scholarly journals Carbonization of Lignin Extracted from Liquid Waste of Coconut Coir Delignification

2020 ◽  
Vol 20 (4) ◽  
pp. 842
Author(s):  
Widiyastuti Widiyastuti ◽  
Mahardika Fahrudin Rois ◽  
Heru Setyawan ◽  
Siti Machmudah ◽  
Diky Anggoro
Keyword(s):  
Pore Size ◽  
Surface Area ◽  
Liquid Waste ◽  
Nitrogen Adsorption ◽  
Nitrogen Atmosphere ◽  
Precipitation Method ◽  
X Ray Diffraction ◽  
Coconut Coir ◽  
Xrd Patterns ◽  
Adsorption Desorption

Lignin as a by-product of the pulping process is less widely used for worth materials. In this study, the utilization of lignin by-product of the soda delignification process of coconut coir converted to the activated carbon by a simple precipitation method followed by the carbonization at various temperatures is presented. The by-product liquor of the soda delignification process having a pH of 13.4 was neutralized by dropping of hydrochloric acid solution to achieve the pH solution of 4 resulting in the lignin precipitation. The precipitated was washed, filtered, and dried. The dried lignin was then carbonized under a nitrogen atmosphere at various temperatures of 500, 700, and 900 °C. The dried lignin and carbonized samples were characterized using SEM, XRD, FTIR, and nitrogen adsorption-desorption analyzer, to examine their morphology, X-Ray diffraction pattern, chemical bonding interaction, and surface area-pore size distribution, respectively. The characterization results showed that the functional groups of lignin mostly disappeared gradually with the increase of temperature approached the graphite spectrum. The XRD patterns confirmed that the carbonized lignin particles were amorphous and assigned as graphitic. All samples had a pore size of 3–4 nm classified as mesoporous particles. This study has shown that the carbonization lignin at a temperature of 700 °C had the highest surface area (i.e. 642.5 m2/g) in which corresponds to the highest specific capacitance (i.e. 28.84 F/g).

Synthesis of Novel Core-Shell Structured Hydroxyapatite/Meso-Silica for Removal of Methylene Blue from Aqueous Solutions

2012 ◽  
Vol 463-464 ◽  
pp. 543-547 ◽  
Author(s):  
Cheng Feng Li ◽  
Xiao Lu Ge ◽  
Shu Guang Liu ◽  
Fei Yu Liu
Keyword(s):  
Methylene Blue ◽  
Aqueous Solutions ◽  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Low Cost ◽  
Nitrogen Adsorption ◽  
Precipitation Method ◽  
Core Shell ◽  
Adsorption Desorption

Core-shell structured hydroxyapatite (HA)/meso-silica was prepared and used as absorbance of methylene blue (MB). HA/meso-silica was synthesized in three steps: preparation of nano-sized HA by wet precipitation method, coating of dense silica and deposition of meso-silica shell on HA. As-received samples were characterized by Fourier transformed infare spectra, small angle X-ray diffraction, nitrogen adsorption-desorption isotherm and transmission electron microscopy. A wormhole framework mesostructure was found for HA/meso-silica. The specific surface area and pore volume were 128 m2•g-1 and 0.36 cm3•g-1, respectively. From the adsorption isotherm, HA/meso-silica with the great specific surface area exhibited a prominent adsorption capacity of MB (134.0 mg/g) in comparison with bare HA (0 mg/g). This study might shed light on surface modification of conventional low-cost adsorbents for removal of organic pollutants from aqueous solutions.

Synthesis and Photocatalytic Property of BiVO4/FeVO4 Composite Novel Photocatalyst

2010 ◽  
Vol 129-131 ◽  
pp. 784-788 ◽  
Author(s):  
Min Wang ◽  
Qiong Liu ◽  
Dong Zhang
Keyword(s):  
Photocatalytic Activity ◽  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Photocatalytic Property ◽  
Precipitation Method ◽  
X Ray Diffraction ◽  
Experimental Conditions ◽  
Triclinic Phase ◽  
Xrd Patterns

BiVO4/FeVO4 composite photocatalyst samples were prepared by calcining the mixture of FeVO4 and BiVO4 precusor which were prepared through liquid phase precipitation method for further increasing the photocatalytic efficiency of FeVO4. The catalysts were characterized by X-ray diffraction (XRD), scanning electron microsoope（SEM）and specific surface area (BET). The photocatalytic activity was evaluated by photocatalytic degradation of methyl orange (MO) solution under visible light. The XRD patterns indicate that BiVO4/FeVO4 composite photocatalysts consist of triclinic phase and the lattice was not distorted beacause of doping Bi. But the morphology change greatly and the specific surface area has little change. In the experimental conditions used, the optimal photocatalytic activity for all the prepared samples was reached when BiVO4 doping was 22 at%. The degradation rate of MO was increased by 20％ or so than that of pure FeVO4.

Positron Annihilation Study of Porous ZnO Synthesized with Soft Template

2017 ◽  
Vol 373 ◽  
pp. 299-302
Author(s):  
Bo Zhou ◽  
Chong Yang Li ◽  
Ning Qi ◽  
Zhi Quan Chen
Keyword(s):  
Pore Size ◽  
Positron Lifetime ◽  
Nitrogen Adsorption ◽  
Soft Template ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Long Lifetime ◽  
Positron Annihilation Study ◽  
Adsorption Desorption

Porous ZnO were synthesized with soft template method using zinc acetate Zn (CH3COO)2·2H2O as precursor and block copolymer F127 as the surfactant. Nitrogen adsorption-desorption measurements indicate that the ZnO sample contains large pores with mean diameter of about 30 nm. However, both small-angle X-ray diffraction and transmission electron microscope measurements indicate that the pore ordering is missing. Positron lifetime measurements reveal two long lifetime components in the porous ZnO. The longest lifetime τ4 (75 ns) corresponds to ortho-positronium (o-Ps) annihilation in large pores. The pore size estimated from τ4 is about 10.6 nm. This is much smaller than that estimated from Nitrogen adsorption-desorption measurements. In addition, the intensity I4 is only about 2.2%. This is probably due to the chemical quenching and/or inhibition of positronium formation induced by ZnO, which reduces o-Ps lifetime and intensity, and leads to under estimation of the pore size.

The Different Morphology of Co3O4 Catalysts and Application in the Abatement of Carbon Monoxide

2021 ◽  
Vol 21 (12) ◽  
pp. 6082-6087
Author(s):  
Chih-Wei Tang ◽  
Hsiang-Yu Shih ◽  
Ruei-Ci Wu ◽  
Chih-Chia Wang ◽  
Chen-Bin Wang
Keyword(s):  
Carbon Monoxide ◽  
Catalytic Activity ◽  
Co Oxidation ◽  
Nitrogen Adsorption ◽  
Catalytic Performance ◽  
Precipitation Method ◽  
X Ray Diffraction ◽  
X Ray ◽  
Temperature Programmed ◽  
Adsorption Desorption

The increase of harmful carbon monoxide (CO) caused by incomplete combustion can affect human health even lead to suffocation. Therefore reducing the CO discharged by vehicles or factories is urgent to improve the air quality. The spinel cobalt (II, III) oxide (Co3O4) is an active catalyst for CO abatement. In this study, we tried to fabricate dispersing Co3O4 via the dispersion-precipitation method with acetic acid, formic acid, and oxalic acid as the chelating dispersants. Then, the asprepared samples were calcined at 300 ºC for 4 h to obtain active catalysts, and assigned as Co(A), Co(F) and Co(O) respectively, the amount of the dispersants used are labeled as I (0.12 mole), II (0.03 mole) and III (0.01 mole). For comparison, another CoAP sample was prepared via alkaliinduced precipitation and calcined at 300 ºC. All samples were characterized by X-ray diffraction (XRD), temperature-programmed reduction (TPR), scanning electron microscope (SEM), and nitrogen adsorption/desorption system, and the catalytic activity focused on the CO oxidation. The influence of chelating dispersant on the performance of abatement of CO was pursued in this study. Apparently, the results showed that the chelating dispersant can influence the catalytic activity of CO abatement. An optimized ratio of dispersant can improve the performance, while excess dispersant lessens the surface area and catalytic performance. The series of Co(O) samples can easily donate the active oxygen since the labile Co–O bonding and indicated the preferential performance than both Co(A) and Co(F) samples. The nanorod Co(O)-II showed preferential for CO oxidation, T50 and T90 approached 96 and 127 ºC, respectively. Also, the favorable durability of Co(O)-II sample maintains 95% conversion still for 50 h at 130 ºC and does not emerge deactivation.

A Facile Template Approach for Preparing Microstructures of Bimodal Crystalline Mesoporous Titania Powders

2012 ◽  
Vol 616-618 ◽  
pp. 1797-1800
Author(s):  
Yu Mei Gong ◽  
Qing Liang ◽  
Jing Chuan Song ◽  
Ling Ming Xia
Keyword(s):  
Electron Microscope ◽  
Surface Area ◽  
Nitrogen Adsorption ◽  
Mesoporous Titania ◽  
Mass Ratio ◽  
X Ray Diffraction ◽  
Average Pore ◽  
X Ray ◽  
Transmission Electron ◽  
Adsorption Desorption

This paper presents the preparation of bimodal crystalline macro-/mesoporous titania powders by using a pluronic polymer (EO20PO70EO20, P123) as a template through a hydrothermal treatment. The as-prepared powders were characterized by X-ray diffraction (XRD), nitrogen adsorption-desorption, scanning electron microscope (SEM) and transmission electron microscope (TEM). The results reveal that the amount of P123 has a significant effect on the surface area of the mesoporous titania. When the mass ratio of P123:TBOT is 1:14, the crystalline macro-/mesoporous titania has the largest surface area (120.96 m2/g), the average pore diameter of this sample reaches a minimum of 6.67 nm.

scholarly journals The Role of the Aluminum Source on the Physicochemical Properties of γ-AlOOH Nanoparticles

2020 ◽  
Vol 39 (1) ◽  
pp. 89
Author(s):  
Rafael Romero Toledo ◽  
Luis M. Anaya Esparza ◽  
J. Merced Martínez Rosales
Keyword(s):  
Electron Microscopy ◽  
Physicochemical Properties ◽  
Surface Area ◽  
Low Cost ◽  
Nitrogen Adsorption ◽  
Bet Surface Area ◽  
Precipitation Method ◽  
X Ray ◽  
Aluminum Salts ◽  
Adsorption Desorption

The effect on the physicochemical properties of aluminum salts on the synthesis of γ-AlOOH nanostructures has been investigated in detail using a hydrolysis-precipitation method. X-ray fluorescence (XRF), Fourier transform infrared spectroscopy (FTIR), X-ray powder diffraction (XRD), field-emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM), were used to characterize the synthesized samples. The specific surface area, pore size distribution and pore diameter of the different γ-AlOOH structures were discussed by the N2 adsorption-desorption analysis. According to the results of the nanostructure, characterization revealed that for synthesized γ-AlOOH nanostructures from AlCl3 and Al(NO3)3, obvious XRD peaks corresponding to the bayerite phase are found indicating an impure γ-AlOOH phase. Furthermore, the nitrogen adsorption-desorption analysis indicated that the obtained γ-AlOOH nanoparticles from Al2(SO4)3 of technical grade (95.0 % of purity) and low cost, possess a high BET surface area of approximately 350 m2/g, compared to the obtained nanostructures from aluminum sources reactive grade, which was attributed to the presence of Mg (0.9 wt.%) in its nanostructure.

scholarly journals Effect of Aluminum Incorporation into Mesoporous Aluminosilicate Framework on Drug Release Kinetics

2017 ◽  
Vol 2017 ◽  
pp. 1-9
Author(s):  
Raul-Augustin Mitran ◽  
Daniela Berger ◽  
Jeanina Pandele-Cusu ◽  
Cristian Matei
Keyword(s):  
Pore Size ◽  
Therapeutic Agent ◽  
Release Kinetics ◽  
Nitrogen Adsorption ◽  
Incipient Wetness Impregnation ◽  
X Ray Diffraction ◽  
Drug Molecules ◽  
Model Drug ◽  
Adsorption Desorption

Mesoporous silica materials are promising nanocarriers for the development of drug delivery systems. In this study, the influence of pore size, volume, surface area, and doping the silica framework on the release kinetics of a model drug, metoprolol, has been studied. 20% or 50% wt. therapeutic agent was loaded into the carrier mesopores through incipient wetness impregnation. The carriers and drug-loaded samples have been characterized by small- and wide-angle X-ray diffraction, FT-IR spectroscopy, scanning electron microscopy, and nitrogen adsorption-desorption isotherms. The in vitro release profiles have been fitted using a three-parameter kinetic model and they have been explained in terms of the release rate during the burst and sustained release stages and the fraction of drug molecules released during the burst stage. The silica framework doping with aluminum was found to decrease the amount of drug released in the burst stage, without affecting the other kinetic parameters. The therapeutic agent release rates depend mainly on the pore size and volume of the mesoporous carriers and drug-loaded samples.

Porous LiMn2O4 Microspheres With Different Pore Size: Preparation and Application as Cathode Materials for Lithium Ion Batteries

2018 ◽  
Vol 16 (1) ◽  
Author(s):  
Shiyou Li ◽  
Konglei Zhu ◽  
Jinliang Liu ◽  
Dongni Zhao ◽  
Xiaoling Cui
Keyword(s):  
Pore Size ◽  
Lithium Ion Batteries ◽  
Rate Capability ◽  
Lithium Ion ◽  
Nitrogen Adsorption ◽  
Electrochemical Performances ◽  
Discharge Process ◽  
Ion Diffusion ◽  
X Ray Diffraction ◽  
Adsorption Desorption

Three types of LiMn2O4 (LMO) microspheres with different pore size are prepared by a facile method, using porous MnCO3–MnO2 and Mn2O3 microspheres as the self-supporting template, for lithium ion batteries (LIBs) cathode material. Briefly, Mn2O3 and MnO2 microspheres are heated in air at 600 °C for 10 h to synthesize porous Mn2O3 spheres. Then the mixture of as-prepared spherical Mn2O3 and LiNO3 is calcined to obtain the LMOs. The morphology and structure of LMOs are characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and nitrogen adsorption/desorption analyses. The result shows that the maximum pore diameters of LMOs are 17 nm, 19 nm, and 11 nm, respectively. All LMOs microspheres are composed of similar sized nanoparticles; however, the surface of these microspheres is strewed with dense tinier pores or sparse larger pores. Generally, the nanoparticles will reduce the path of Li+ ion diffusion and increases the reaction sites for lithium insertion/extraction. Moreover, the pores can provide buffer spaces for the volume changes during charge–discharge process. The electrochemical performances of LMOs are investigated and LMO2 exhibits extremely good electrochemical behavior, especially the rate capability. The as-prepared LMO2 delivers a discharge capacity of 124.3 mAh g−1 at 0.5 C, retaining 79.6 mAh g−1 even at 5 C. The LMO2 sample also shows good capacity retention of 96.9% after 100 cycles at 0.5 C.

Effect of Polyethylene Glycol Additive on Structure and Performance of Active Alumina by Reverse Precipitation Method

2012 ◽  
Vol 487 ◽  
pp. 649-652
Author(s):  
Fang Hu ◽  
Jiao Ma ◽  
Yu Sheng Wu ◽  
Di Zhang
Keyword(s):  
Polyethylene Glycol ◽  
Nitrogen Adsorption ◽  
Precipitation Method ◽  
Infrared Analysis ◽  
X Ray Diffraction ◽  
X Ray ◽  
Active Alumina ◽  
And Performance ◽  
Adsorption Desorption ◽  
Reverse Precipitation

Active alumina (γ-Al2O3) was prepared from NaAlO2 and HNO3 by a reverse precipitation method with addition of polyethylene glycol (PEG). The effect of PEG additived in the different stages during the preparing process was investigated by powder X-ray diffraction (XRD), fourier transform infrared analysis (FTIR) and nitrogen adsorption-desorption. It was found that the mesoporous alumina sample with the PEG additived into the initial HNO3 solution was the most effective at improving the surface area and the pore volume of γ-Al2O3.

scholarly journals Zinc Titanate Nanopowders. Synthesis and Characterization

2021 ◽  
Author(s):  
M Gabal ◽  
Y.M. Al Angari
Keyword(s):  
Nitrogen Adsorption ◽  
Precipitation Method ◽  
X Ray Diffraction ◽  
Zinc Titanate ◽  
Low Dielectric ◽  
Transmission Electron ◽  
Different Temperatures ◽  
Precursor Decomposition ◽  
Co Precipitation ◽  
Adsorption Desorption

Abstract Zinc titanates nanopowders viz.; Zn2TiO4, ZnTi3O8 and ZnTiO3 were synthesized through the thermal decomposition course of ZnC2O4.2H2O-TiO2 precursor (1:1 mole ratio), prepared via a new co-precipitation method up to 900oC. Thermogravimetric measurement (TG) was utilized to characterize the precursor decomposition while X-ray diffraction (XRD), Fourier transform infra-red (FT-IR) were used to characterize the decomposition products as well as the phase transitions at different temperatures. XRD revealed the starting of titanates formation at 700oC via detecting Zn2TiO4 along with ZnO and TiO2 (anatase) diffraction peaks. By increasing the calcination temperature to 800oC, the ZnO content vanished with the appearing of Zn2Ti3O8 besides ZnTi2O4 and impurities of TiO2 (anatase). Finally at 900oC, the Zn2Ti3O8 content was decomposed into ZnTiO3. Nitrogen adsorption-desorption isotherm of the calcined precursor at 900oC indicated low specific surface area of 7.1 m2 g-1 in accordance with the agglomeration nature estimated via transmission electron microscopy (TEM) study. The conductivity measurements showed semiconducting behavior of the prepared titanates with ferroelectric transition in the range 200-308oC.The obtained low dielectric value suggests the uses of present titanates as a co-fired ceramic or resonator ceramics.