In-Suit Synthesis (ZrB2-SiC)/Si High Temperature Oxidation Resistance Coating by Argon Arc Cladding
2014 ◽
Vol 1035
◽
pp. 134-137
Keyword(s):
X Ray
◽
In order to overcome the occurrence of insufficient oxidation reaction, high temperature oxidation resistance (ZrB2-SiC)/Si composite coating was fabricated on the surface of graphite electrode by argon arc cladding, process using the Si, Zr and B4C power blends. The microstructure and phase composition of the clad layer were researched by means of scanning electron microscopy (SEM) and X-ray diffraction analysis (XRD). The result shows that the coating consist of ZrB2 and SiC particles, The combination of the cladding layer and the graphite matrix results in kind of a continuous interface without visible defects. As the result of burning 60 min at 1573K, the oxidation weightlessness rate is 0.62%.