Characterization and Calculation of the Dynamic Recrystallization Texture in Fe-3.0 Wt.% Si Alloy

High-temperature plane-strain compression tests were performed on Fe-3.0 wt.% Si alloy from 900 °C to 1150 °C at strain rates of 5 s−1 to 1 s−1, and the texture development from different initial textures was investigated by means of electron backscattered diffraction. Dynamic recrystallization occurs by strain-induced boundary migration, and the evolutions of the microstructure and different texture components vary with the initial texture. The critical orientation boundary separating the weakened and enhanced texture components moves with the initial texture, and a quantitative relationship is established to represent the dependence of the critical Taylor factor on the instantaneous texture. A model is proposed to describe the dynamic recrystallization texture by incorporating the oriented nucleation probability with a variable critical Taylor factor. The present work could improve the accuracy of hot deformation texture prediction based on strain-induced boundary migration.

Rapid Secondary Recrystallization of the Goss Texture in Fe81Ga19 Sheets Using Nanosized NbC Particles

Herein, a simple and efficient method is proposed for fabricating Fe81Ga19 alloy thin sheets with a high magnetostriction coefficient. Sharp Goss texture ({110}<001>) was successfully produced in the sheets by rapid secondary recrystallization induced by nanosized NbC particles at low temperatures. Numerous NbC precipitates (size ~90 nm) were obtained after hot rolling, intermediate annealing, and primary recrystallization annealing. The relatively higher quantity of nanosized NbC precipitates with 0.22 mol% resulted in finer and uniform grains (~10 μm) through thickness after primary recrystallization annealing. There was a slow coarsening of the NbC precipitates, from 104 nm to 130 nm, as the temperature rose from 850 °C to 900 °C in a pure nitrogen atmosphere, as well as a primary recrystallization textured by strong γ fibers with a peak at {111} <112> favoring the development of secondary recrystallization of Goss texture at a temperature of 850 °C. Matching of the appropriate inhibitor characteristics and primary recrystallization texture guaranteed rapid secondary recrystallization at temperatures lower than 950 °C. A high magnetostriction coefficient of 304 ppm was achieved for the Fe81Ga19 sheet after rapid secondary recrystallization.