Aluminum matrix composites (AMC) are of great interest and importance as high-performance materials with enhanced mechanical properties. Al2O3 is a commonly used reinforcement in AMCs fabricated by means of various technological methods, including casting and sintering. Selective laser melting (SLM) is a suitable modern method of the fabrication of net-shape fully dense parts from AMC with alumina. The main results, achievements, and difficulties of SLM applied to AMCs with alumina are discussed in this review and compared with conventional methods. It was shown that the initial powder preparation, namely the particle size distribution, sphericity, and thorough mixing, affected the final microstructure and properties of SLMed materials drastically. The distribution of reinforcing particles tends to consolidate the near-melting pool-edges process because of pushing by the liquid–solid interface during the solidification process that is a common problem of various fabrication methods. The achievement of an homogeneous distribution was shown to be possible through both the thorough mixing of the initial powders and the precise optimization of SLM parameters. The strength of the AMCs fabricated by the SLM method was relatively low compared with materials produced by conventional methods, while for superior relative densities of more than 99%, hardness and tribological properties were obtained, making SLM a promising method for the Al-based matrix composites with Al2O3.
EFFECT OF SOLUTIONISING TIME ON MECHANICAL PROPERTIES OF SQUEEZE CASTED AL 6082 – SICP COMPOSITE