Thermal conductivity and bending strength of SiC composites reinforced by pitch-based carbon fibers

In this work, pitch-based carbon fibers were utilized to reinforce silicon carbide (SiC) composites via reaction melting infiltration (RMI) method by controlling the reaction temperature and resin carbon content. Thermal conductivities and bending strengths of composites obtained under different preparation conditions were characterized by various analytical methods. Results showed the formation of SiC whiskers (SiCw) during RMI process according to vapor—solid (VS) mechanism. SiCw played an important role in toughening the Cpf/SiC composites due to crack bridging, crack deflection, and SiCw pull-out. Increase in reaction temperature during RMI process led to an initial increase in thermal conductivity along in-plane and thickness directions of composites, followed by a decline. At reaction temperature of 1600 °C, thermal conductivities along the in-plane and thickness directions were estimated to be 203.00 and 39.59 W/(m·K), respectively. Under these conditions, bending strength was recorded as 186.15±3.95 MPa. Increase in resin carbon content before RMI process led to the generation of more SiC matrix. Thermal conductivities along in-plane and thickness directions remained stable with desirable values of 175.79 and 38.86 W/(m·K), respectively. By comparison, optimal bending strength improved to 244.62±3.07 MPa. In sum, these findings look promising for future application of pitch-based carbon fibers for reinforcement of SiC ceramic composites.

Influence of SiC Content on Microstructure, Dislocation Density and Mechanical Behavior of Cu/SiC Composite

The present investigation has examined the impact of micro-SiC on microstructure, dislocation and mechanical behavior of Cu/SiC composite. The micro-composite samples have been fabricated under a constant pressure (480 MPa) and sintered temperature (860oC) for 2 h. The sintering process was performed under argon gas. The microstructure examination was conducted using SEM/EDS and XRD diffraction. The SiC contents were 0, 5, 10,15,20,25 and 30 volume fraction. The outcomes showed that the density was significantly decreased with an increase of silicon carbide content. The relative densities of Cu and Cu/SiC composites was ranged from 91.24% to 83.56% for pure Cu and Cu/30 vol%SiC composites. The copper crystallite size was reduced with growing SiC content while the hardness, ultimate and yield compressive strength increased with increment of SiC volume fraction to 20% vol. The values of hardness, ultimate and yield compressive strength increased to 231 HV,343 and 176 N/mm2 , respectively for the composite sample containing 20% SiC particles with a percentage increase of 75%,26.6% and 57.2% compared with pure Cu.

Fabrication and characterization of SiC-reinforced Al-4032 metal matrix composites

Aluminium metal matrix composites (AMCs) have become quite popular for light weight, low cost, and good workability. The present work reports the impact of silicon carbide (SiC) reinforcement on the physical, microstructural, and mechanical characteristics of Al-4032/SiC composites with 4, 6, 8% of SiC (particle size 54μm) fabricated through bottom pouring stir casting. Density and porosity measurements of all three AMCs have been performed using the rule of mixture. The microstructure of the AMC samples has been analyzed using an optical microscope (OM), x-ray diffraction analysis (XRD), and scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS). The mechanical properties, in terms of the ultimate tensile strength (UTS), elongation, micro-hardness, and impact toughness of the AMCs have also been obtained according to American society for testing and materials (ASTM) standards. A maximum 1.52% increase in theoretical density, while a maximum 2.92% decrease in experimental density has been recorded for 8% reinforcement. The UTS, microhardness, and impact toughness of the AMC have been found to improve significantly owing to the addition of ceramic particles. The uniform distribution of SiC particles all over base Al-4032 matrix material has been noticed by SEM and OM for AMCs up to 6% reinforcement.