scholarly journals Coated stainless steel archwires' discoloration measured by computerized system (An in-vitro study)

2020 ◽  
Vol 32 (4) ◽  
pp. 1-4
Author(s):  
Abeer B Mahmood
Keyword(s):  
Stainless Steel ◽  
Color Change ◽  
Artificial Saliva ◽  
In Vitro Study ◽  
Chemical Compositions ◽  
Color Changes ◽  
The Aesthetic ◽  
Post Hoc ◽  
Computerized System

Background: Aesthetic archwires are used to overcome the aesthetic problems of stainless steel wires but the color of the coating layer can be changed with time when exposed to oral environments. The aim of this study was to evaluate the degree of color change of different aesthetic archwires from different companies under different coloring solutions. Materials and Methods: One hundred fifty samples of coated archwires from three companies (Highland, G&H and Dany) were immersed in 5 solutions (artificial saliva, turmeric, tea, coffee and Miranda) to evaluate the degree of color changes after 7, 14 and 21 days using visible spectrophotometer. Data were collected and analyzed using one way ANOVA and post hoc Tukey’s tests. Results: Turmeric solution caused high color change than other solutions. Aesthetic archwires from Highland company showed the highest degree of color change than archwires from other companies. Conclusions: Turmeric solution produced more discoloration than other solutions and the effects of these solutions are related to different chemical compositions of those solutions.

scholarly journals Evaluation of color changes of white spot lesions treated with three different treatment approaches: an in-vitro study

2020 ◽  
Vol 25 (1) ◽  
pp. 26-27
Author(s):  
Shaza M. Hammad ◽  
Noha A. El-Wassefy ◽  
Mohamed A. Alsayed
Keyword(s):  
Color Change ◽  
Artificial Saliva ◽  
In Vitro Study ◽  
Color Stability ◽  
White Spot ◽  
Control Group ◽  
White Spot Lesions ◽  
Color Changes ◽  
Icon Resin Infiltrant

ABSTRACT Objective: To qualitatively and quantitatively assess the color changes effect and the color stability of the resin infiltrant on white spot lesions (WSLs), in comparison with nano-hydroxyapatite (nano-HA) toothpaste and microabrasion. Methods: WSLs were artificially created on sixty human premolars enamel surfaces and randomly assigned to equal four groups (n = 15 each): nano-HA toothpaste, microabrasion (Opalusture), resin infiltrant (Icon) treatment, or artificial saliva (control group). The color change (ΔE) of each specimen was measured by dental spectrophotometer (Vita Easyshade) at different time points: baseline, after WSLs’ creation, after application of treatments, one month, three and six months after treatments application. Results: The ΔE value did not differ significantly for the four groups at baseline measurement before treatment (p> 0.05). Icon resin infiltrant improved the color of WSLs significantly immediately after its application, giving the lowest ΔE value (3.00 ± 0.59), when compared to other treatments (p< 0.001). There were no significant changes in ΔE (p> 0.05) for all groups during the follow up intervals (one month, three and six months after treatments application). Conclusion: Resin infiltrant can improve the color of WSLs and restore the natural appearance of enamel better than nano-HA toothpaste and microabrasion.

scholarly journals In vitro study of color stability of polycrystalline and monocrystalline ceramic brackets

2014 ◽  
Vol 19 (4) ◽  
pp. 114-121 ◽  
Author(s):  
Cibele Braga de Oliveira ◽  
Luiz Guilherme Martins Maia ◽  
Ary Santos-Pinto ◽  
Luiz Gonzaga Gandini Júnior
Keyword(s):  
Red Wine ◽  
Color Change ◽  
Artificial Saliva ◽  
In Vitro Study ◽  
Color Stability ◽  
Black Tea ◽  
Color Changes ◽  
Ceramic Brackets ◽  
Dye Solutions

OBJECTIVE: The aim of this in vitro study was to analyze color stability of monocrystalline and polycrystalline ceramic brackets after immersion in dye solutions. METHODS: Seven ceramic brackets of four commercial brands were tested: Two monocrystalline and two polycrystalline. The brackets were immersed in four dye solutions (coffee, red wine, Coke and black tea) and in artificial saliva for the following times: 24 hours, 7, 14 and 21 days, respectively. Color changes were measured by a spectrophotometer. Data were assessed by Multivariate Profile Analysis, Analysis of Variance (ANOVA) and Multiple Comparison Tests of means. RESULTS: There was a perceptible change of color in all ceramic brackets immersed in coffee (ΔE* Allure = 7.61, Inspire Ice = 6.09, Radiance = 6.69, Transcend = 7.44), black tea (ΔE* Allure = 6.24, Inspire Ice = 5.21, Radiance = 6.51, Transcend = 6.14) and red wine (ΔE* Allure = 6.49, Inspire Ice = 4.76, Radiance = 5.19, Transcend = 5.64), but no change was noticed in Coke and artificial saliva (ΔE < 3.7). CONCLUSION: Ceramic brackets undergo color change when exposed to solutions of coffee, black tea and red wine. However, the same crystalline structure, either monocrystalline or polycrystalline, do not follow the same or a similar pattern in color change, varying according to the bracket fabrication, which shows a lack of standardization in the manufacturing process. Coffee dye produced the most marked color changes after 21 days of immersion for most ceramic brackets evaluated.

scholarly journals Tooth discoloration induced by apical plugs with hydraulic calcium silicate-based cements in teeth with open apices—a 2-year in vitro study

2021 ◽  
Author(s):  
Ralf Krug ◽  
C. Ortmann ◽  
S. Reich ◽  
B. Hahn ◽  
G. Krastl ◽  
...  
Keyword(s):  
Calcium Silicate ◽  
In Vitro Study ◽  
Color Difference ◽  
Blood Contamination ◽  
Tooth Color ◽  
Color Changes ◽  
Gutta Percha ◽  
Tooth Discoloration ◽  
Post Hoc

Abstract Objectives To assess tooth discoloration induced by different hydraulic calcium silicate-based cements (HCSCs), including effects of blood and placement method. Materials and methods Eighty bovine teeth cut to a length of 18 mm (crown 8 mm, root 10 mm) were randomly assigned to 10 groups (n = 8), receiving orthograde apical plug treatment (APT). Apical plugs were 4 mm in length and made of ProRoot MTA (Dentsply), Medcem MTA (Medcem), TotalFill BC RRM Fast Set Putty (Brasseler), or Medcem Medical Portland Cement (Medcem) plus bismuth oxide (Bi2O3) with and without bovine blood. Further, orthograde (with or without preoperative adhesive coronal dentin sealing) and retrograde APT were compared. Teeth were obturated with gutta-percha and sealer, sealed with composite and stored in distilled water. Tooth color was measured on apical plug, gutta-percha/sealer, and crown surface before treatment versus 24 h, 1, 3, 6, 12, and 24 months after treatment by spectrophotometry. Color difference (ΔE) values were calculated and analyzed by Shapiro–Wilk test, ANOVA with post hoc tests, Friedman test, t test, and post hoc tests with Bonferroni correction (α = .05). Results Tooth discoloration occurred in all groups with no significant differences between HCSCs (p > .05). After 24 months, color changes were prominent on roots but insignificant on crowns. Blood contamination induced a significantly decreased luminescence (p < .05). Blood had a stronger impact on tooth color than Bi2O3. No relevant effects of retrograde placement (p > .05) or preoperative dentin sealing (p > .05) were detected. Conclusions Apical plugs of the tested HCSCs cause discoloration of bovine roots, but not discoloration of bovine tooth crowns within a 24-month period. Clinical relevance APT should be performed carefully while avoiding direct contact with the coronal dentin, and in that case no aesthetic impairments occur.

scholarly journals Potential of different fluoride gels to prevent erosive tooth wear caused by gastroesophageal reflux

2021 ◽  
Vol 21 (1) ◽  
Author(s):  
Philipp Körner ◽  
Luca Georgis ◽  
Daniel B. Wiedemeier ◽  
Thomas Attin ◽  
Florian J. Wegehaupt
Keyword(s):  
Gastroesophageal Reflux ◽  
Artificial Saliva ◽  
In Vitro Study ◽  
Tooth Wear ◽  
Control Group ◽  
Erosive Tooth Wear ◽  
Custom Made ◽  
Post Hoc ◽  
Bovine Enamel

Abstract Background This in-vitro-study aimed to evaluate the potential of different fluoride gels to prevent gastroesophageal reflux induced erosive tooth wear. Methods Surface baseline profiles of a total of 50 bovine enamel specimens [randomly assigned to five groups (G1–5)] were recorded. All specimens were positioned in a custom made artificial oral cavity and perfused with artificial saliva (0.5 ml/min). Reflux was simulated 11 times a day during 12 h by adding HCl (pH 3.0) for 30 s (flow rate 2 ml/min). During the remaining 12 h (overnight), specimens were stored in artificial saliva and brushed twice a day (morning and evening) with a toothbrush and toothpaste slurry (15 brushing strokes). While specimens in the control group (G1) did not receive any further treatment, specimens in G2–5 were coated with different fluoride gels [Elmex Gelée (G2); Paro Amin Fluor Gelée (G3); Paro Fluor Gelée Natriumfluorid (G4); Sensodyne ProSchmelz Fluorid Gelée (G5)] in the evening for 30 s. After 20 days, surface profiles were recorded again and enamel loss was determined by comparing them with the baseline profiles. The results were statistically analysed using one-way analysis of variance (ANOVA) followed by Tukey`s HSD post-hoc test. Results The overall highest mean wear of enamel (9.88 ± 1.73 µm) was observed in the control group (G1), where no fluoride gel was applied. It was significantly higher (p < 0.001) compared to all other groups. G2 (5.03 ± 1.43 µm), G3 (5.47 ± 0.63 µm, p = 0.918) and G4 (5.14 ± 0.82 µm, p > 0.999) showed the overall best protection from hydrochloric acid induced erosion. Enamel wear in G5 (6.64 ± 0.86 µm) was significantly higher compared to G2 (p = 0.028) and G4 (p = 0.047). Conclusions After 20 days of daily application, all investigated fluoride gels are able to significantly reduce gastroesophageal reflux induced loss of enamel.

scholarly journals Color Stability and Gloss of Esthetic Restorative Materials after Chemical Challenges

2019 ◽  
Vol 30 (1) ◽  
pp. 52-57 ◽  
Author(s):  
Eduardo Haruki Ozera ◽  
Fernanda Miori Pascon ◽  
Américo Bortolazzo Correr ◽  
Regina Maria Puppin-Rontani ◽  
Aline Rogéria de Castilho ◽  
...  
Keyword(s):  
Color Change ◽  
Artificial Saliva ◽  
Color Stability ◽  
Initial Surface ◽  
Resin Composites ◽  
Cranberry Juice ◽  
Color Changes ◽  
Restorative Materials ◽  
Post Hoc ◽  
Acidic Beverages

Abstract This study evaluated gloss and color changes of esthetic restorative materials subjected to different acidic beverages. Specimens of resin composites (Z350XT (Z350), IPS Empress Direct (ED), Charisma Diamond (CD)) were prepared and the initial surface gloss and color (ΔE) were measured (n=10). Then, the specimens were immersed in 4 mL of each of the different beverages (cranberry juice; Coca-Cola; coffee or artificial saliva) during 15 min, 3x/day for 14 days and new gloss and color readings were obtained. Color change was evaluated with the ΔE formula and gloss change values were obtained by the formula: (final gloss - initial gloss). Data was submitted to two-way ANOVA followed by Tukey’s post hoc test (a=0.05). CD showed the lowest color change among resin composites. The highest ΔE values were obtained after immersion in coffee and cranberry juice. Coffee promoted the highest gloss change (worst gloss retention), followed by cranberry juice, Coca-cola and artificial saliva (p<0.05). The type of beverage significantly influenced the gloss of resin composites. Coca-cola reduced gloss of the three resin composites in a similar manner. Coffee affected the ED gloss more than that of Z350 and CD, while cranberry juice affected Z350 more than ED and CD. Saliva had a more pronounced effect on the gloss retention of CD than ED. The beverages used in this study influenced the optical surface properties of the composites studied.

The Effect of Bleaching Agents on the Color Stability of Ceromer and Porcelain Restorative Materials In Vitro

2012 ◽  
Vol 38 (1) ◽  
pp. E1-E8 ◽  
Author(s):  
HB Kara ◽  
F Aykent ◽  
B Ozturk
Keyword(s):  
Color Change ◽  
Glass Ceramics ◽  
In Vitro Study ◽  
Color Stability ◽  
Color Changes ◽  
Bleaching Procedure ◽  
Significant Difference ◽  
Restorative Materials ◽  
The Difference

SUMMARY Purpose The aim of this in vitro study was to determine the color changes of five different restorative materials after exposing these materials to two different home bleaching agents. Methods This study applied bleaching agents to an ultralow-fusing porcelain, a low-fusing porcelain, two types of heat-pressed glass ceramics, and a ceromer. A total of 24 disc-shaped specimens were fabricated (with a diameter of 10 mm and a thickness of 2 mm) from each material (n=12). The initial color measurements were taken with a spectrophotometer. The first set of specimens were bleached with 10% hydrogen peroxide (HP) for one hour daily for 10 days. The other set of specimens were bleached with 10% carbamide peroxide (CP) bleaching gel for eight hours daily for 14 days. Data were analyzed with the one-way analysis of variance and Kruskal-Wallis statistical test. The difference in the prebleaching and postbleaching color of each material was considered to be statistically significant at p &lt; 0.05. Results The study found a statistically significant difference among the color changes of the test groups after exposing them to both bleaching agents (p&lt;0.05). Appreciable color change was observed in the Estenia (ΔE=3.99) specimens that were bleached with the HP, and noticeable color changes were observed in the Estenia (ΔE=1.89) and IPS Empress 2 (ΔE=1.66) groups when they were treated with the CP. Conclusions Restorations (especially polymer-containing restorative materials) should be protected before any bleaching procedure due to the high risk of color change.

scholarly journals A Comparative Evaluation of Static Frictional Resistance Using Various Methods of Ligation at Different Time Intervals: An In Vitro Study

2015 ◽  
Vol 2015 ◽  
pp. 1-7 ◽  
Author(s):  
Amanpreet Singh Natt ◽  
Amandeep Kaur Sekhon ◽  
Sudhir Munjal ◽  
Rohit Duggal ◽  
Anup Holla ◽  
...  
Keyword(s):  
Stainless Steel ◽  
Artificial Saliva ◽  
In Vitro Study ◽  
Frictional Resistance ◽  
Static Friction ◽  
Significant Difference ◽  
Dry Conditions ◽  
The Mean ◽  
Time Periods

Aim. To compare and evaluate the static frictional resistance offered by the four different types of ligation methods in both dry and wet conditions and at different durations when immersed in artificial saliva.Material and Methods. Alastik Easy to Tie modules, Super Slick Mini Stix elastomeric modules, Power “O” modules, and 0.009″Stainless Steel ligatures were used to compare the static friction using maxillary canine and premolar Preadjusted Edgewise brackets with 0.022″× 0.028″slot and 0.019″× 0.025″stainless steel wires.Results. The mean frictional resistance for Alastik modules was the lowest and that of Stainless Steel ligatures was found to be highest among the four groups compared and the difference among the four groups was statistically significant (P<0.005). The mean static frictional resistance in all groups under dry conditions was lower than that under wet conditions. No statistical significant differences were found when the groups were compared at different time periods of immersion in artificial saliva.Conclusion. This study concludes that the Alastik modules showed the lowest mean static frictional forces compared to any other ligation method, though no significant difference was found for different time periods of immersion in the artificial saliva.

scholarly journals Evaluation of degradation of force of esthetic elastomeric chains

2019 ◽  
Vol 48 ◽  
Author(s):  
Mayra Teixeira Cortat LUCINDO ◽  
Diego Patrik Alves CARNEIRO ◽  
Felipe Alexandre de SOUZA ◽  
Américo Bortolazzo CORRER ◽  
Heloisa Cristina VALDRIGHI
Keyword(s):  
Repeated Measures ◽  
Artificial Saliva ◽  
In Vitro Study ◽  
Time Interval ◽  
Test Machine ◽  
Reduction In Force ◽  
Original Length ◽  
The Aesthetic ◽  
Elastomeric Chains

Abstract Introduction Elastomers are considered important allies to orthodontic treatment and due to the aesthetic demand, aesthetic elastomers are increasingly used in adult patients. Objective The aim of this experimental in vitro study was to evaluate the degradation of force of esthetic elastomeric chains, of three different sizes: short, medium and long. Material and method For evaluating the degradation of force, 90 elastomeric chain segments were used, divided into 9 Groups (n=10), as follows: Morelli short elastomer, Morelli medium, Morelli long, Orthometric short, Orthometric medium, Orthometric long, American Orthodontic short, American Orthodontic medium and American Orthodontic long. Acrylic plates with pins were used to provide stretching of the elastomeric chains. The initial stretching force of the elastomeric chain was 150 grams, measured by a tensiometer. After this, they were prestretched to 50% of their original length, measured in an Instron 4411 Universal test machine, and placed on the seating pin on the plate. The plate was immersed in artificial saliva at 37 °C in a plastic receptacle, and removed for measurement after a time interval of 21 days. For statistical analysis, the methodology of mixed models for repeated measures in time and Tukey-Kramer test were used. Degradation of the forces was analyzed by 2-way analysis of variance (ANOVA) and the Tukey test. Result All the elastomeric chains showed statistically significant reduction in force (p<0.05). The American Orthodontic elastomeric chains showed higher reduction in force values, irrespective of the elastic size (p<0.05). Conclusion The three commercial brands studied underwent significant reduction in the quantity of force released; the American Orthodontic brand of elastomer showed the highest value of degradation in force.

scholarly journals Evaluation of surface roughness and color change of bovine enamel after immersion in dye solution

2018 ◽  
Vol 5 (5) ◽  
pp. 95
Author(s):  
Ana Carolina Trentino ◽  
Larissa Marinho Azevedo ◽  
Felipe Fabrício Farias Da Silva ◽  
Maria Cristina Carvalho de Almedra Freitas ◽  
Marina Studart Alencar Borges ◽  
...  
Keyword(s):  
Hydrogen Peroxide ◽  
Surface Roughness ◽  
Color Change ◽  
Artificial Saliva ◽  
In Vitro Study ◽  
Black Tea ◽  
Control Group ◽  
Change Analysis ◽  
Miller Test

Aim: The aim of this in vitro study was to evaluate the influence of dye solution on enamel color change after bleaching protocols and the effectiveness in maintaining the color of these agents.Material and Methods: The buccal surfaces of sixty-five bovine incisors were cleaned and polished, and the enamel specimens were divided into thirteen groups: G1 to G6: treated with 6% hydrogen peroxide using different surface agents; G7 to G12: treated with 15% hydrogen peroxide using different surface agents; G13: control. After 24 hours, the groups treated were immersed in black tea solution; the control group was stored in artificial saliva. The color was evaluated prior to bleaching, 24 hours later and after immersion in the dye solution; the roughness was measured immediately after bleaching, 24 hours later and 7 days after immersion in the dye solution. The data was analyzed using the Kruskal-Wallis test, followed by the Miller test for roughness analysis, and the Duncan test for color change analysis. It was used 5% significant level with p<0.05.Results: The data found in the evaluation of surface roughness after bleaching indicated a reduction of roughness in all the groups. The surface agent Bifluoride, when applied, showed an increase in roughness after its application and it decreases after immersion in dye solution; the surface agent Desensibilize and the XP Bond adhesive showed greater color alteration after immersion in dye solution.Conclusions: All the groups studied, under different whitening technique, were effective in promoting whitening.

scholarly journals Influence of Prolonged Dental Bleaching on the Adhesive Bond Strength to Enamel Surfaces

2020 ◽  
Vol 2020 ◽  
pp. 1-9
Author(s):  
Juliana C. P. Baia ◽  
Roberta P. Oliveira ◽  
Mara E. S. Ribeiro ◽  
Rafael R. Lima ◽  
Sandro C. Loretto ◽  
...  
Keyword(s):  
Bond Strength ◽  
Artificial Saliva ◽  
In Vitro Study ◽  
Adhesive Bond ◽  
Dental Bleaching ◽  
The Moment ◽  
Post Hoc ◽  
Storage Times ◽  
Composite Cylinders

The objective of this in vitro study was to assess the influence of prolonged bleaching pre- and postrestoration on the bond strength (microshear) to enamel using 4% hydrogen peroxide (PH4). In the postrestorative bleached specimens evaluation, the composite cylinders were assembled after bleaching, while in the prebleached specimens, the cylinders were assembled before. Therefore, in the postbleached specimens, 60 bovine teeth were randomly assigned as follows: G1: control; G2: 14 days bleaching before bond strength (BS) testing; G3: 21 days; and G4: 28 days. In prebleached specimens, 180 bovine teeth were randomly assigned as follows: G1: control; G5: 14 days bleaching, storage in artificial saliva (AS) for 24 h before BS testing; G6: 14 days beaching, AS storage for 7 days before BS testing; G7: 21 days bleaching, AS storage for 24  h before BS testing; G8: 21 days bleaching, AS storage for 7 days before BS testing; G9: 28 days bleaching, AS storage for 24 hours before BS testing; and G10 : 28 days bleaching, AS storage for 7 days before BS testing. The results were submitted to ANOVA one-way (postrestoration bleaching) and two-way (prerestoration bleaching) and Tukey’s post hoc test (p≤0.05). In the postrestoration bleaching, no statistical difference between times was found. However, when bleached groups were compared to the control (G1), an expressive difference was detected (p≤0.0001). For prerestoration bleaching, all experimental groups were statistically different from G1 (p≤0.05), except G6 (p≥0.01), and for G5 and G6, statistical differences were found (p≤0.01). There were no significant differences between G7 and G8 and between G9 and G10, regardless of the AS storage times (p≥0.05). It was concluded that prolonged bleaching with PH4 decreased adhesion resistance regardless of the moment of the bleaching (post- and prerestoration bleaching).

Sign in / Sign up

Export Citation Format

Share Document