Purpose
The purpose of this paper is to evaluate and compare the protective, anticorrosion properties of silane- and polyrhodanine-based bilayer coatings pRh/IBTES and IBTES/pRh on an X20Cr13 stainless steel substrate.
Design/methodology/approach
IBTES/pRh and pRh/IBTES have been coated using the dip-coating method and the cyclic voltammetry technique. The electrochemical measurements have been used to assess the anticorrosion properties of the resulting bilayer coatings. Morphological and chemical characterizations have been performed using scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS).
Findings
The results clearly show that the combination of both the deposits of polyrhodanine and silane yields a more protective structure that affords better protection against corrosion with time. The best barrier properties are achieved by the substrates coated with polyrhodanine film upon which silane is subsequently adsorbed – the pRh/IBTES bilayer coating.
Originality/value
The paper reveals that the procedure of modification of silane films with polyrhodanine had a marked effect on the anti-corrosive performance of the obtained two types of bilayers coatings (pRh/IBTES, IBTES/pRh) applied on a stainless steel surface. The coating where polyrhodanine was first electrodeposited on the steel surface and then the silane layer adsorbed (pRh/IBTES) achieved the best protective properties.
Nitriding of 304 Steel by a Nitrogen Plasma: Increasing Corrosion Resistance