ◽  
Laser Powder Bed Fusion ◽  
Powder Bed ◽  
Laser Absorption ◽  
Multiple Uses

In this paper, a detailed assessment of Inconel 718 powder, with varying degrees of degradation due to repeated use in the Laser Powder Bed Fusion (LPBF) process, has been undertaken. Four states of IN718 powder (virgin, used, overflow and spatter) were characterized in terms of their morphology, flowability and physico-chemical properties. Studies showed that used and overflow powders were almost identical. The fine particle-size distribution of the virgin powder, in which 50% of particles were found to be below the nominal particle-size distribution (PSD), was recognized as the main reason for its lower flowability and the main cause of the differentiation between virgin, used and overflow powders. Only spatter powder was found to be degraded enough to preclude its direct LPBF reuse. The oxygen content in the spatter powder exceeded the limit value for IN718 by 290 ppm, and aluminum oxide spots were found on the spatter particles surfaces. Laser absorption analysis showed 10 pp higher laser absorption compared to the other powders. The results of evaluation showed that IN718 powder is resistant to multiple uses in the LPBF process. Due to the low degradation rate of IN718 powder, overflow powder can be re-enabled for multiple uses with a proper recycling strategy.

Investigating the Sensitivity of Particle Size Distribution on Part Geometry in Additive Manufacturing

2020 ◽  
Author(s):  
Vaishak Ramesh Sagar ◽  
Samuel Lorin ◽  
Johan Göhl ◽  
Johannes Quist ◽  
Christoffer Cromvik ◽  
...  
Keyword(s):  
Particle Size ◽  
Additive Manufacturing ◽  
Particle Size Distribution ◽  
Size Distribution ◽  
Complex Geometry ◽  
Structural Mechanics ◽  
Raw Material ◽  
Test Bed ◽  
Powder Bed ◽  
Melted Zone

Abstract Selective laser melting process is a powder bed fusion additive manufacturing process that finds applications in aerospace and medical industries for its ability to produce complex geometry parts. As the raw material used is in powder form, particle size distribution (PSD) is a significant characteristic that influences the build quality in turn affecting the functionality and aesthetics aspects of the end product. This paper investigates the effect of PSD on deformation for 316L stainless steel powder, where three coupled in-house simulation tools based on Discrete Element Method (DEM), Computational Fluid Dynamics (CFD), and Structural Mechanics are employed. DEM is used for simulating the powder distribution based on the different particle size distribution of the powder. The CFD is used as a virtual test bed to determine thermal parameters such as density, heat capacity and thermal conductivity of the powder bed viewed as a continuum. The values found as a stochastic function of the powder distribution is used to test the sensitivity of the melted zone and distortion using Structural Mechanics. Results showed significant influence of particle size distribution on the packing density, surface height, surface roughness, the stress state and displacement of the melted zone. The results will serve as a catalyst in developing geometry assurance strategies to minimize the effect of particle size distribution on the geometric quality of the printed part.