Effect of Lightweight Aggregate Impregnation on Selected Concrete Properties

The impregnation of lightweight aggregate (LWA) is an alternative method to its pre-moistening, which is used to limit the loss of fresh concrete workability due to the aggregate’s ability to absorb a great amount of mixing water. The aim of this study was to access the effectiveness, by pre-coating LWAs with cement paste, in modifying the properties of concrete composites. Two types of lightweight aggregates (Lytag and Leca) characterized with a relatively open-structure shell were selected. The other changeable parameters taken into consideration in this research were: LWA size, initial moisture of aggregate before the impregnation process and type of cement paste applied as an impregnant. Sixteen concretes prepared with pre-moistened and pre-coated lightweight aggregates were subject to a density test in different moisture conditions, a water absorption test and a compressive strength test. On the one hand, the pre-coating of LWAs with cement paste resulted in a relatively slight increase in concrete density (by up to 19%) compared to the pre-moistening of LWAs. On the other hand, it caused a very significant reduction (by up to 52%) in the composite’s water absorption and an incomparably greater growth (by up to 107%) in compressive strength. The most crucial factors determining the effectiveness of impregnation of LWAs with cement pastes in improvement of composite properties were the aggregate type and its size. The composition of impregnating slurry and the initial moisture content of LWA before pre-coating also mattered.

Effect of Aggregate and Binder Type on the Functional and Durability Parameters of Lightweight Repair Mortars

The subject matter of the work presented here is the development and evaluation of novel lightweight mortars that meet the functional and technical criteria imposed on repair mortars. In a broad experimental campaign, lime, natural hydraulic lime, and lime–cement mortars were designed and tested. Lightweight aggregate, expanded perlite, granules from expanded glass and zeolite were used as full replacements for quartz sand. The hardened mortars were tested at the ages of 28 days and 90 days. The conducted tests and analyses were focused on the assessment of structural, mechanical, hygric and thermal parameters. The salt crystallization resistance and effect of salt presence on the hygroscopicity of the investigated mortars were also investigated. The use of lightweight aggregates in the composition of mortars resulted in their high porosity, low density, satisfactory mechanical parameters, improved water vapor transmission capability and water absorption. The mortars with expanded perlite and glass granulate were ranked among thermal insulation mortars of classes T1 and T2, respectively. The use of lightweight aggregates enabled the development of mortars with great durability in terms of salt action, which was almost independent of binder type. The ability to accommodate water vapor was increased by the effect, i.e., the use of lightweight aggregates and the presence of salt in mortars increased porous space. Taking into account the compatibility, functional, and technical criteria, lime- and natural hydraulic lime-based lightweight mortarswere classified as repair mortars, providing improved thermal performance. The lime–cement lightweight plasters can be recommended only for repair of building structures where cement and lime–cement materials were original applied.

Effect of Thermal Properties of Aggregates on the Mechanical Properties of High Strength Concrete under Loading and High Temperature Conditions

The effect of the thermal properties of aggregates on the mechanical properties of high-strength concrete was evaluated under loading and high-temperature conditions. For the concrete, granite was selected as a natural aggregate, and ash-clay and clay as lightweight aggregates. The mechanical properties of the concrete (stress–strain, compressive strength, elastic modulus, thermal strain, and transient creep) were evaluated experimentally under uniform heating from 20 to 700 °C while maintaining the load at 0, 20, and 40% of the compressive strength at room temperature. Experimental results showed that the concrete containing lightweight aggregates had better mechanical properties, such as compressive strength and elastic modulus, than that of the concrete with a granite aggregate at high temperature. In particular, the concrete containing lightweight aggregates exhibited high compressive strength (60–80% of that at room temperature) even at 700 °C. Moreover, the concrete containing granite exhibited a higher thermal strain than that containing lightweight aggregates. The influence of the binding force under loaded conditions, however, was found to be larger for the latter type. The transient creep caused by the loading was constant regardless of the aggregate type below 500 °C but increased more rapidly when the coefficient of the thermal expansion of the aggregate was above 500 °C.