The Effect of Different Pre-Surface Finishing Method on the Aluminium Anodization of the 6XXX Series Alloy

In this study, the effect of different pre-surface finishing method on the aluminium anodization was investigated for AA 6063 alloy. Within the scope of pre-surface finishing method which is acidic solution concentrations and process time were determined. Acidic solution was determined by using hydrofluoric acid (HF) and nitric acid (HNO3). Also Gresoff LIM-5 LV chemical was used with different concentrations and process time for degreasing process. The etching effect of acidic solution on aluminium samples was investigated. The optimal etching behaviour was obtained with 1.0% concentration of HF and 3.2% concentration of HNO3 at 10 minutes process time. Also optimal surface properties were observed with 1.0% concentration of Gresoff LIM-5 LV at 12 minutes process time. Then anodic oxidation was performed by using 180 g / L sulfuric acid (H2SO4) and 18 volt (V). Surface morphology of the final aluminium profiles were examined with SEM analysis, Roughness, Gloss and Thickness tests.

Review On Progress of 7xxx Series Aluminum Alloy Materials

Since the first generation of 7xxx superhard aluminum alloy was investigated in 1930, hitherto the fifth generation aluminum alloy materials with high comprehensive properties such as high static strength, high strength, heat resistance, high toughness, damage resistance, low density and low quenching sensitivity have been improved and developed. This paper reviews the progress of 7xxx aluminum alloy materials in composition, microstructure, properties, preparation methods, heat treatment strengthening and applications from 2014 to 2021. The effect of adding trace elements on microstructure and properties of 7xxx series alloy and the problems existing in aging precipitation characteristics and reinforcement mechanism are discussed. The future development direction of 7xxx superhard aluminum alloy is prospected by optimizing heat treatment technological, adding appropriate trace elements to alloy and controlling alloy microstructure.