Preparation and Characterization of Soybean Oil-based Flame Retardant Rigid Polyurethane Foams Containing Phosphaphenanthrene Groups

2020 ◽  
Vol 17 (10) ◽  
pp. 760-771
Author(s):  
Qirui Gong ◽  
Niangui Wang ◽  
Kaibo Zhang ◽  
Shizhao Huang ◽  
Yuhan Wang
Keyword(s):  
Soybean Oil ◽  
Flame Retardant ◽  
Chemical Structure ◽  
Cell Structure ◽  
Polyurethane Foams ◽  
Limiting Oxygen Index ◽  
Rigid Polyurethane Foams ◽  
Degradation Activation Energy ◽  
Ft Ir

A phosphaphenanthrene groups containing soybean oil based polyol (DSBP) was synthesized by epoxidized soybean oil (ESO) and 9,10-dihydro-oxa-10-phosphaphenanthrene-10-oxide (DOPO). Soybean oil based polyol (HSBP) was synthesized by ESO and H2O. The chemical structure of DSBP and HSBP were characterized with FT-IR and 1H NMR. The corresponding rigid polyurethane foams (RPUFs) were prepared by mixing DSBP with HSBP. The results revealed apparent density and compression strength of RPUFs decreased with increasing the DSBP content. The cell structure of RPUFs was examined by scanning electron microscope (SEM) which displayed the cells as spherical or polyhedral. The thermal degradation and flame retardancy of RPUFs were investigated by thermogravimetric analysis, limiting oxygen index (LOI), and UL 94 vertical burning test. The degradation activation energy (Ea) of first degradation stage reduced from 80.05 kJ/mol to 37.84 kJ/mol with 80 wt% DSBP. The RUPF with 80 wt% DSBP achieved UL94 V-0 rating and LOI 28.3. The results showed that the flame retardant effect was mainly in both gas phase and condensed phase.

scholarly journals Synthesis and characterization of different soybean oil-based polyols with fatty alcohol and aromatic alcohol

e-Polymers ◽  
2021 ◽  
Vol 21 (1) ◽  
pp. 491-499
Author(s):  
Fukai Yang ◽  
Hao Yu ◽  
Yuyuan Deng ◽  
Xinyu Xu
Keyword(s):  
Molecular Weight ◽  
Soybean Oil ◽  
Retention Time ◽  
Ring Opening ◽  
Isoamyl Alcohol ◽  
Synthesis And Characterization ◽  
Intermolecular Force ◽  
H Nmr ◽  
Epoxy Groups

Abstract In this article, five kinds of soybean oil-based polyols (polyol-E, polyol-P, polyol-I, polyol-B, and polyol-M) were prepared by ring-opening the epoxy groups in epoxidized soybean oil (ESO) with ethyl alcohol, 1-pentanol, isoamyl alcohol, p-tert-butylphenol, and 4-methoxyphenol in the presence of tetrafluoroboric acid as the catalyst. The SOPs were characterized by FTIR, 1H NMR, GPC, viscosity, and hydroxyl numbers. Compared with ESO, the retention time of SOPs is shortened, indicating that the molecular weight of SOPs is increased. The structure of different monomers can significantly affect the hydroxyl numbers of SOPs. Due to the large steric hindrance of isoamyl alcohol, p-hydroxyanisole, and p-tert-butylphenol, SOPs prepared by these three monomers often undergo further dehydration to ether reactions, which consumes the hydroxyl of polyols, thus forming dimers and multimers; therefore, the hydroxyl numbers are much lower than polyol-E and polyol-P. The viscosity of polyol-E and polyol-P is much lower than that of polyol-I, polyol-B, and polyol-M. A longer distance between the molecules and the smaller intermolecular force makes the SOPs dehydrate to ether again. This generates dimer or polymers and makes the viscosity of these SOPs larger, and the molecular weight greatly increases.

Controllable Synthesis and Characterization of Soybean-Oil-Based Hyperbranched Polymers via One-Pot Method

2018 ◽  
Vol 6 (10) ◽  
pp. 12865-12871 ◽  
Author(s):  
Xuan Qin ◽  
Yong He ◽  
Shafilluah Khan ◽  
Baihui Zhang ◽  
Fanxing Chen ◽  
...  
Keyword(s):  
Soybean Oil ◽  
Hyperbranched Polymers ◽  
Synthesis And Characterization ◽  
Controllable Synthesis ◽  
One Pot

Synthesis and Characterization of Alkyd Resin Based on Soybean Oil Polyols

2011 ◽  
Vol 239-242 ◽  
pp. 1721-1724 ◽  
Author(s):  
Xiao Qing Zheng ◽  
Li Ting Yang ◽  
Kun Peng Wang
Keyword(s):  
Maleic Anhydride ◽  
Soybean Oil ◽  
Phthalic Anhydride ◽  
Alkyd Resin ◽  
Ring Opening ◽  
Molar Ratio ◽  
Synthesis And Characterization ◽  
Hydroxyl Value

Soybean oil-based alkyd resin was prepared using soy-based polyol, maleic anhydride and phthalic anhydride. The soy-based polyol was obtained through the epoxidization of soybean oil, followed by ring-opening with methanol and, the hydroxyl values of soybean oil-based polyols used in this reaction is 169.93 mgKOH/g. In the reactions of soy-based polyol, maleic anhydride and phthalic anhydride, the molar ratio of hydroxyl value is equal to carboxyl value and the molar ratio of maleic anhydride to phthalic anhydride is 2:1, 1:1 and 1:2, respectively. 1% hydroquinone based on total reactants was used as inhibitor of polymerization, 1% dibutyltin oxide was used as catalyst.