Photo-induced changes in the bulk density of gap states in hydrogenated amorphous silicon associated with the Staebler-Wronski effect

Solar Cells ◽  
1983 ◽  
Vol 9 (1-2) ◽  
pp. 119-131 ◽  
Author(s):  
J.David Cohen ◽  
David V. Lang ◽  
James P. Harbison ◽  
A.M. Sergent
Keyword(s):  
Amorphous Silicon ◽  
Bulk Density ◽  
Hydrogenated Amorphous Silicon ◽  
Staebler Wronski Effect ◽  
Gap States ◽  
Induced Changes ◽  
Hydrogenated Amorphous

Contributions of D0 and non-D0 Gap States to the Kinetics of Light Induced Degradation of Amorphous Silicon under 1 sun Illumination

2001 ◽  
Vol 664 ◽  
Author(s):  
J. Pearce ◽  
X. Niu ◽  
R. Koval ◽  
G. Ganguly ◽  
D. Carlson ◽  
...  
Keyword(s):  
Amorphous Silicon ◽  
Degradation Kinetics ◽  
Hydrogen Dilution ◽  
Spin Resonance ◽  
The Creation ◽  
Staebler Wronski Effect ◽  
Gap States ◽  
Induced Changes ◽  
Induced Defects ◽  
Hydrogenated Amorphous

ABSTRACTLight induced changes to 1 sun degraded steady state (DSS) have been investigated on hydrogenated amorphous silicon (a-Si:H) p-i-n solar cells and corresponding films fabricated with and without hydrogen dilution of silane. Striking similarities are found for the degradation kinetics, between the electron mobility lifetime (μτ) products and the corresponding fill factors (FF). These correlations that exist for both intrinsic materials at temperatures between 25 and 100°C, are present for the DSS as well as in the kinetics, which exihibit distinctly different dependence on temperature. No such correlations are present between μτ, FF and densities of D0 defects, measured with subgap absorption α(E) at 1.2eV, and electron spin resonance (ESR). The creation of non-D0 defects is also clearly indicated by the temperature dependence of the kinetics and the changes in the shape of α(E) with the results suggesting the presence of more than one mechanism for the creation of light induced defects associated with the Staebler-Wronski effect (SWE).

Mechanical Spectroscopy Study on the Light Soaking Effect on Hydrogenated Amorphous Silicon

2012 ◽  
Vol 184 ◽  
pp. 416-421 ◽  
Author(s):  
H. Mizubayashi ◽  
I. Sakata ◽  
H. Tanimoto
Keyword(s):  
Internal Friction ◽  
Temperature Dependence ◽  
Amorphous Silicon ◽  
Hydrogenated Amorphous Silicon ◽  
Wide Distribution ◽  
Activation Energies ◽  
Mechanical Spectroscopy ◽  
Induced Changes ◽  
Mild Temperature ◽  
Hydrogenated Amorphous

For hydrogenated amorphous silicon (a-Si:H) films deposited at temperatures between 423 K and 623 K (a-Si:H423Kand so on), the light-induced changes in the internal friction between 80 K and 400 K were studied. The internal friction is associated with H2motion in microvoid networks, and shows the mild temperature dependence between about 80 K and 300 K (Q-180-300K) and the almost linear increase above 300 K (Q-1>300K). BothQ-180-300KandQ-1>300Kdecrease with increasing the deposition temperature, and show the mild temperature dependence ina-Si:H623K. The white light soaking with 100 mW/cm2(WLS100and so on) below 300 K caused a change inQ-180-300Kand no changes inQ-1>300K, respectively, and the light-induced changes inQ-180-300Krecovered after annealing at 423 K. The wide distribution of activation energies for H2motions between microvoids indicate that most of neighboring microvoids are connected through windows, i.e., the microvoid networks are existing ina-Si:H, and the spatially loose or solid structures are responsible for the low or high activation energies for the H2motion between microvoids, respectively. Furthermore, the light-induced hydrogen evolution (LIHE) was observed for WLS200to WLS400in a vacuum between 400 and 500 K, resulting in the disappearance of the internal friction due to the H2motion in the microvoid network.

Improved Light Soaking Stability of R.F. Sputter Deposited Amorphous Silicon

1991 ◽  
Vol 219 ◽  
Author(s):  
A. Wynveen ◽  
J. Fan ◽  
J. Kakalios ◽  
J. Shinar
Keyword(s):  
Amorphous Silicon ◽  
Hydrogen Content ◽  
Defect Density ◽  
Hydrogenated Amorphous Silicon ◽  
Dark Conductivity ◽  
Initial Defect ◽  
Optical Gap ◽  
Sputter Deposited ◽  
Staebler Wronski Effect ◽  
Hydrogenated Amorphous

ABSTRACTStudies of r.f. sputter deposited hydrogenated amorphous silicon (a-Si:H) find that the light induced decrease in the dark conductivity and photoconductivity (the Staebler-Wronski effect) is reduced when the r.f. power used during deposition is increased. The slower Staebler-Wronski effect is not due to an increase in the initial defect density in the high r.f. power samples, but may result from either the lower hydrogen content or the smaller optical gap found in these films.

Sign in / Sign up

Export Citation Format

Share Document