The present work deals with the relationship between microstructure and mechanical properties of A356 aluminum alloy which was produced via thixocasting process under different casting conditions. Feedstock billets were heated to a target temperature to obtain a semi-solid slurry with the required solid fraction. Some billets were heated to a fully-melted condition. In order to obtain fine and spheroidized Al grains, some billets for the partially melting were compressed axially by 33% at a room temperature before heating. The completely-melted and partially-melted slurries were die-cast by using a die-cast machine, and hour glass-shaped rod-type tensile specimens and small-size plate-type tensile specimens were obtained. Small cubic specimens were also collected from the die-cast products for microstructural evaluation. They were polished, and etched by Weck’s reagent. The partially-melted specimen which was compressed before heating shows the spherical Al grains. But the grain of the strain-free partially-melted specimen exhibited complicated morphology. The fully-melted specimen shows the fine and dendrite structure.
Effect of Ti on microstructure and mechanical properties of die-cast Al-Mg-Zn-Si alloy