Experimental Study on Sustainable Concrete with the Mixture of Low Calcium Fly Ash and Lime as a Partial Replacement of Cement

2011 ◽  
Vol 250-253 ◽  
pp. 307-312 ◽  
Author(s):  
Muthuramalingam Jayakumar ◽  
M. Salman Abdullahi
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Water Absorption ◽  
Chloride Ion ◽  
Apparent Volume ◽  
Partial Replacement ◽  
Fly Ash Concrete ◽  
Low Calcium ◽  
Chloride Ion Penetration ◽  
Ion Penetration

Even though the use of fly ash in concrete is nowadays a common practice, its relatively slow pozzolanic reactivity hinders its greater utilization; hence efficient methods of activation are on demand. This study was carried out to evaluate the influence of lime as a chemical activator on the mechanical and durability properties of high strength fly ash concrete. Mixtures were made with 0, 30, 40, and 50% of cement replaced by low calcium fly ash. Corresponding mixtures were also made with the same amount of fly ash and addition of 10% of lime to each mixture. For each concrete mixture, slump, compressive strength, water absorption, sorptivity, apparent volume of permeable voids, and resistance to chloride-ion penetration were measured. The results obtained showed that addition of lime improved the compressive strength significantly at all ages. The strength of all the fly ash mixtures containing lime surpassed that of the corresponding Portland cement mix at 60 days. Addition of lime also improved the sorptivity and resistance to chloride-ion penetration of the fly ash concrete. It however increases the water absorption and the volume of permeable voids of the fly ash concrete.

scholarly journals Potential use of PET and PP as partial replacement of sand in structural concrete

2021 ◽  
Vol 26 (3) ◽  
Author(s):  
Priscila Marques Correa ◽  
Diego Guimarães ◽  
Ruth Marlene Campomanes Santana ◽  
Ângela Gaio Graeff
Keyword(s):  
Compressive Strength ◽  
Water Absorption ◽  
Elasticity Modulus ◽  
Chloride Ion ◽  
Morphological Properties ◽  
Partial Replacement ◽  
Chloride Ion Penetration ◽  
Mechanical Durability ◽  
Dsc Curves ◽  
Potential Use

ABSTRACT The use of polymeric residues in the civil construction has been the target of many studies aiming to reduce the volume of post-consumer plastics in the environment. This work focuses on the viability to use polyethylene terephthalate (PET) and polypropylene (PP) as partial replacement to sand in concrete. PET and PP flakes from post-consumer packings were used as light aggregate to partially replace, individually, 10% in volume of sand. The effect of adding these polymers was investigated in terms of physical, mechanical, durability and morphological properties of the concrete. Physical properties were measured in terms of water absorption, voids content and specific mass. Mechanical properties were measured in terms of compressive strength and elasticity modulus. Durability properties were measured in terms of capillarity water absorption and electrical indication of the concrete to resist to chloride ion penetration. MEV and EDS were used to carry out morphological analysis. DSC curves were carried out to evaluate thermal properties of the polymeric flakes. Contact anlge test was also performed. The partial addition of PET and PP polymers reduced the compressive strength by 20%, whilst the reduction of the elasticity modulus was 16% for PET samples, and almost insignificant for PP samples. The durability results show that the polymers contributed to increase the resistance of the samples to chloride penetration by 15% and 57%, for PET and PP samples, respectively; however, there was an increase in the voids content and water absorption. In the morphological test it is possible to observe a lower interfacial adhesion between PP and the cementions paste in comparison to PET.

scholarly journals Alkali-activated concretes based on fly ash and blast furnace slag: Compressive strength, water absorption and chloride permeability

2020 ◽  
Vol 40 (2) ◽  
Author(s):  
Daniela Eugenia Angulo-Ramírez ◽  
William Gustavo Valencia-Saavedra ◽  
Ruby Mejía de Gutiérrez
Keyword(s):  
Compressive Strength ◽  
Blast Furnace ◽  
Fly Ash ◽  
Water Absorption ◽  
Blast Furnace Slag ◽  
Construction Materials ◽  
Chloride Ion ◽  
Chloride Permeability ◽  
Alkaline Activator ◽  
Furnace Slag

Concretes based on alkaliactivated binders have attracted considerable attention as new alternative construction materials, which can substitute Portland Cement (OPC) in several applications. These binders are obtained through the chemical reaction between an alkaline activator and reactive aluminosilicate materials, also named precursors. Commonly used precursors are fly ash (FA), blast furnace slag (GBFS), and metakaolin. The present study evaluated properties such as compressive strength, rate of water absorption (sorptivity), and chloride permeability in two types of alkaliactivated concretes (AAC): FA/GBFS 80/20 and GBFS/OPC 80/20. OPC and GBFS/OPC* concretes without alkaliactivation were used as reference materials. The highest compressive strength was observed in the FA/GBFS concrete, which reported 26,1% greater strength compared to OPC concrete after 28 days of curing. The compressive strength of alkaliactivated FA/GBFS 80/20 and GBFS/OPC 80/20 was 61 MPa and 42 MPa at 360 days of curing, respectively. These AAC showed low permeability to the chloride ion and a reduced water absorption. It is concluded that these materials have suitable properties for various applications in the construction sector.

scholarly journals The Influence of Crystalline Admixtures on the Properties and Microstructure of Mortar Containing By-Products

Buildings ◽  
2020 ◽  
Vol 10 (9) ◽  
pp. 146
Author(s):  
Jakub Hodul ◽  
Nikol Žižková ◽  
Ruben Paul Borg
Keyword(s):  
Mechanical Properties ◽  
Fly Ash ◽  
Chloride Ion ◽  
Capillary Suction ◽  
Chloride Ion Penetration ◽  
Chloride Migration ◽  
Cement Mortars ◽  
Polymer Mortar ◽  
By Products ◽  
Ion Penetration

Crystalline admixtures and industrial by-products can be used in cement-based materials in order to improve their mechanical properties. The research examined long-term curing and the exposure to environmental actions of polymer–cement mortars with crystalline admixture (CA) and different by-products, including Bengħisa fly ash and Globigerina limestone waste filler. The by-products were introduced as a percentage replacement of the cement. A crystallization additive was also added to the mixtures in order to monitor the improvement in durability properties. The mechanical properties of the mortar were assessed, with 20% replacement of cement with fly ash resulting in the highest compressive strength after 540 days. The performance was analyzed with respect to various properties including permeable porosity, capillary suction, rapid chloride ion penetration and chloride migration coefficient. It was noted that the addition of fly ash and crystalline admixture significantly reduced the chloride ion penetration into the structure of the polymer cement mortar, resulting in improved durability. A microstructure investigation was conducted on the samples through Scanning Electron Microscopy-Energy Dispersive X-ray Spectroscopy (SEM-EDS). Crystals forming through the crystalline admixture in the porous structure of the material were clearly observed, contributing to the improved properties of the cement-based polymer mortar.

scholarly journals Effect of Vietnamese Fly Ash on Selected Physical Properties, Durability and Probability of Corrosion of Steel in Concrete

Materials ◽  
2019 ◽  
Vol 12 (4) ◽  
pp. 593 ◽  
Author(s):  
Chinh Van Nguyen ◽  
Paul Lambert ◽  
Quang Hung Tran
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Acid Resistance ◽  
Steel Corrosion ◽  
Strength Loss ◽  
Reinforced Concrete Beams ◽  
Partial Replacement ◽  
Nacl Solution ◽  
Fly Ash Concrete ◽  
Corrosion Of Steel

Vietnamese fly ash was used as a partial replacement for ordinary Portland cement in the proportions of 10%, 20% and 40%, while the water to cementitious ratios were kept constant at 0.42, 0.5 and 0.55, respectively, for three groups. The compressive strengths of all mixes were determined up to 90 days. The acid resistance of fly ash concrete was examined by the mass loss and compressive strength loss of 100 × 100 × 100 mm3 cubes immersed in a 10% H2SO4 solution. The probability of steel corrosion in the fly ash concrete was assessed by measuring the half-cell potentials of steel bars within beams dimensions of 100 × 100 × 500 mm3, and the flexural strengths of these beams after 300 days of immersion in a 5% NaCl solution were determined. The results demonstrate that the compressive strength of fly ash concrete is reduced at an early age but increases as the concrete continues to hydrate. The fly ash increases the sulfuric acid resistance of concrete. Fly ash additions have only a limited effect on reducing the risk of probability of corrosion of steel in the concrete. The load capacities of 10% and 20% fly ash reinforced concrete beams are higher than that of the control beams after 300 days immersed in a 5% NaCl solution.