Inhibition Effect of Ti on the Formation of Martensite Lath in 14Cr Oxide Dispersion Strengthened Steel

Three model powders defined as MP powders (milled pre-alloyed powders), mixed powders (MX, 50 wt.% MP powders + 50 wt.% Oxide-Dispersion Strengthened powders) and Oxide Dispersion Strengthened (ODS) powders (alloyed pre-alloyed powders with the addition of Ti and Y2O3) are obtained under identical ball milling parameters. These powders are then consolidated under same sintering condition by spark plasma sintering (SPS) in order to investigate the formation mechanism of martensite lath in the MP steel and the effect of Ti on the stability of ferrite. The results indicate that the addition of Y2O3 and Ti powders can act as friction material during the mechanical alloying process, thus promoting the refinement effect. The formation of martensite lath in the MP steel is attributed to the local Cr depletion resulted from the large amounts of M23C6 precipitation. Ti possesses a strong affinity to C and long range diffusion ability, which efficiently prevents the martensite lath formation and local Cr depletion. Present study supports the conclusion that the lack of martensite in the MX and ODS steel is due to the addition of Ti. Secondary phases in these steels are identified and analyzed as well.

A Hydrogen Embrittlement Mechanism for Sensitized Types 304, 316 and 310 Austenitic Stainless Steels

The hydrogen embrittlement behavior of sensitized types 304, 316 and 310 in boiling saturated magnesium chloride solutions was explained in more details in terms of an inhibiting effect of chloride ions, martensite transformation, Cr depletion, HELP, and the degree of corrosiveness through the comparison with those for the solution annealed steels. Furthermore, a transgranular HE (TG-HE) cracking mode that was not observed for the solution annealed steels was discussed as well as IG-HE. Then a TG-HE mechanism for sensitized austenitic stainless steels was proposed, while the IG-HE mechanism for solution annealed austenitic stainless steels was discussed in details and was applied to IG-HE of sensitized austenitic stainless steels. It was also pointed out that the occurrence of both TG-HE and IG-HE was explained with an identical concept.