Thiol-Ene Coupling of High Oleic Sunflower Oil towards Application in the Modification of Flexible Polyurethane Foams

High oleic sunflower oil-based polyol was obtained by thiol-ene coupling and applied in the preparation of flexible polyurethane foams. The photochemically initiated thiol-ene click reaction was carried out under UV irradiation using 2-mercaptoethanol. Bio-based polyol with hydroxyl value of 201.4 mg KOH/g was used as 30 wt% substituent of petrochemical polyether polyol in the formulations of flexible foams. Both reference foams, as well as foams modified with bio-based polyol, were formulated to have various isocyanate indices (0.85, 0.95, 1.05). Flexible foams were compared in terms of their thermomechanical properties and analyzed using FT-IR and SEM microscopy. Modification with bio-based polyol resulted in foams with superior compression properties, higher support factor, and lower resilience than reference foams. TGA and FT-IR curves confirmed the presence of urethane/urea and ether linkages in the polyurethane matrix. Moreover, double glass transition temperature corresponding to soft and hard segments of polyurethane was observed by DSC proving the phase-separated morphology.

Characterization and Properties of Water-Blown Rigid Polyurethane Foams Reinforced with Silane-Modified Nanosepiolites Functionalized with Graphite

In the present study, a promising flame retardant consisting of 80 wt% silane-modified nanosepiolites functionalized with 20 wt% graphite (SFG) is used to obtain a synergistic effect principally focussed on the thermal stability of water-blown rigid polyurethane (RPU) foams. Density, microcellular structure, thermal stability and thermal conductivity are examined for RPU foams reinforced with different contents of SFG (0, as reference material, 2, 4 and 6 wt%). The sample with 6 wt% SFG presents a slightly thermal stability improvement, although its cellular structure is deteriorated in comparison with the reference material. Furthermore, the influence of SFG particles on chemical reactions during the foaming process is studied by FTIR spectroscopy. The information obtained from the chemical reactions and from isocyanate consumption is used to optimize the formulation of the foam with 6 wt% SFG. Additionally, in order to determine the effects of functionalization on SFG, foams containing only silane-modified nanosepiolites, only graphite, or silane-modified nanosepiolites and graphite added separately are studied here as well. In conclusion, the inclusion of SFG in RPU foams allows the best performance to be achieved.

Low density rigid polyurethane foam incorporated with renewable polyol as sustainable thermal insulation material

Palm olein-based polyol (PP) was used as a partial replacement for commercial sucrose/glycerine initiated polyether polyol (GP) for the production of low density rigid polyurethane foams (RPUFs). The hydroxyl value (OHV) of the GP was 380 mg KOH/g, whereas the OHV for PP was 360 mg KOH/g. The RPUFs were prepared by replacing the GP with PP up to 50 parts per hundred parts of polyols (pph). Characterisation of the RPUFs, including density, compressive strength and strain, cell morphology and thermal conductivity ( k-value), were conducted. The dimensional stability of the foams was also evaluated. The study showed improvement in the compressive strength and strain for palm-based RPUFs with the incorporation of up to 30 pph PP as compared to GP foams. The lowest k-value (0.0232 W/m.K) of RPUF with density below 30 kg/m3 was obtained with the incorporation of 10 pph PP. This was due to the smallest and uniform pore size distribution observed using SEM images. The dimensional stability of the RPUF prepared from PP was within the acceptable range. Thus, the RPUFs made from PP are potential candidates to be used as insulation for refrigerators, freezers and piping.

Exploring the Potential to Repurpose Flexible Moulded Polyurethane Foams as Acoustic Insulators

Polyurethane flexible foams are widely used for a variety of applications to improve comfort and durability. Their long-term frequent use inevitably leads to the generation of waste that needs to be treated. The recycling and reuse of polyurethane waste are essential to achieve an environmentally friendly economy. The present study investigates the potential to reuse and repurpose flexible polyurethane foam from automotive seat cushion waste materials. Flexible foams were prepared with different hardnesses using isocyanate–polyol ratios between 0.8 and 1.2 NCO-index. Dry heat aging tests were performed to mimic the long-term usage of the materials. The decrease in compressive strength was compared with the change in acoustic damping properties before and after the aging tests using an acoustic tube, and the change in foam cell structures was also analyzed by micro-CT. On the basis of the results obtained, although the foam systems are no longer suitable to be used as seat cushions due to aging, they can still be used as sound insulation materials within a given frequency range, as their sound absorption capacity is suitable for such purpose.

Cryogenic thermal insulating and mechanical properties of rigid polyurethane foams blown with hydrofluoroolefin: Effect of perfluoroalkane

The effect of perfluoroalkane (PFA) on the morphology, thermal conductivity, mechanical properties and thermal stability of rigid polyurethane (PU) foams was investigated under ambient and cryogenic conditions. The PU foams were blown with hydrofluorolefin. Morphological results showed that the minimum cell size (153 μm) was observed when the PFA content was 1.0 part per hundred polyols by weight (php). This was due to the lower surface tension of the mixed polyol solution when the PFA content was 1.0 php. The thermal conductivity of PU foams measured under ambient (0.0215 W/mK) and cryogenic (0.0179 W/mK at −100°C) conditions reached a minimum when the PFA content was 1.0 php. The low value of thermal conductivity was a result of the small cell size of the foams. The above results suggest that PFA acted as a nucleating agent to enhanced the thermal insulation properties of PU foams. The compressive and shear strengths of the PU foams did not appreciably change with PFA content at either −170°C or 20°C. However, it shows that the mechanical strengths at −170°C and 20°C for the PU foams meet the specification. Coefficient of thermal expansion, and thermal shock tests of the PU foams showed enough thermal stability for the LNG carrier’s operation temperature. Therefore, it is suggested that the PU foams blown by HFO with the PFA addition can be used as a thermal insulation material for a conventional LNG carrier.

Bio-Based Rigid Polyurethane Foams Modified with Phosphorus Flame Retardants

Rigid polyurethane foams (RPURF) containing a bio-polyol from rapeseed oil and different phosphorus-based flame retardants were obtained. Triethyl phosphate (TEP), dimethyl propane phosphonate (DMPP) and cyclic phosphonates Addforce CT 901 (20 parts per hundred polyol by weight) were used in the synthesis of RPURF. The influence of used flame retardants on foaming process, cell structure, and physical–mechanical properties as well as flammability of RPURF were examined. The addition of flame retardants influenced the parameters of the cellular structure and decreased compressive strength. All obtained foam materials had a low thermal conductivity coefficient, which allows them to be used as thermal insulation. The research results of bio-based RPURF were compared with foams obtained without bio-polyol. All modified materials had an oxygen index above 21 vol%; therefore, they can be classified as self-extinguishing materials. The analysis of parameters obtained after the cone calorimeter test showed that the modified RPURF have a lower tendency to fire development compared to the reference foams, which was particularly noticeable for the materials with the addition of DMPP.

High performance biobased pour-in-place rigid polyurethane foams from facile prepared castor oil-based polyol: Good compatibility with pentane series blowing agent

In this paper, biobased and environmentally friendly rigid polyurethane foams (RPUF) from high hydroxyl value castor oil-based polyols have been prepared without the addition of petroleum-based polyols in the formulation. The new Biopolyol with high hydroxyl value was designed on the basis of the analysis of functionality, structure and hydroxyl value relation and synthesized directly from castor oil in a facile one-pot three-step system. A series of Biopolyols with hydroxyl values in the range of 550–650 mg KOH/g were obtained through transesterification, epoxidation, and hydrolysis. The Biopolyol chemical structure was characterized using FT-IR,1H NMR spectroscopies. The formulated blend polyol with amine catalysts and cyclopentane as a blowing agent have good cyclopentane solubility and phase separation between cyclopentane and polyol was not observed after 30 days. The foaming characteristics were evaluated and improved results were obtained. The thermal conductivity, thermal stability, compressive strength, morphology, dimensional stability, density, and foam flow of the RPUFs were characterized. The results are compared with RPUF prepared using standard commercial polyether polyols for pour-in-place RPUFs. The prepared biobased RPUFs from Biopolyol was able to reach the required satisfactory properties for the appliance industry.