Optical properties of ZnO nanoparticles synthesized by varying the sodium hydroxide to zinc acetate molar ratios using a Sol-Gel process

Open Physics ◽  
2011 ◽  
Vol 9 (5) ◽  
Author(s):  
Francis Dejene ◽  
Abdub Ali ◽  
Hendrik Swart ◽  
Reinhardt Botha ◽  
Kittesa Roro ◽  
...  
Keyword(s):  
Zno Nanoparticles ◽  
Sol Gel ◽  
Visible Region ◽  
Blue Emission ◽  
Molar Ratio ◽  
Broad Emission Band ◽  
Photoluminescence Intensity ◽  
Molar Ratios ◽  
Quantum Confinement Effects ◽  
Sol Gel Process

AbstractMaterial property dependence on the OH−/Zn2+ molar ratio of the precursor was investigated by varying the amount of NaOH during synthesis of ZnO. It was necessary to control the water content and temperature of the mixture to ensure the reproducibility. It was observed that the structural properties, particle size, photoluminescence intensity and wavelength of maximum intensity were influenced by the molar ratio of the precursor. The XRD spectra for ZnO nanoparticles show the entire peaks corresponding to the various planes of wurtzite ZnO, indicating a single phase. UV measurements show the absorption that comes from the ZnO nanoparticles in visible region. The absorption edge of these ZnO nanoparticles are shifted to higher energies and the determined band gap energies are blue shifted as the OH−/Zn2 molar ration increases, due to the quantum confinement effects. The photoluminescence characterization of the ZnO nanostructures exhibited a broad emission band centred at green (600 nm) region for all molar ratios except for OH−/Zn2+ = 1.7 where a second blue emission around 468 nm was also observed. The photoluminescence properties of ZnO nanoparticles were largely determined by the size and surface properties of the nanoparticles.

Effect of Mn doping on the structural and optical properties of sol-gel derived ZnO nanoparticles

Open Physics ◽  
2012 ◽  
Vol 10 (2) ◽  
Author(s):  
Abdub Ali ◽  
Francis Dejene ◽  
Hendrik Swart
Keyword(s):  
Band Gap ◽  
Zno Nanoparticles ◽  
Sol Gel ◽  
Visible Region ◽  
Green Emission ◽  
Ion Concentration ◽  
Photoluminescence Intensity ◽  
Preparation Conditions ◽  
Doped Zno ◽  
Mn Doped

AbstractUn-doped and Mn-doped ZnO nanoparticles were successfully synthesized in an ethanolic solution by using a sol-gel method. Material properties of the samples dependence on preparation conditions and Mn concentrations were investigated while other parameters were controlled to ensure reproducibility. It was observed that the structural properties, particle size, band gap, photoluminescence intensity and wavelength of maximum intensity were influenced by the amount of Mn ions present in the precursor. The XRD spectra for ZnO nanoparticles show the entire peaks corresponding to the various planes of wurtzite ZnO, indicating a single phase. The diffraction peaks of doped samples are slightly shifted to lower angles with an increase in the Mn ion concentration, signifying the expansion of the lattice constants and increase in the band gap of ZnO. All the samples show the absorption in the visible region. The absorbance spectra show that the excitonic absorption peak shifts towards the lower wavelength side with the Mn-doped ZnO nanoparticles. The PL spectra of undoped ZnO consist of UV emission at 388 nm and broad visible emission at 560 nm with varying relative peak intensities. The doping of ZnO with Mn quenches significantly the green emission while UV luminescence is slightly affected.

scholarly journals Green Synthesis of N/Zr Co-Doped TiO2 for Photocatalytic Degradation of p-Nitrophenol in Wastewater

Catalysts ◽  
2021 ◽  
Vol 11 (2) ◽  
pp. 235
Author(s):  
Hayette Benkhennouche-Bouchene ◽  
Julien G. Mahy ◽  
Cédric Wolfs ◽  
Bénédicte Vertruyen ◽  
Dirk Poelman ◽  
...  
Keyword(s):  
Visible Light ◽  
Tio2 Nanoparticles ◽  
Sol Gel ◽  
Visible Region ◽  
Chemical Properties ◽  
Pure Tio2 ◽  
Molar Ratio ◽  
Xps Spectra ◽  
Doped Tio2 ◽  
Co Doped

TiO2 prepared by a green aqueous sol–gel peptization process is co-doped with nitrogen and zirconium to improve and extend its photoactivity to the visible region. Two nitrogen precursors are used: urea and triethylamine; zirconium (IV) tert-butoxide is added as a source of zirconia. The N/Ti molar ratio is fixed regardless of the chosen nitrogen precursor while the quantity of zirconia is set to 0.7, 1.4, 2, or 2.8 mol%. The performance and physico-chemical properties of these materials are compared with the commercial Evonik P25 photocatalyst. For all doped and co-doped samples, TiO2 nanoparticles of 4 to 8 nm of size are formed of anatase-brookite phases, with a specific surface area between 125 and 280 m2 g−1 vs. 50 m2 g−1 for the commercial P25 photocatalyst. X-ray photoelectron (XPS) measurements show that nitrogen is incorporated into the TiO2 materials through Ti-O-N bonds allowing light absorption in the visible region. The XPS spectra of the Zr-(co)doped powders show the presence of TiO2-ZrO2 mixed oxide materials. Under visible light, the best co-doped sample gives a degradation of p-nitrophenol (PNP) equal to 70% instead of 25% with pure TiO2 and 10% with P25 under the same conditions. Similarly, the photocatalytic activity improved under UV/visible reaching 95% with the best sample compared to 50% with pure TiO2. This study suggests that N/Zr co-doped TiO2 nanoparticles can be produced in a safe and energy-efficient way while being markedly more active than state-of-the-art photocatalytic materials under visible light.

Preparation, Characterization and its Photocatalytic Performance of Rare Earth Element Erbium Doped with TiO2 Material

2012 ◽  
Vol 568 ◽  
pp. 380-383
Author(s):  
Song Tian Li ◽  
Guo Xu He ◽  
Wei Ma ◽  
Yan Hua Liu
Keyword(s):  
Titanium Dioxide ◽  
Rare Earth ◽  
Rare Earth Element ◽  
Earth Element ◽  
Photocatalytic Performance ◽  
Sol Gel ◽  
Visible Region ◽  
Erbium Doped ◽  
Sol Gel Process ◽  
Reduce Energy Consumption

In order to expand photoresponse range of TiO2, reduce energy consumption of semiconductor material optical catalytic, certain amount of rare earth element Erbiun was doped during preparation of anatase titanium dioxide to improve the light absorption and photocatalysis efficiency. A series of rare earth element doped TiO2 material were prepared by sol-gel process, and characterized by means of UV-vis diffuse reflectance spectra. UV-vis absorption verified that doping of Er3+ enhanced absorptive capacity of catalyst in visible region. The photocatalytic performance of anatase titanium dioxide and rare earth element Erbiun doped with TiO2 to basic fuchsin were studied.

scholarly journals Synthesis of ZnO and CuO nanoparticles via Sol gel method and Its Characterization by using XRD and FT-IR Analysis

2022 ◽  
Author(s):  
Monika Patel ◽  
Sunita Mishra ◽  
Ruchi Verma ◽  
Deep Shikha
Keyword(s):  
Particle Size ◽  
Zno Nanoparticles ◽  
Sol Gel ◽  
Broad Band ◽  
Zinc Nitrate ◽  
Zno Nanoparticle ◽  
Absorption Bands ◽  
Characteristic Absorption ◽  
Sol Gel Process ◽  
Ft Ir

Abstract Nanotechnology is a completely unique branch of technology that offers with substances in a very small size between (1-100 nm) with various crystal shapes which include spherical nanoparticles, flower shaped, Nano rods, Nano ribbons, and Nano platelets. Metals have ability to produce large number of oxides. These metal oxides play an major role in many areas of chemistry, physics, material science and food science. In this research, Zinc Oxide (ZnO) and Copper (II) oxide nanoparticles were synthesized via sol-gel process using zinc nitrate and copper (II) nitrate as precursor respectively. The characterization of CuO and ZnO nanoparticles was done by using various techniques. X-ray Diffraction (XRD) indicates the crystallinity and crystal size of CuO and ZnO nanoparticle. Fourier transform infrared spectroscopy (FT-IR) was used to get the infrared spectrum of the sample indicating composition of the sample which contains various functional groups. XRD result shows the particle size of CuO at highest peak 29.40140 was 61.25 nm and the particle size of ZnO at highest peak 36.24760 was 21.82 nm. FT-IR spectra peak at 594.56 cm-1 indicated characteristic absorption bands of ZnO nanoparticles and the broad band peak at 3506.9 cm-1 can be attributed to the characteristic absorption of O-H group. The analysis of FT-IR spectrum of CuO shows peaks at 602.09, 678.39, and 730.19cm−1 which refer to the formation of CuO. A broad absorption peak noticed at 3308.2 cm−1 attributed to O–H stretching of the moisture content.

Sol-gel synthesis and characterization of Ag nanoparticles in ZrO2 thin films

2009 ◽  
Vol 24 (8) ◽  
pp. 2541-2546 ◽  
Author(s):  
Eisuke Yokoyama ◽  
Hironobu Sakata ◽  
Moriaki Wakaki
Keyword(s):  
Thin Films ◽  
Sol Gel ◽  
Composite Films ◽  
Dip Coating ◽  
Molar Ratio ◽  
X Ray Diffraction ◽  
Silver Surface ◽  
Molar Ratios ◽  
Sol Gel Synthesis

ZrO2 thin films containing silver nanoparticles were prepared using the sol-gel method with Ag to Zr molar ratios [Ag]/[Zr] = 0.11, 0.25, 0.43, 0.67, 1.00, 1.50, and 2.33. After dip coating on glass substrate, coated films were annealed at 200 and 300 °C in air. X-ray diffraction peaks corresponding to crystalline Ag were observed, but a specific peak corresponding to ZrO2 was not observed. At the molar ratio [Ag]/[Zr] = 0.25, the particle size of Ag distributed broadly centered at 17 nm for an annealing temperature of 200 °C and at 25 nm for 300 °C. The films annealed in air at 200 °C showed an absorption band centered at 450 nm because of the silver surface plasmon resonance, whereas films heated at 300 °C in air caused a red shift of the absorption to 500 nm. The absorption peak was analyzed using the effective dielectric function of Ag-ZrO2 composite films modeled with the Maxwell-Garnett expression.

Synthesis of ZnO Nanoparticles via Sol-Gel Process Using Triethanolamine as a Novel Surfactant

2008 ◽  
pp. 626-631
Author(s):  
Ali Shokuhfar ◽  
Javad Samei ◽  
A. Esmaielzadeh Kandjani ◽  
Mohammad Reza Vaezi
Keyword(s):  
Zno Nanoparticles ◽  
Sol Gel ◽  
Sol Gel Process

scholarly journals Interlayer-free Glucose Carbonised Template Silica Membranes for Brine Water Desalination

2019 ◽  
Vol 280 ◽  
pp. 03010 ◽  
Author(s):  
Dwi Rasy Mujiyanti ◽  
Muthia Elma ◽  
Mufidah Amalia
Keyword(s):  
Sol Gel ◽  
Tetraethyl Orthosilicate ◽  
Water Desalination ◽  
Molar Ratio ◽  
Solution Temperature ◽  
Nacl Solution ◽  
Silica Membranes ◽  
Salt Ions ◽  
Sol Gel Process ◽  
Free Glucose

Interlayer-free glucose carbonized template silica membranesbased on tetraethyl orthosilicate (TEOS) and glucose were successfullyprepared using an acid-base catalysed sol-gel method for artificial brinewater desalination (7.5% wt NaCl solution %) at temperatures range from25, 40 and 60 °C. These membranes calcined at 250 and 400 °C. Themembranes were fabricated through sol-gel process by using TEOS(tetraethyl orthosilicate); ethanol; nitric acid; ammonia; aquadest andglucose as a template. By molar ratio is 1: 38: 0.0007: 0.0003: 5 and0.25%; 0.5%, 1% w/v glucose as template. The results show the highestwater fluxes of 1.8, 2.2 and 4.8 kg m−2 h−1 for 25, 40 and 60 °Cdesalination process with excellent salt rejections of 99.5, 99.5 and 99.7%, respectively. It was found that the higher the NaCl solution temperature asfeed solution as well as glucose concentration (0.25% to 1% wt) astemplate attached in the silica matrixes, the higher water fluxes eventhough the salt rejection remain the same. This study demonstrates that theorganosilica membranes offered the carbonized silica mesostructuremembranes with excellent separation of water from the hydrated salt ions, particularly for processing brine salt solutions.

scholarly journals Photocatalytic Improvement under Visible Light inTiO2Nanoparticles by Carbon Nanotube Incorporation

2015 ◽  
Vol 2015 ◽  
pp. 1-10 ◽  
Author(s):  
Mathana Wongaree ◽  
Siriluk Chiarakorn ◽  
Surawut Chuangchote
Keyword(s):  
Photocatalytic Activity ◽  
Visible Light ◽  
Sol Gel ◽  
Multiwall Carbon Nanotubes ◽  
High Specific Surface Area ◽  
Molar Ratio ◽  
Molar Ratios ◽  
Calcination Temperatures ◽  
Photocatalytic Activities ◽  
Multiwall Carbon

Photocatalytic activity ofTiO2nanoparticles was successfully enhanced by addition of multiwall carbon nanotubes (MWCNT) to make CNT/TiO2nanocomposites by sol-gel method at ambient temperature. CNT treated by HNO3 : H2SO4treatment (1 : 3 v/v) was mixed withTiO2nanoparticles at various molar ratios and calcination temperatures. The optimal molar ratio of CNT : TiO2was found at 0.05 : 1 by weight. The optimal calcination condition was 400°C for 3 h. From the results, the photocatalytic activities of CNT/TiO2nanocomposites were determined by the decolorization of 1 × 10−5 M methylene blue (MB) under visible light. CNT/TiO2nanocomposites could enhance the photocatalytic activity and showed faster for the degradation of MB with only 90 min. The degradation efficiency of the MB solution with CNT/TiO2nanocomposite achieved 70% which was higher than that with pristineTiO2(22%). This could be explained that CNT preventsTiO2from its agglomeration which could further enhance electron transfer in the composites. In addition, CNT/TiO2nanocomposites had high specific surface area (202 m2/g) which is very promising for utilization as a photocatalyst for environmental applications.

The Influences of Different Precursors on Morphology of Bi3TiNbO9 Powders Prepared by a Sol-Gel Method

2013 ◽  
Vol 815 ◽  
pp. 765-772 ◽  
Author(s):  
Zuo Dong Li ◽  
Dan Liu
Keyword(s):  
Ethylene Glycol ◽  
Chemical Method ◽  
Single Phase ◽  
Perovskite Phase ◽  
Sol Gel ◽  
Particle Morphology ◽  
Deionized Water ◽  
Molar Ratio ◽  
Molar Ratios ◽  
Baking Process

Bi3NbTiO9 (BNTO) powders were synthesized by a sol-gel chemical method using niobium oxalates, bismuth nitrate and tetra-n-butyl-titanate as starting materials. In order to determine the influence of the molar ratio of the deionized water to ethylene glycol on the particle morphology and crystallization, different molar ratios, the deionized water/ethylene glycol, were chosen to prepare BNTO powders. Single phase BNTO powders could be obtained at a calcinations temperature of 600°C. Moreover, the possible formation mechanism of BNTO powders was also proposed in this paper. In the baking process, perovskite phase BNTO was formed via a reaction between oxides and bismuth niobium.