Abstract
Herein, the evolution of reduction process of ultrafine tungsten powder in industrial conditions was investigated. The transition process of morphology and composition was examined via SEM, XRD, and calcination experiments. The results show that the reduction sequence of WO2.9 was WO2.9 → WO2.72 → WO2 → W on the surface, but WO2.9 → WO2 → W inside the oxide particles. With the aid of chemical vapor transport of WO
x
(OH)
y