Inspired by steel forming strategies, this study focuses on the effect of differential cooling on mechanical properties and precipitation kinetics during hot stamping of high strength AA7075 alloy. For this aim, different forming strategies were performed using segmented and differentially heated forming tools to provide locally tailored microstructures. Upon processing, uniaxial tensile tests and hardness measurements were used to characterize the mechanical properties after the aging treatment. Microstructure investigations were conducted to examine the strengthening mechanisms using the electron channeling contrast imaging (ECCI) technique in a scanning electron microscope (SEM). Based on the obtained results, it can be deduced that the tool temperatures play a key role in influencing the mechanical properties. Lower tool temperatures result in higher material strength and higher tool temperatures in lower mechanical properties. By changing the cooling rate with the use of differently heated forming tools, the mechanical properties can be controlled. Microstructure investigations revealed the formation of very fine and homogeneously distributed particles at cooled zones, which were associated with elevated mechanical properties due to the suppression of second phase particle formation during cooling. In contrast, coarse particles were observed at lower cooling rates, explaining the lower material strength found in these zones.
Grain Refinement by Second Phase Particles under Applied Stress in ZK60 Mg Alloy with Y through Phase Field Simulation