Influence of Irradiation Doses on Mechanical Properties of PA6

2015 ◽  
Vol 752-753 ◽  
pp. 136-141
Author(s):  
Petr Kratky ◽  
David Manas ◽  
Miroslav Manas ◽  
Michal Stanek ◽  
Martin Ovsik ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Polymer Material ◽  
Applied Load ◽  
Polyamide 6 ◽  
Polymer Materials ◽  
Cross Linking ◽  
Depth Sensing ◽  
Hard Surface ◽  
End Use

The presented article deals with influence of mechanical properties of the hard surface layer of modified polyamide 6. The mechanical properties were acquired by nanohardness test with using the DSI method (Depth Sensing Indentation). Hard surface layer was created by radiation cross-linking technology. This technology allows polymer materials modification followed by the change of their end-use properties. The surface layer of polymer material is modified by β - radiation. When the polymer material is exposed to the β radiation, it is possible to observe changes of the surface layer at applied load.

Improvement of PA6 Mechanical Properties by Radiation Cross-Linking

2015 ◽  
Vol 1120-1121 ◽  
pp. 1163-1166 ◽  
Author(s):  
Petr Kratky ◽  
David Manas ◽  
Miroslav Manas ◽  
Michal Stanek ◽  
Martin Ovsik ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Polymer Material ◽  
Polyamide 6 ◽  
Polymer Materials ◽  
Cross Linking ◽  
Depth Sensing ◽  
Surface Layers ◽  
Hard Surface ◽  
End Use

Influence of mechanical properties of the hard surface layer of modified polyamide 6 is studied. Mechanical properties are acquired by nanohardness test with using the DSI method (Depth Sensing Indentation). Hard surface layers are created by radiation cross-linking technology. This technology allows polymer materials modification followed by the change of their end-use properties. The surface layer of polymer material is modified by ionizing β - radiation. When the polymer material is exposed to the β radiation, it is possible to observe changes of the surface layer at applied load. Radiation cross-linking usually improves strength, reduces creep, contributes to chemical resistance improvement, and in many cases improves tribological properties.

Influence of Irradiation Doses on Mechanical Properties of Glass Fiber Filled PBT

2015 ◽  
Vol 752-753 ◽  
pp. 130-135
Author(s):  
Petr Kratky ◽  
David Manas ◽  
Miroslav Manas ◽  
Michal Stanek ◽  
Martin Ovsik ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Polymer Material ◽  
Applied Load ◽  
Glass Fibers ◽  
Polymer Materials ◽  
Cross Linking ◽  
Depth Sensing ◽  
Hard Surface ◽  
End Use

The submitted paper compares mechanical properties of the hard surface layer of modified PBT filled by 35% of glass fibers. Hard surface layer was made by radiation cross-linking technology which allows polymer materials modification followed by the change of their end-use properties. The surface layer of polymer material is modified by β – radiation. When the polymer material is exposed to the β – radiation, it is possible to observe changes of the surface layer at applied load. The mechanical properties were measured by nanohardness test with using the DSI method (Depth Sensing Indentation).

The Effect of Cross-Linking on Nano-Mechanical Properties of Polyamide

2016 ◽  
Vol 699 ◽  
pp. 37-42 ◽  
Author(s):  
Martin Ovsik ◽  
David Manas ◽  
Miroslav Manas ◽  
Michal Stanek ◽  
Martin Reznicek
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Material Properties ◽  
Basic Material ◽  
Nanoindentation Test ◽  
Cross Linking ◽  
Indentation Hardness ◽  
Depth Sensing ◽  
Nanomechanical Properties ◽  
Radiation Crosslinking

Radiation crosslinking of polyamidu 6 (PA 6) is a well-recognized modification of improving basic material characteristics. Radiation, which penetrated through specimens and reacted with the cross-linking agent, gradually formed cross-linking (3D net), first in the surface layer and then in the total volume, which resulted in considerable changes in specimen behaviour. This research paper deals with the possible utilization of irradiated PA6. The material already contained a special cross-linking agent TAIC (5 volume %), which should enable subsequent cross-linking by ionizing β – radiation (15, 30 and 45 kGy). The effect of the irradiation on mechanical behavior of the tested PA 6 was investigated. Material properties created by β – radiation are measured by nanoindentation test using the DSI method (Depth Sensing Indentation). Hardness increased with increasing dose of irradiation at everything samples; however results of nanoindentation test shows increasing in nanomechanical properties of surface layer. The highest values of nanomechanical properties were reached radiation dose of 45 kGy, when the nanomechanical values increased by about 95%. These results indicate advantage cross-linking of the improved mechanical properties.

Influence of Content of Crosslinking Agent on the Micromechanical Properties of Glass-Filled Polyamide 6

2015 ◽  
Vol 752-753 ◽  
pp. 357-362
Author(s):  
David Manas ◽  
Martin Ovsik ◽  
Miroslav Manas ◽  
Michal Stanek ◽  
Marcela Spanhelova ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Crosslinking Agent ◽  
Polyamide 6 ◽  
Polymer Structure ◽  
Polymer Materials ◽  
Cross Link ◽  
Micromechanical Properties ◽  
Radiation Crosslinking ◽  
Injection Technology

The process of radiation crosslinking helps to improve some mechanical properties of polymer materials. Some types of polymers do not cross-link during radiation crosslinking but degrade. In order to create 3D net in the polymer structure it is necessary to add a crosslinking agent. The specimens were prepared by injection technology with the TAIC crosslinking agent at 0, 1, 2 and 3 %. The changes of micromechanical properties of the surface layer were measured by instrumented microhardness test. It was found that micromechanical properties of the surface layer of the tested polyamide changed.

Micromechanical Properties of Glass-Filled Polyamide 6

2015 ◽  
Vol 1120-1121 ◽  
pp. 3-6
Author(s):  
David Manas ◽  
Martin Ovsik ◽  
Miroslav Manas ◽  
Michal Stanek ◽  
Pavel Stoklasek ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Polyamide 6 ◽  
Polymer Materials ◽  
Beta Radiation ◽  
Indentation Hardness ◽  
Radiation Doses ◽  
High Radiation ◽  
Radiation Crosslinking ◽  
Injection Technology

The process of radiation crosslinking helps to improve some mechanical properties of polymer materials. Micromechanical changes in the surface layer of glass-filled PA-6 modified by beta radiation were measured by instrumented test of microhardness. The specimens were prepared by injection technology and subjected to radiation doses of 0, 66, 99, 132 kGy. Measurements of microhardness showed considerable changes of behavior of surface layer in middle as well as high radiation doses with higher values of indentation hardness and stiffness.

Surface Layer Micro-Hardness of Modified LDPE by Radiation Cross-Linking after Temperature Load

2015 ◽  
Vol 662 ◽  
pp. 177-180 ◽  
Author(s):  
Ales Mizera ◽  
Miroslav Manas ◽  
David Manas ◽  
Martin Ovsik ◽  
Martina Kaszonyiová ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Cross Linking ◽  
Indentation Hardness ◽  
Micro Hardness ◽  
Depth Sensing ◽  
Indentation Method ◽  
Temperature Load ◽  
Irradiation Process ◽  
Different Doses

The presented article deals with the research of surface layer ́s micro-mechanical properties of modified LDPE by radiation cross-linking after temperature load. These micro-mechanical properties were measured by the DSI (Depth Sensing Indentation) method on samples which were non-irradiated and irradiated by different doses of the β – radiation and then were temperature loaded. The purpose of the article is to consider to what extent the irradiation process influences the resulting micro-mechanical properties measured by the DSI method. The LDPE tested showed significant changes of indentation hardness and modulus after temperature load.

The Behaviour of Cross-Linking Filled PA66 by Micro-Indentation Test

2016 ◽  
Vol 699 ◽  
pp. 43-48
Author(s):  
Martin Ovsik ◽  
David Manas ◽  
Miroslav Manas ◽  
Michal Stanek ◽  
Vojtech Senkerik
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Glass Fiber ◽  
Indentation Test ◽  
Polymer Materials ◽  
Beta Radiation ◽  
Indentation Hardness ◽  
Indentation Modulus ◽  
Polyamide 66 ◽  
Depth Sensing

The process of radiation crosslinking helps to improve some mechanical properties of polymer materials. Micro-mechanical changes in the surface layer of glass-fiber filled PA 66 modified by beta radiation were measured by the Depth Sensing Indentation - DSI method on samples which were non-irradiated and irradiated by different doses of the β - radiation. The specimens were prepared by injection technology and subjected to radiation doses of 0, 33, 66 nad 99 kGy. The change of micro-mechanical properties is greatly manifested mainly in the surface layer of the modified polypropylene where a significant growth of micro-hardness values can be observed. Indentation modulus increased from 1.8 to 3.0 GPa (increasing about 66%) and indentation hardness increased from 87 to 157 MPa (increasing about 80%). This research paper studies the influence of the dose of irradiation on the micro-mechanical properties of semi-crystalline polyamide 66 filled by 30% glass fiber at room temperature. The study is carried out due to the ever-growing employment of this type of polymer.

Irradiation of Polyamide Measured by Micro-Indentation Test

2015 ◽  
Vol 1120-1121 ◽  
pp. 1179-1182
Author(s):  
Martin Ovsik ◽  
David Manas ◽  
Miroslav Manas ◽  
Michal Stanek ◽  
Adam Skrobak ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Material Properties ◽  
Indentation Test ◽  
Polymer Chains ◽  
Cross Linking ◽  
Indentation Hardness ◽  
Chemical Bonds ◽  
Depth Sensing ◽  
Micro Indentation

Cross-linking is a process in which polymer chains are associated through chemical bonds. This research paper deals with the possible utilization of irradiated polyamide. Influence of the intensity of irradiation on micro-indentation hardness was investigated. Material properties created by β – radiation are measured by micro-indentation test using the DSI method (Depth Sensing Indentation). Hardness increased with increasing dose of irradiation at everything samples; however results of micro-indentation test shows increasing in micro-mechanical properties of surface layer. The highest values of micro-mechanical properties were reached radiation dose of 99 kGy, when the micro-mechanical values increased by about 18%.

Effect of High Doses Beta Irradiation on the Micromechanical Properties of Surface Layer of Glass-Filled Polypropylene

2015 ◽  
Vol 662 ◽  
pp. 185-188 ◽  
Author(s):  
David Manas ◽  
Miroslav Manas ◽  
Ales Mizera ◽  
Michal Stanek ◽  
Martin Bednarik ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Glass Fibers ◽  
Cross Linking ◽  
Radiation Doses ◽  
Depth Sensing ◽  
Significant Growth ◽  
Micromechanical Properties ◽  
High Doses ◽  
Different Doses

The presented article deals with the research of micro-mechanical properties in the surface layer of modified Polypropylene filled by 25% of glass fibers. These micro-mechanical properties were measured by the Depth Sensing Indentation - DSI method on samples which were non-irradiated and irradiated by different doses of the β - radiation. Radiation doses used were 0, 66 and 99 kGy for filled Polypropylene with the 6% cross-linking agent (triallyl isocyanurate). The change of micromechanical properties is greatly manifested mainly in the surface layer of the modified polypropylene where a significant growth of microhardness values can be observed.

Micro-Hardness Test of Cross-Linking LLDPE

2017 ◽  
Vol 1142 ◽  
pp. 134-137
Author(s):  
Martin Ovsik ◽  
David Manas ◽  
Miroslav Manas ◽  
Michal Stanek ◽  
Vaclav Janostik
Keyword(s):  
Mechanical Properties ◽  
Surface Layer ◽  
Hardness Test ◽  
Cross Linking ◽  
Radiation Doses ◽  
Micro Hardness ◽  
Depth Sensing ◽  
Linear Polyethylene ◽  
Hardness Values ◽  
Different Doses

The presented article deals with the research of micro-mechanical properties in the surface layer of modified linear polyethylene (LLDPE). These micro-mechanical properties were measured by the Depth Sensing Indentation - DSI method on samples which were non-irradiated and irradiated by different doses of the β - radiation (0, 66, 132 and 198 kGy ). Individual radiation doses caused structural and micro-mechanical changes which have a significant effect on the final properties of the LLDPE tested. The highest values of micro-mechanical properties were reached at radiation dose of 132 kGy, when the micro-hardness values increased by about 29%. These results indicate advantage crosslinking of the improved mechanical properties.