scholarly journals Amorphization of CuZr Based Alloy Powders by Mechanical Milling

2014 ◽  
Vol 790-791 ◽  
pp. 509-514 ◽  
Author(s):  
Kinga Tomolya ◽  
Dóra Janovszky ◽  
Anna Sycheva
Keyword(s):  
Amorphous Alloys ◽  
Eutectic Composition ◽  
Supercooled Liquid ◽  
Xrd Analysis ◽  
Supercooled Liquid Region ◽  
Glass Forming Ability ◽  
Liquid Region ◽  
Glass Forming ◽  
Nickel Addition ◽  
Thermal Stability Of

The effect of nickel addition was studied in the CuZr system creating alloys with near eutectic composition. Nickel and aluminum have been regarded as useful elements to improve the plasticity, thermal stability of the CuZr-based amorphous alloys. Cu49Zr45Al6and (Cu49Zr45Al6)95Ni5were selected because of the good glass-forming ability. After 15 h of milling the structure of the powders was amorphous based on the XRD analysis. By adding nickel, the crystallization temperature (Tx) shifted to higher temperatures compared to CuZrAl alloy. The value of supercooled liquid region was 64 K, which means CuZrAl has a comparatively high glass forming ability.

Glass-forming ability and thermal stability of Fe62Nb8−xZrxB30 and Fe72Zr8B20 amorphous alloys?

Open Physics ◽  
2004 ◽  
Vol 2 (1) ◽  
Author(s):  
M. Shapaan ◽  
J. Lábár ◽  
L. Varga ◽  
J. Lendvai
Keyword(s):  
Thermal Stability ◽  
Amorphous Alloys ◽  
Strong Dependence ◽  
Supercooled Liquid ◽  
Supercooled Liquid Region ◽  
Glass Forming Ability ◽  
Partial Replacement ◽  
Liquid Region ◽  
Glass Forming ◽  
Thermal Stability Of

AbstractGlass-forming ability (GFA) and thermal stability of Fe62Nb8B30, Fe62Nb6Zr2B30 and Fe72Zr8B20 at % amorphous alloys were investigated by calorimetric (DSC and DTA) measurements. The crystallization kinetics was studied by DSC in the mode of continuous versus linear heating and it was found that both the glass transition temperature, Tg, and the crystallization peak temperature, Tp, display strong dependence on the heating rate. The partial replacement of Nb by Zr leads to lower Tg and Tx temperatures and causes a decrease of the supercooled liquid region. JMA analysis of isothermal transformation data measured between Tg and Tx suggests that the crystallization of the Fe62Nb8B30 and Fe62Nb6Zr2B30 amorphous alloys take place by three-dimensional growth with constant nucleation rate. Nb enhances the precipitation of the metastable Fe23B6 phase and stabilizes it up to the third crystallization stage. Zr addition increases the lattice constant of Fe23B6 and, at the same time, decreases the grain size.

scholarly journals Crystallization Behavior of Al70Fe12.5V12.5Nb5 Amorphous Alloy Formed by Mechanical Alloying

Materials ◽  
2019 ◽  
Vol 12 (3) ◽  
pp. 383 ◽  
Author(s):  
Xuan Liu ◽  
Xingfu Wang ◽  
Yongli Si ◽  
Xiaokang Zhong ◽  
Fusheng Han
Keyword(s):  
Amorphous Alloy ◽  
Mechanical Alloying ◽  
Amorphous Alloys ◽  
Crystallization Behavior ◽  
Supercooled Liquid ◽  
Supercooled Liquid Region ◽  
Glass Forming Ability ◽  
Liquid Region ◽  
Application Field ◽  
Glass Forming

In this study, the formation and crystallization of the Al70Fe12.5V12.5Nb5 amorphous alloys has been investigated. The addition of Nb enhances the supercooled liquid region and glass forming ability of the Al-Fe-V amorphous alloys. The Al70Fe12.5V12.5Nb5 amorphous alloy exhibits two distinct crystallization steps and a large supercooled liquid region at more than 100 K. Kissinger and Ozawa analyses showed that the two activation energies for crystallization (Ex) were estimated to be 366.3 ± 23.9 and 380.5 ± 23.9 kJ/mol. Large supercooled liquid regions are expected to gain an application field of Al-based amorphous alloys.

scholarly journals Structural and Phase Evolution upon Annealing of Fe76Si9−xB10P5Mox (x = 0, 1, 2 and 3) Alloys

Metals ◽  
2020 ◽  
Vol 10 (7) ◽  
pp. 881
Author(s):  
Darling Perea ◽  
Carolina Parra ◽  
Parthiban Ramasamy ◽  
Mihai Stoica ◽  
Jürgen Eckert ◽  
...  
Keyword(s):  
Thermal Stability ◽  
Amorphous Alloys ◽  
Structural Evolution ◽  
Supercooled Liquid ◽  
Phase Evolution ◽  
Supercooled Liquid Region ◽  
Liquid Region ◽  
Glass Forming ◽  
Different Temperatures ◽  
Thermal Stability Of

Alloying elements play an important role in adjusting the magnetic and thermal properties of Fe-based amorphous alloys. In this work, the effect of Mo addition on the thermal stability, structural evolution, and magnetic properties of Fe76Si9B10P5 metallic glass was studied. The study revealed that the substitution of a small amount of Mo (1 at.%) for Si enhances the glass-forming ability (GFA) but reduces the thermal stability of the alloy, causing a reduction of the supercooled liquid region. Substitution of up to 3 at.% Mo for Si lowers the Curie temperature from 677 to 550 K and the saturation magnetization drops from 160 to 138 Am2/kg. The structural evolution was evaluated by annealing the glassy samples at different temperatures, revealing that the crystallization proceeds in multiple steps, beginning with the formation of different iron borides (FeB, Fe2B, FeB2 and Fe23B6) followed by transformation to a mixture of more stable phases.

Comments on “Fabrication of ternary Mg–Cu–Gd bulk metallic glass with high glass-forming ability under air atmosphere” [H. Men and D.H. Kim, J. Mater. Res. 18, 1502 (2003)]

2004 ◽  
Vol 19 (2) ◽  
pp. 427-428 ◽  
Author(s):  
Z.P. Lu ◽  
C.T. Liu
Keyword(s):  
Glass Transition ◽  
Metallic Glasses ◽  
Supercooled Liquid ◽  
Supercooled Liquid Region ◽  
Glass Forming Ability ◽  
Bulk Amorphous Alloy ◽  
Liquid Region ◽  
Glass Forming ◽  
Air Atmosphere ◽  
Acta Mater

A new Mg-based bulk amorphous alloy (i.e., Mg65Cu25Gd10) has successfully been developed by Men and Kim [H. Men and D.H. Kim, J. Mater. Res. 18, 1502 (2003)]. They showed that this alloy exhibits significantly improved glass-forming ability (GFA) in comparison with Mg65Cu25Y10 alloy. However, this improved GFA cannot be indicated by the supercooled liquid region ΔT and the reduced glass-transition temperature Trg. As shown in the current comment, the new parameter γ, Tx/(Tg + Tl) defined in our recent papers [Z.P. Lu and C.T. Liu, Acta Mater. 50, 3501 (2002); Z.P. Lu and C.T. Liu, Phys. Rev. Lett. 91, 115505 (2003)] can well gauge GFA for bulk metallic glasses, including the current Mg-based alloys.

Glass-forming ability and magnetic properties of CoFeMoYB bulk glassy alloys with large supercooled liquid region

2010 ◽  
Vol 504 ◽  
pp. S132-S134 ◽  
Author(s):  
Qikui Man ◽  
Huaijun Sun ◽  
Yaqiang Dong ◽  
Baolong Shen ◽  
Hisamichi Kimura ◽  
...  
Keyword(s):  
Magnetic Properties ◽  
Supercooled Liquid ◽  
Supercooled Liquid Region ◽  
Glass Forming Ability ◽  
Liquid Region ◽  
Glass Forming ◽  
Glassy Alloys

GLASS FORMING ABILITY AND KINETIC CHARACTERS OF PARAMAGNETIC Nd60Co40-xAlx(x=5, 10, 15) BULK METALLIC GLASSES

2004 ◽  
Vol 18 (14) ◽  
pp. 679-685 ◽  
Author(s):  
L. XIA ◽  
Y. D. DONG
Keyword(s):  
Glass Transition ◽  
Metallic Glasses ◽  
Bulk Metallic Glasses ◽  
Supercooled Liquid ◽  
Supercooled Liquid Region ◽  
Glass Forming Ability ◽  
Ternary Alloys ◽  
Liquid Region ◽  
Scanning Calorimetry ◽  
Glass Forming

Paramagnetic Nd 60 Co 40-x Al x(x=5, 10, 15) bulk metallic glasses (BMGs) were prepared in the shape of rods 2 mm in diameter by suction casting. The ternary alloys have shown distinct glass transitions in Differential Scanning Calorimetry (DSC) measurements and excellent glass-forming ability. The glass transition and crystallization behaviors as well as their kinetics have been studied. The reduced glass transition temperature and the supercooled liquid region of the alloys were found to increase with the increasing content of Al . The role of Al was discussed. The parameter γ defined by Liu et al. was employed to discuss the glass-forming ability of the alloys and the critical cooling rates as well as the critical section thickness of the alloys were predicted accordingly.

Critical Cooling Rate of Y36Nd20Al24Co20 Bulk Amorphous Alloy

2014 ◽  
Vol 670-671 ◽  
pp. 86-89
Author(s):  
Shi Wen He
Keyword(s):  
Glass Transition ◽  
Amorphous Alloy ◽  
Cooling Rate ◽  
Supercooled Liquid ◽  
Supercooled Liquid Region ◽  
Glass Forming Ability ◽  
Bulk Amorphous Alloy ◽  
Liquid Region ◽  
Critical Cooling Rate ◽  
Glass Forming

A new bulk amorphous alloy, Y36Nd20Al24Co20, with a diameter of 5 mm was successfully fabricated by the method of equiatomic substitution for the Y element in Y56Al24Co20amorphous alloy. The values of the supercooled liquid region ∆Tx(=Tx-Tg), the reduced glass transition temperature Trg(=Tg/Tl) and the parameter γ (=Tx/(Tg+Tl)) for Y36Nd20Al24Co20bulk amorphous alloy are 60K, 0.605 and 0.415, respectively. The critical cooling rate of the Y36Nd20Al24Co20bulk amorphous alloy was determined to be 40 K/s, providing an indication that this alloy has a high glass-forming ability.

Sign in / Sign up

Export Citation Format

Share Document