Lab Scale Synthesis of Al-Sc Alloys in NaF-AlF3-Al2O3-Sc2O3 Melt
2015 ◽
Vol 1088
◽
pp. 213-216
◽
Keyword(s):
The liquidus temperature in the [NaF-AlF3(30 mol.%)]-Sc2O3 molten system with the Sc2O3 additions up to 12 wt% was measured by the thermo analysis. The effect of the cathode current density (0, 0.25, 0.50, and 1.0 A∙cm-2), the Sc2O3 content (1, 2, 4, and 8 wt%) in the NaF-AlF3(30 mol.%)-Al2O3-Sc2O3 electrolyte, the rate of the molten aluminum agitation (0, 100 rotates/min), the synthesis duration (30-210 min) on the Sc content in the aluminum alloy at 980 °С was studied. The Al-Sc alloys with the scandium content of 0.15-1.30 wt%, depending on the synthesis conditions, and with the uniform Sc distribution throughout the aluminum matrix were produced.
2020 ◽
Vol 4
(141)
◽
pp. 140-147
2005 ◽
Vol 475-479
◽
pp. 921-924
◽
Keyword(s):
1996 ◽
Vol 46
(1)
◽
pp. 97-111
◽
Keyword(s):
2011 ◽
Vol 284-286
◽
pp. 1477-1482
◽
2011 ◽
Vol 239-242
◽
pp. 1452-1456
2021 ◽
Vol 3
(6 (111))
◽
pp. 53-58
2015 ◽
Vol 788
◽
pp. 75-81
◽
Keyword(s):
2012 ◽
Vol 217-219
◽
pp. 1331-1335