On the Effects of High and Ultra-High Rotational Speeds on the Strength, Corrosion Resistance, and Microstructure during Friction Stir Welding of Al 6061-T6 and 316L SS Alloys

In this study, under the conditions of using tools at a high rotational speed (HRS) of 10,000 rpm and an ultra-high rotational speed (ultra-HRS) of 18,000 rpm, the produced welding heat input was utilized to weld two specimens of Al alloy 6061-T6 with 1.0 mm thickness and 316L SS with 0.8 mm thickness. The microstructural characteristics, mechanical properties, and electrochemical corrosion properties of the aluminum alloy–steel joints were analyzed. The higher tool offset forms an intermetallic compound layer of less than 1 µm at the Fe-Al interface on the advancing side (AS) at different speeds. This results in a mixed zone structure. The lower tool offset forms intermetallic compounds of only 2 µm. The formation of a composite material based on aluminum alloy in the weld nugget zone improves the hardness value. The intermetallic compounds are Fe3Al and FeAl3, respectively. It was observed that the formation of intermetallic compounds is solely related to the rotational speed, and the iron-rich intermetallic compounds produced under ultra-HRS parameters have higher corrosion resistance. When the tool offset is 0.55 mm, using the HRS parameters, the tensile strength is 220.8 MPa (about 75.9% of that of the base metal).

Investigation of Mechanical and Microstructural Properties of Welded Specimens of AA6061-T6 Alloy with Friction Stir Welding and Parallel-Friction Stir Welding Methods

The present study investigates the effect of two parameters of process type and tool offset on tensile, microhardness, and microstructure properties of AA6061-T6 aluminum alloy joints. Three methods of Friction Stir Welding (FSW), Advancing Parallel-Friction Stir Welding (AP-FSW), and Retreating Parallel-Friction Stir Welding (RP-FSW) were used. In addition, four modes of 0.5, 1, 1.5, and 2 mm of tool offset were used in two welding passes in AP-FSW and RP-FSW processes. Based on the results, it was found that the mechanical properties of welded specimens with AP-FSW and RP-FSW techniques experience significant increments compared to FSW specimens. The best mechanical and microstructural properties were observed in the samples welded by RP-FSW, AP-FSW, and FSW methods, respectively. Welded specimens with the RP-FSW technique had better mechanical properties than other specimens due to the concentration of material flow in the weld nugget and proper microstructure refinement. In both AP-FSW and RP-FSW processes, by increasing the tool offset to 1.5 mm, joint efficiency increased significantly. The highest weld strength was found for welded specimens by RP-FSW and AP-FSW processes with a 1.5 mm tool offset. The peak sample of the RP-FSW process (1.5 mm offset) had the closest mechanical properties to the base metal, in which the Yield Stress (YS), ultimate tensile strength (UTS), and elongation percentage (E%) were 76.4%, 86.5%, and 70% of base metal, respectively. In the welding area, RP-FSW specimens had smaller average grain size and higher hardness values than AP-FSW specimens.

Analysis of Friction Stir Welding Tool Offset on the Bonding and Properties of Al–Mg–Si Alloy T-Joints

Research on T-configuration aluminum constructions effectively decreases fuel consumption, increases strength, and develops aerial structures. In this research, the effects of friction stir welding (FSW) tool offset (TO) on Al–Mg–Si alloy mixing and bonding in T-configurations is studied. The process is simulated by the computational fluid dynamic (CFD) technique to better understand the material mixing flow and the bonding between the skin and flange during FSW. According to the results, the best material flow can be only achieved at an appropriate TO. The appropriate TO generates enough material to fill the joint line and results in formation of the highest participation of the flange in the stir zone (SZ) area. The results show that, in the T-configuration, FSW joints provide raw materials from the retreating side (RS) of the flange that play a primary role in producing a sound mixing flow. The selected parameters were related to the geometric limitations of the raw sheets considered in this study. The failure point of all tensile samples was located on the flange. Surface tunneling is the primary defect in these joints, which is produced at high TOs. Among the analyzed cases, the most robust joint was made at +0.2 mm TO on the advancing side (AS), resulting in more than 60% strength of the base aluminum alloy being retained.