Fatigue Performance of Low Pressure Carbonitrided 20MnCr5 and SAE 8620 Steel Alloys

2021 ◽  
Author(s):  
Larissa Vilela Costa ◽  
Vincent Lelong ◽  
Dennis Beauchesne ◽  
Robert L. Cryderman ◽  
Kip O. Findley
Keyword(s):  
Retained Austenite ◽  
Prior Austenite ◽  
Endurance Limit ◽  
Fatigue Testing ◽  
Surface Hardness ◽  
Low Pressure ◽  
Austenite Grain Size ◽  
Steel Alloys ◽  
Austenite Grain ◽  
Prior Austenite Grain

Abstract Low pressure carbonitriding and pressurized gas quenching heat treatments were conducted on four steel alloys. Bending fatigue tests were performed, and the highest endurance limit was attained by 20MnCr5+B, followed by 20MnCr5, SAE 8620+Nb, and SAE 8620. The differences in fatigue endurance limit occurred despite similar case depths and surface hardness between alloys. Low magnitude tensile residual stresses were measured near the surface in all conditions. Additionally, nonmartensitic transformation products (NMTPs) were observed to various extents near the surface. However, there were no differences in retained austenite profiles, and retained austenite was mostly stable against deformation-induced transformation to martensite during fatigue testing, contrasting some studies on carburized steels. The results suggest that the observed difference in fatigue lives is due to differences in chemical composition and prior austenite grain size. Alloys containing B and Nb had refined prior austenite grain sizes compared to their counterparts in each alloy class.

Homology Analysis of Prior Austenite Grain Size of SAE52100 Bearing Steel Processed by Cyclic Heat Treatment

2013 ◽  
Vol 813 ◽  
pp. 116-119 ◽  
Author(s):  
Kazuaki Nakane ◽  
Katsuyuki Kida ◽  
Koshiro Mizobe
Keyword(s):  
Heat Treatment ◽  
Grain Size ◽  
Retained Austenite ◽  
Prior Austenite ◽  
Cyclic Heat Treatment ◽  
Austenite Grain Size ◽  
Austenite Grain ◽  
Cyclic Heat ◽  
Prior Austenite Grain Size ◽  
Prior Austenite Grain

Here, we introduce the mathematical methods to quantitatively evaluate the change of the tissue to quenching. SAE 52100 sample was repeatedly quenched and the influence of this cyclic heat treatment was investigated. The repeated quenching process increased the retained austenite content and had little influence on the materials hardness. The prior austenite grain size was decreased and consequently, refinement of the martensitic phase in the material occurred. The higher content of the retained austenite (higher fracture toughness) and the refinement of the microstructure accounted for the higher fatigue properties of the repeatedly quenched material. Here we use mathematical homology to quantify these features.

scholarly journals A New Systematic Approach Based on Dilatometric Analysis to Track Bainite Transformation Kinetics and the Influence of the Prior Austenite Grain Size

Metals ◽  
2021 ◽  
Vol 11 (2) ◽  
pp. 324
Author(s):  
David San-Martin ◽  
Matthias Kuntz ◽  
Francisca G. Caballero ◽  
Carlos Garcia-Mateo
Keyword(s):  
Heat Treatment ◽  
Grain Size ◽  
Prior Austenite ◽  
Bainitic Transformation ◽  
Transformation Rate ◽  
Transformation Kinetics ◽  
Austenite Grain Size ◽  
Austenite Grain ◽  
Prior Austenite Grain Size ◽  
Prior Austenite Grain

This investigation explores the influence of the austenitisation heat treatment and thus, of the prior austenite grain size (PAGS), on the kinetics of the bainitic transformation, using as A case study two high-carbon, high-silicon, bainitic steels isothermally transformed (TIso = 250, 300, 350 °C), after being austenised at different temperatures (γTγ = 925–1125 °C). A methodology, based on the three defining dilatometric parameters extracted from the derivative of the relative change in length, was proposed to analyse the transformation kinetics. These parameters are related to the time to start bainitic transformation, the time lapse for most of the transformation to take place and the transformation rate at the end of the transformation. The results show that increasing the PAGS up to 70 µm leads to an increase in the bainite nucleation rate, this effect being more pronounced for the lowest TIso. However, the overall transformation kinetics seems to be weakly affected by the applied heat treatment (γTγ and TIso). In one of the steels, PAGS > 70 µm (γTγ > 1050 °C), which weakly affects the progress of the transformation, except for TIso = 250 °C, for which the enhancement of the autocatalytic effect could be the reason behind an acceleration of the overall transformation.

scholarly journals Exploring the Difference in Bainite Transformation with Varying the Prior Austenite Grain Size in Low Carbon Steel

Metals ◽  
2018 ◽  
Vol 8 (12) ◽  
pp. 988 ◽  
Author(s):  
Liangyun Lan ◽  
Zhiyuan Chang ◽  
Penghui Fan
Keyword(s):  
Grain Size ◽  
Prior Austenite ◽  
Low Carbon Steel ◽  
Low Carbon ◽  
Bainite Transformation ◽  
Austenite Grain Size ◽  
Austenite Grain ◽  
Austenite Grains ◽  
Prior Austenite Grain Size ◽  
Prior Austenite Grain

The simulation welding thermal cycle technique was employed to generate different sizes of prior austenite grains. Dilatometry tests, in situ laser scanning confocal microscopy, and transmission electron microscopy were used to investigate the role of prior austenite grain size on bainite transformation in low carbon steel. The bainite start transformation (Bs) temperature was reduced by fine austenite grains (lowered by about 30 °C under the experimental conditions). Through careful microstructural observation, it can be found that, besides the Hall–Petch strengthening effect, the carbon segregation at the fine austenite grain boundaries is probably another factor that decreases the Bs temperature as a result of the increase in interfacial energy of nucleation. At the early stage of the transformation, the bainite laths nucleate near to the grain boundaries and grow in a “side-by-side” mode in fine austenite grains, whereas in coarse austenite grains, the sympathetic nucleation at the broad side of the pre-existing laths causes the distribution of bainitic ferrite packets to be interlocked.

Induction Hardening of a 0.40 % C Novel Microalloyed Steel: Effects of Heating Rate on the Prior Austenite Grain Size

2018 ◽  
Vol 941 ◽  
pp. 64-70
Author(s):  
Vahid Javaheri ◽  
Nasseh Khodaei ◽  
Tun Tun Nyo ◽  
David A. Porter
Keyword(s):  
Grain Size ◽  
Heating Rate ◽  
Prior Austenite ◽  
Induction Hardening ◽  
High Wear Resistance ◽  
Heating Rates ◽  
Austenite Grain Size ◽  
Austenite Grain ◽  
Prior Austenite Grain Size ◽  
Prior Austenite Grain

This work explores the effect of heating rate on the prior austenite grain size and hardness of a thermomechanically processed novel niobium-microalloyed 0.40 % carbon low-alloyed steel intended for use in induction hardened slurry pipelines. The aim was to identify the heating rates that lead to the maximum hardness, for high wear resistance, and minimum prior austenite grain size, for high toughness. For this purpose, a Gleeble 3800 machine has been employed to simulate the induction hardening process and provide dilatometric phase transformation data. The prior austenite grain structure has been reconstructed from the EBSD results using a MatlabR script supplemented with MTEX texture and crystallography analyses. Heating rates ranged from 1 to 50 °C/s and the cooling rate was 50 °C/s. The results show that the prior austenite grain size greatly depended on the heating rate: compared to the lower heating rates, the maximum heating rate of 50 C/s produces remarkably fine prior austenite grains and a fine final martensitic microstructure after quenching. In addition, a relation between the heating rate and the deviation from equilibrium temperature has been established.

Sign in / Sign up

Export Citation Format

Share Document