scholarly journals Assessment of Corrosive Behaviour and Microstructure Characterization of Hybrid Friction Stir Welded Martensitic Stainless Steel

2021 ◽  
Vol 21 (4) ◽  
pp. 67-78
Author(s):  
Dhanesh G. Mohan ◽  
S. Gopi ◽  
Jacek Tomków ◽  
Shabbir Memon
Keyword(s):  
Stainless Steel ◽  
Friction Stir Welding ◽  
Welding Speed ◽  
Spindle Speed ◽  
Grain Structure ◽  
Welding Parameters ◽  
Plunge Depth ◽  
Friction Stir ◽  
Fine Grain ◽  
Weight Loss Method

Abstract This study examined the effect of induction heating on the microstructure and corrosion characteristics of hybrid friction stir welded AISI 410 stainless steel. Five joints have been produced with different friction stir welding parameters like welding speed, spindle speed, plunge depth, and induction power. Their microstructures were evaluated using a scanning electron microscope, and chemical composition was examined using energy-dispersive X-ray spectroscopy (EDX). The rate of corrosion was found out via the weight loss method in a 1 M HCL solution. The hybrid friction stir welding method used for this work is induction assisted friction stir welding; the results show that this method could produce sound AISI 410 stainless steel Joints. The experiment results show that the joint made at a spindle speed of 1150 rpm, welding speed 40 mm/min, plunge depth 0.5 mm, and in-situ heat by induction 480°C show a better corrosion resistance property with a fine grain structure.

scholarly journals Thermo-mechanical analysis of linear welding stage in friction stir welding - influence of welding parameters

2021 ◽  
pp. 186-186
Author(s):  
Darko Veljic ◽  
Marko Rakin ◽  
Aleksandar Sedmak ◽  
Nenad Radovic ◽  
Bojan Medjo ◽  
...  
Keyword(s):  
Friction Stir Welding ◽  
Heat Generation ◽  
Welding Speed ◽  
Reaction Force ◽  
Material Model ◽  
Element Model ◽  
Welding Parameters ◽  
Al Alloy ◽  
Friction Stir ◽  
Fsw Parameters

The influence of friction stir welding (FSW) parameters on thermo-mechanical behaviour of the material during welding is analysed. An aluminium alloy is considered (Al 2024 T351), and different rotating speed and welding speed are applied. Finite element model consists of the plate (Al alloy), backing plate and welding tool, and it is formed and solved in software package Simulia Abaqus. The influence of the welding conditions on material behaviour is taken into account by application of the Johnson-Cook material model. The rotation of the tool affects the results: if increased, it contributes to an increase of friction-generated heat intensity. The other component of the generated heat, the plastic deformation of the material, is negligibly changed. When the welding speed is increased, the intensity of friction-generated heat decreases, while the heat generation due to plastic deforming increases. Combined, these two effects cause small change of the total heat generation. For the same welded joint length, the plate welded by lower speed will be heated more intensively. The changes of the heat generation influence both the temperature field and reaction force, which are also considered.

Mechanical Property of Friction Stir Welded Retardant Magnesium Alloy Joint

2011 ◽  
Vol 295-297 ◽  
pp. 1929-1932
Author(s):  
Yi Min Tu ◽  
Ran Feng Qiu ◽  
Hong Xin Shi ◽  
Xin Zhang ◽  
Ke Ke Zhang
Keyword(s):  
Mechanical Properties ◽  
Mechanical Property ◽  
Friction Stir Welding ◽  
Magnesium Alloy ◽  
Welding Speed ◽  
Rotational Speed ◽  
Maximum Strength ◽  
Welding Parameters ◽  
Tool Rotational Speed ◽  
Friction Stir

In order to obtain better understanding of the friction stir weldability of the magnesium alloy and provide some foundational information for improving mechanical properties of retardant magnesium alloy joints. A retardant magnesium alloy was weld using the method of friction stir welding. The influence of welding parameters on the strength of the joint was investigated. The maximum strength of 230 MPa was obtained from the joint welded at the tool rotational speed of 1000 r/min and welding speed of 750 mm/min.

Process Parameter Optimization of Friction Crush Welding (FCW) of AISI 304 Stainless Steel

2017 ◽  
Author(s):  
Gurinder Singh Brar ◽  
Manpreet Singh ◽  
Ajay Singh Jamwal
Keyword(s):  
Stainless Steel ◽  
Friction Stir Welding ◽  
Welding Process ◽  
Pressure Vessels ◽  
304 Stainless Steel ◽  
Welding Parameters ◽  
Work Piece ◽  
Aisi 304 Stainless Steel ◽  
Aisi 304 ◽  
Friction Stir

AISI 304 stainless steel is one of the grades of steel widely used in engineering applications particularly in chemical equipments, food processing, pressure vessels and paper industry. Friction crush welding (FCW) is type of friction welding, where there is a relative motion between the tool and work-piece. In FCW process, the edges of the work-piece to be joined are prepared with flanged edges and then placed against each other. A non-consumable friction disc tool will transverse with a constant feed rate along the edges of the work-piece, which leads to welding. The joint is formed by the action of crushing a certain amount of additional flanged material into the gap formed by the contacting material. The novelty of present work is that FCW removes the limitations of friction stir welding and Steel work pieces can be economically welded by FCW. Taguchi method of Design of Experiments (DOE) is used to find optimal process parameters of Friction Crush Welding (FCW). A L9 Orthogonal Array, Signal to Noise ratio (S/N) and Analysis of Variance are applied to analyze the effect of welding parameters (welding speed, RPM, tool profile) on the weld properties like bond strength. Grain refinement takes place in friction crush welding as is seen in friction stir welding. Friction crush welding process also has added advantage in reducing distortion and residual stresses.

On the formation of grain structure during friction stir welding of duplex stainless steel

2010 ◽  
Vol 527 (24-25) ◽  
pp. 6484-6488 ◽  
Author(s):  
T. Saeid ◽  
A. Abdollah-zadeh ◽  
T. Shibayanagi ◽  
K. Ikeuchi ◽  
H. Assadi
Keyword(s):  
Stainless Steel ◽  
Friction Stir Welding ◽  
Duplex Stainless Steel ◽  
Grain Structure ◽  
Friction Stir

scholarly journals Microstructural developments and mechanical properties of friction stir welding of AZ91D magnesium alloy plates

10.30544/221 ◽  
2017 ◽  
Vol 23 (2) ◽  
pp. 119-130 ◽  
Author(s):  
Nagabhushan Kumar Kadigithala ◽  
Vanitha C
Keyword(s):  
Friction Stir Welding ◽  
Welding Speed ◽  
Rotational Speed ◽  
Grain Structure ◽  
Friction Stir ◽  
Transverse Tensile ◽  
Α Phase ◽  
Die Cast ◽  
Constant Strength ◽  
Fusion Weld

Friction stir welding (FSW) is an efficient technique which can be used particularly for magnesium and aluminum alloys that are difficult to fusion weld. In this work AZ91D Mg alloy plates 3mm thick were friction stir welded at different process variables such as rotational speed and welding speed. The range of rotational speeds varied from 1025 to 1525 rpm, and the welding speed varied from 25 to 75 mm/min. Good quality welds were obtained under 1025 rpm of rotational speed with the welding speeds range from 25 to 75 mm/min. The microstructure of the AZ91D alloy consists of primary α-phase, eutectic α-phase and eutectic β (Mg17Al12) phase in the received condition (gravity die cast). The original dendrite grain structure completely disappeared and was transformed to fine equiaxed grains in stir zone (SZ). It was observed that there was a slight increase in hardness in SZ, because of fine recrystallized grain structure. The transverse tensile test results of weld specimens indicated constant strength irrespective of traveling speed. Fractrographic analysis of the friction stir welded specimens showed the brittle failure.

Effects of welding speeds on the microstructural and mechanical properties of AZ91D Mg alloy by friction stir welding

2020 ◽  
Vol 11 (6) ◽  
pp. 769-782 ◽  
Author(s):  
Nagabhushan Kumar Kadigithala ◽  
Vanitha C
Keyword(s):  
Mechanical Properties ◽  
Friction Stir Welding ◽  
Magnesium Alloy ◽  
Welding Speed ◽  
Base Material ◽  
Welding Parameters ◽  
Content Type ◽  
Friction Stir ◽  
Az91d Magnesium Alloy ◽  
Transverse Tensile

PurposeThe main purpose of the present work is to evaluate, the microstructural and mechanical properties of friction stir welded plates of AZ91D magnesium alloy with 3 mm thickness, and to determine the optimum range of welding conditions.Design/methodology/approachMicrostructure and fractographic studies were carried out using scanning electron microscopy (SEM). Vickers micro hardness test was performed to evaluate the hardness profile in the region of the weld area. The phases in the material were confirmed by X-Ray diffraction (XRD) analysis. Transverse tensile tests were conducted using universal testing machine (UTM) to examine the joint strength of the weldments at different parameters.FindingsMetallographic studies revealed that each zone shown different lineaments depending on the mechanical and thermal conditions. Significant improvement in the hardness was observed between the base material and weldments. Transverse tensile test results of weldments had shown almost similar strength that of base material regardless of welding speed. Fractographic examination indicated that the welded specimens failed due to brittle mode fracture. Through these studies it was confirmed that friction stir welding (FSW) can be used for the welding of AZ91D magnesium alloy.Research limitations/implicationsIn the present study, the welding speed varied from 25 mm/min to 75 mm/min, tilt angle varied from 1.5° to 2.5° and constant rotational speed of 500 rpm.Practical implicationsMagnesium and aluminum based alloys which are having high strength and low density, used in automotive and aerospace applications can be successfully joined using FSW technique. The fusion welding defects can be eliminated by adopting this technique.Originality/valueLimited work had been carried out on the FSW of magnesium based alloys over aluminum based alloys. Furthermore, this paper analyses the influence of welding parameters over the microstructural and mechanical properties.

Experimental Analysis on Mechanical Properties of Friction Stir Welding in Dissimilar Aluminum Alloys

2020 ◽  
pp. 64-68
Author(s):  
Anganan K ◽  
Narendran RJ ◽  
Naveen Prabhu N ◽  
Rahul Varma R ◽  
Sivasubramaniyam R
Keyword(s):  
Tensile Strength ◽  
Friction Stir Welding ◽  
Aluminum Alloys ◽  
Welding Speed ◽  
Rotational Speed ◽  
Copper Alloys ◽  
Welding Parameters ◽  
Tool Rotational Speed ◽  
Friction Stir ◽  
Dissimilar Aluminum Alloys

Friction stir welding (FSW) is an innovative solid state joining technique and has been employed in industries for joining aluminum, magnesium, zinc and copper alloys. The FSW process parameters such as tool, rotational speed, welding speed, axial force, etc play major role in deciding the weld quality. A mathematical modeling was developed based on experiments to predict the tensile strength of dissimilar FSW aluminum alloys. The maximum tensile strength of 210 MPa can be obtained at the tool rotational speed of 1100 rpm, welding speed of 35mm/min and an axial load of 7 kN is the Optimum welding parameters.