A Facile Template Approach for Preparing Microstructures of Bimodal Crystalline Mesoporous Titania Powders

2012 ◽  
Vol 616-618 ◽  
pp. 1797-1800
Author(s):  
Yu Mei Gong ◽  
Qing Liang ◽  
Jing Chuan Song ◽  
Ling Ming Xia
Keyword(s):  
Electron Microscope ◽  
Surface Area ◽  
Nitrogen Adsorption ◽  
Mesoporous Titania ◽  
Mass Ratio ◽  
X Ray Diffraction ◽  
Average Pore ◽  
X Ray ◽  
Transmission Electron ◽  
Adsorption Desorption

This paper presents the preparation of bimodal crystalline macro-/mesoporous titania powders by using a pluronic polymer (EO20PO70EO20, P123) as a template through a hydrothermal treatment. The as-prepared powders were characterized by X-ray diffraction (XRD), nitrogen adsorption-desorption, scanning electron microscope (SEM) and transmission electron microscope (TEM). The results reveal that the amount of P123 has a significant effect on the surface area of the mesoporous titania. When the mass ratio of P123:TBOT is 1:14, the crystalline macro-/mesoporous titania has the largest surface area (120.96 m2/g), the average pore diameter of this sample reaches a minimum of 6.67 nm.

Positron Annihilation Study of Porous ZnO Synthesized with Soft Template

2017 ◽  
Vol 373 ◽  
pp. 299-302
Author(s):  
Bo Zhou ◽  
Chong Yang Li ◽  
Ning Qi ◽  
Zhi Quan Chen
Keyword(s):  
Pore Size ◽  
Positron Lifetime ◽  
Nitrogen Adsorption ◽  
Soft Template ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Long Lifetime ◽  
Positron Annihilation Study ◽  
Adsorption Desorption

Porous ZnO were synthesized with soft template method using zinc acetate Zn (CH3COO)2·2H2O as precursor and block copolymer F127 as the surfactant. Nitrogen adsorption-desorption measurements indicate that the ZnO sample contains large pores with mean diameter of about 30 nm. However, both small-angle X-ray diffraction and transmission electron microscope measurements indicate that the pore ordering is missing. Positron lifetime measurements reveal two long lifetime components in the porous ZnO. The longest lifetime τ4 (75 ns) corresponds to ortho-positronium (o-Ps) annihilation in large pores. The pore size estimated from τ4 is about 10.6 nm. This is much smaller than that estimated from Nitrogen adsorption-desorption measurements. In addition, the intensity I4 is only about 2.2%. This is probably due to the chemical quenching and/or inhibition of positronium formation induced by ZnO, which reduces o-Ps lifetime and intensity, and leads to under estimation of the pore size.

Synthesis and Characterization of Mesoporous Molecular Sieve Al-MCM-41 Using Kaolin as Raw Material

2013 ◽  
Vol 779-780 ◽  
pp. 201-204
Author(s):  
Miao Li ◽  
Hong Wang ◽  
Xian Qing Li ◽  
Jin Rong Liu
Keyword(s):  
Molecular Sieve ◽  
Nitrogen Adsorption ◽  
Mesoporous Molecular Sieve ◽  
Raw Material ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Adsorption Desorption ◽  
Calcined Kaolin ◽  
Mcm 41

Ordered hexagonally mesoporous molecular sieve Al-MCM-41 with Si/Al (atom) ratio=9 was prepared by hydrothermal synthesis using raw kaolin. X-ray diffraction (XRD), Nitrogen adsorption desorption, Transmission Electron Microscope (TEM) and Energy Dispersive X-ray Detector (EDX) were employed to characterise raw kaolin, calcined kaolin, as-synthesized and calcined Al-MCM-41. The results indicated that characteristic reflections of raw kaolin disappeared after calcination, both of as-synthesized and calcined Al-MCM-41 exhibited well ordered hexagonally mesoporous molecular sieve structure.

Preparation and Characterization TiO2 Aerogel Fibers

2013 ◽  
Vol 743-744 ◽  
pp. 434-437
Author(s):  
Miao Lv ◽  
Guo Tong Qin ◽  
Wei Wei
Keyword(s):  
Electron Microscopy ◽  
Pore Diameter ◽  
Supercritical Drying ◽  
Mass Ratio ◽  
Composite Fibers ◽  
X Ray Diffraction ◽  
Average Pore ◽  
X Ray ◽  
Adsorption Desorption ◽  
Scanning Electron

TiO2aerogel fibers have been fabricated by electron span combined supercritical drying technique. Polyvinylpyrrolidone (PVP)/TiO2composite fibers are prepared by electrospinning PVP and TiO2precursor Ti (OC4H9)4. TiO2aerogel fibers are obtained by supercritical drying PVP/TiO2composite fibers using ethanol as media. Structural of the aerogel fibers was investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD) and N2adsorption at 77 K. The effect of mass ratio of PVP/TiO2was investigated. SEM shows that pore structure of nanofibers was well developed, with the diameter of nanofibers about 2 μm. N2adsorption/desorption data show that the highest surface area of aerogel fibers reached 241.6 m2/g with the average pore diameter about 10 nm. The aerogel fibers were anatase type TiO2.

SYNTHESIS, CHARACTERIZATION AND THE APPLICABILITY OF β-CYCLODEXTRINS FUNCTIONALIZED MESOPOROUS SBA-15 MOLECULAR SIEVES

NANO ◽  
2013 ◽  
Vol 08 (05) ◽  
pp. 1350050
Author(s):  
MIN GUAN ◽  
HAI-PENG BI ◽  
ZUYUAN WANG ◽  
SHAOHUA BU ◽  
LING HUANG ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Photoelectron Spectroscopy ◽  
Molecular Sieves ◽  
Nitrogen Adsorption ◽  
X Ray Diffraction ◽  
X Ray ◽  
Adsorption Capacities ◽  
Transmission Electron ◽  
Potential Applications ◽  
Adsorption Desorption

Mesoporous silicas SBA-15 are modified with β-Cyclodextrins (β-CD) by simple grafting method. β-CD functionalized SBA-15 was characterized by Fourier transform infrared (FTIR) spectroscopy, transmission electron microscopy (TEM), scanning electron microscopy (SEM), powder X-ray diffraction (PXRD), nitrogen adsorption–desorption measurements, thermogravimetric analysis (TGA) and X-ray photoelectron spectroscopy (XPS). Furthermore, the applicability of it is investigated through studying the adsorption properties of clenbuterol. It showed better adsorption capacities of clenbuterol than pure SBA-15. β-CD functionalized SBA-15 material has the potential applications in the treatment of clenbuterol contamination in food and environment science.

Synthesis of Anatase/Brookite Mixtured TiO2 Nanoparticles by a Chimie Douce Technique

2013 ◽  
Vol 734-737 ◽  
pp. 2528-2531
Author(s):  
Yu Mei Gong ◽  
Qing Liang ◽  
Jing Guo ◽  
Hong Zhang ◽  
Fu Cheng Guan
Keyword(s):  
Electron Microscope ◽  
Anatase Phase ◽  
Spherical Shape ◽  
Nitrogen Adsorption ◽  
X Ray Diffraction ◽  
Average Pore ◽  
Specific Pore Volume ◽  
Transmission Electron ◽  
Bet Method ◽  
Ft Ir

Anatase/brookite mixtured TiO2nanoparticles have been synthesized by using a two-step process through a chimie douce technique. The as-prepared powders were characterized by Fourier transform infrared (FT-IR) spectra, X-ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscope (SEM), and a nitrogen adsorption apparatus in multipoint Brunauer-Emmett-Teller (BET) method. The results indicated that the TiO2nanoparticles were composed of biphasial anatase/brookite mixtures, 38% anatase phase formed in quasi-spherical shape and 62% brookite phase formed in nanorod shape. The specific surface area, the average pore diameter, and the specific pore volume were 100.06 m2/g, 14.0 nm, and 0.561 cm3/g, respectively.

Mesoporous TiO2 Prepared by Using Lac Red as Template：Synthesis, Characterization, and Adsorption of Gaseous Acetaldehyde

2013 ◽  
Vol 742 ◽  
pp. 448-451
Author(s):  
Ming Feng Wang ◽  
Tou Gen Liao ◽  
Bao Kun Zhu ◽  
Yao Wang ◽  
Yan Qing Duan ◽  
...  
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Mesoporous Titania ◽  
X Ray Diffraction ◽  
High Adsorption ◽  
X Ray ◽  
Transmission Electron ◽  
Adsorption Desorption ◽  
Scanning Electron

Mesoporous TiO2 with anatase crystalline structure (MTiO2) has been synthesized by using Lac Red as template. The synthesized mesoporous titania samples were characterized by a combination of various physicochemical techniques, such as X-ray diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), N2 adsorption/desorption. It was found that without any external doping MTiO2 exhibited significant high adsorption abilities for adsorbing the gaseous acetaldehyde by the adsorption ratio of 39.15%.

Novel Route for Incorporation of Palladium Nanoparticles into Mesostructured Silicas Sba 15 and Sba-16

2013 ◽  
Vol 22 (3) ◽  
pp. 096369351302200
Author(s):  
N. Ivashchenko ◽  
V. Tertykh ◽  
J. Skubiszewska-Zięba ◽  
R. Leboda ◽  
S. Khainakov ◽  
...  
Keyword(s):  
Palladium Nanoparticles ◽  
Nitrogen Adsorption ◽  
Pd Nanoparticles ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Adsorption Desorption ◽  
Desorption Method ◽  
Material Study

Palladium nanoparticles with controlled size were synthesized within the pores of the mesoporous SBA-15 and SBA-16 silicas with grafted silicon hydride groups. Nitrogen adsorption-desorption method, X-ray diffraction and transmission electron microscopy (TEM) were used for characterization of palladium-containing composites. Results of material study clearly revealed that Pd nanoparticles prepared by this method were located inside the porous channels and were quite uniform in size (mostly 5–6 nm). The influence of metal content on the particles size and porous structure of supports was investigated.

scholarly journals MesoporousTiO2Micro-Nanometer Composite Structure: Synthesis, Optoelectric Properties, and Photocatalytic Selectivity

2012 ◽  
Vol 2012 ◽  
pp. 1-9 ◽  
Author(s):  
Kun Liu ◽  
Lianjie Zhu ◽  
Tengfei Jiang ◽  
Youguang Sun ◽  
Hongbin Li ◽  
...  
Keyword(s):  
Electron Microscope ◽  
Composite Structure ◽  
Mixed Solution ◽  
X Ray Diffraction ◽  
Sunlight Irradiation ◽  
X Ray ◽  
Transmission Electron ◽  
Structure Synthesis ◽  
Ft Ir ◽  
Adsorption Desorption

Mesoporous anatase TiO2micro-nanometer composite structure was synthesized by solvothermal method at 180°C, followed by calcination at 400°C for 2 h. The as-prepared TiO2was characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), and Fourier transform infrared spectrum (FT-IR). The specific surface area and pore size distribution were obtained from N2adsorption-desorption isotherm, and the optoelectric property of the mesoporous TiO2was studied by UV-Vis absorption spectrum and surface photovoltage spectra (SPS). The photocatalytic activity was evaluated by photodegradation of sole rhodamine B (RhB) and sole phenol aqueous solutions under simulated sunlight irradiation and compared with that of Degussa P-25 (P25) under the same conditions. The photodegradation preference of this mesoporous TiO2was also investigated for an RhB-phenol mixed solution. The results show that the TiO2composite structure consists of microspheres (∼0.5–2 μm in diameter) and irregular aggregates (several hundred nanometers) with rough surfaces and the average primary particle size is 10.2 nm. The photodegradation activities of this mesoporous TiO2on both RhB and phenol solutions are higher than those of P25. Moreover, this as-prepared TiO2exhibits photodegradation preference on RhB in the RhB-phenol mixture solution.

scholarly journals Modification of TiO2 nanoparticles through lanthanum doping and peg templating

2014 ◽  
Vol 8 (4) ◽  
pp. 195-202 ◽  
Author(s):  
Marija Milanovic ◽  
Ljubica Nikolic
Keyword(s):  
Anatase Phase ◽  
Sol Gel ◽  
Nitrogen Adsorption ◽  
Sem Analysis ◽  
X Ray Diffraction ◽  
Average Pore ◽  
Lanthanum Doping ◽  
X Ray ◽  
Doped Titania ◽  
Adsorption Desorption

Pure and lanthanum doped titania nanopowders were synthesized through a room temperature sol-gel method using a template of polyethylene glycol (PEG). The progress of the synthesis in terms of phase formation and size of nanoparticles was monitored by X-ray diffraction, FTIR spectroscopy and SEM analysis. After calcination at 450?C in air, the results have shown the presence of small particles crystallized predominantly in the form of anatase phase, with significant agglomeration. Nitrogen adsorption-desorption measurements confirmed that all prepared powders are mesoporous with an average pore diameter in range 3.1-3.8 nm. The addition of lanthanum ions leads to the nanopowders with the highest specific surface (BET) area (203m2/g). The obtained powders were compared to TiO2 prepared without a template.

scholarly journals Preparation of Triple-Functionalized Montmorillonite Layers Promoting Thermal Stability of Polystyrene

Nanomaterials ◽  
2021 ◽  
Vol 11 (9) ◽  
pp. 2170
Author(s):  
Chengcheng Yu ◽  
Xu Hu ◽  
Shichao Lu ◽  
Yangchuan Ke ◽  
Jianbin Luo
Keyword(s):  
Thermal Stability ◽  
Thermal Characteristics ◽  
Nitrogen Adsorption ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Chemical Grafting ◽  
Adsorption Desorption ◽  
Maximum Mass Loss ◽  
Thermal Stability Of

The objective of this study was to investigate the effect of three different treatments on the morphology, microstructure, and the thermal characteristics of a montmorillonite (Mt) sample, by using hydrochloric acid (HCl), tributyl tetradecyl phosphonium chloride (TTPC) surfactant, and γ-methacryloxypropyltrimethoxysilane (γ-MPS). The resultant nanofillers were characterized by Fourier transform infrared (FTIR), X-ray diffraction (XRD), transmission electron microscopy (TEM), nitrogen adsorption–desorption analysis, X-ray fluorescence spectrometry (XRF), and thermogravimetric analysis (TGA). The results showed that the amount of chemical grafting of the γ-MPS was increased after the acid treatment, whereas the amount of intercalation of the TTPC surfactant was decreased. The preintercalation of TTPC or silylation of γ-MPS, for the Mt sample, had a certain hindrance effect on its subsequent silylation or intercalation treatments. Furthermore, the effect of four different nanofillers on the thermal stability properties of the polystyrene (PS) matrix were also investigated. The results showed an increase in thermal stability for the triple-functionalized Mt, compared with the double-functionalized samples. The onset decomposition temperatures and the maximum mass loss temperatures of the PS nanocomposites were increased by 27 °C and 32 °C, respectively, by the incorporation of triple-modified Mt, as a result of the good exfoliation and dispersion of the nanolayers, more favorable polymer–nanofiller interaction, as well as the formation of a more remarkable tortuous pathway in the continuous matrix.

Sign in / Sign up

Export Citation Format

Share Document