scholarly journals Influence of Additives on the Fatigue Life and Stiffness of Asphalt Concrete

2021 ◽  
pp. 8-15
Author(s):  
Saad I. Sarsam
Keyword(s):  
Fatigue Life ◽  
Fly Ash ◽  
Asphalt Concrete ◽  
Concrete Beam ◽  
Asphalt Binder ◽  
Flexural Stiffness ◽  
Beam Test ◽  
Modified Asphalt ◽  
Wet Process ◽  
Modified Binder

Implementation of additives to the asphalt binder can enhance the overall physical properties of the modified asphalt concrete. In the present assessment, an attempt has been made to use 2 % of silica fumes and 4 % of fly ash class F for modification of asphalt binder in wet process. Asphalt concrete wearing course mixtures have been prepared and compacted by roller in the laboratory. The beam specimens of 400 mm length and 50 mm height and 63 mm width were extracted from the slab samples. The specimens were subjected to the four-point repeated flexural bending beam test. The flexural stiffness was calculated under three constant micro strain levels of (250, 400, and 750). The fatigue life was monitored in terms the number of load repetitions to reach the required reduction in stiffness. It was concluded that the flexural stiffness increases by (11, and 15) %, (17.7, and 63.6) %, (57.2, and 65) % when 2% of silica fumes or 4 % of fly ash are implemented and the specimen’s practices 750, 400, and 250 microstrain levels respectively. However, the fatigue life of asphalt concrete beam specimens increases by (40, and 72.8) %, (115, and 220.6) %, (46, and 94.6) % when 2% of silica fumes or 4 % of fly ash are implemented and the specimen’s practices 750, 400, and 250 microstrain levels respectively. It is recommended to use modified binder with fly ash and silica fumes in asphalt concrete to enhance the fatigue life and stiffness.

scholarly journals Assessment of Fatigue Life and Stiffness of Asphalt Concrete After Implementation of Additives

2021 ◽  
Vol 2 (4) ◽  
pp. 8-12
Author(s):  
Saad Issa Sarsam
Keyword(s):  
Fatigue Life ◽  
Fly Ash ◽  
Physical Properties ◽  
Asphalt Concrete ◽  
Asphalt Binder ◽  
Roller Compaction ◽  
Flexural Stiffness ◽  
Beam Test ◽  
Wet Process ◽  
Modified Binder

Modifying asphalt binder with additives can enhance the overall physical properties of asphalt concrete. In the present investigation, an attempt has been made to use 2 % of silica fumes and 4 % of fly ash class F for modification of asphalt binder in wet process. Asphalt concrete wearing course slab samples have been prepared under roller compaction. The beam specimens of 400 mm length and 50 mm height and 63 mm width were extracted from the slab samples. The beam specimens were subjected to the four-point repeated flexural bending beam test. The flexural stiffness was calculated under three constant micro strain levels of (250, 400, and 750). The fatigue life was monitored in terms the number of load repetitions to reach the required reduction in stiffness of 50 %. It was concluded that the flexural stiffness increases by (11, and 15) %, (17.7, and 63.6) %, (57.2, and 65) % when 2% of silica fumes or 4 % of fly ash are implemented and the specimen’s practices 750, 400, and 250 micro strain levels respectively. However, the fatigue life increases by (40, and 72.8) %, (115, and 220.6) %, (46, and 94.6) % when 2% of silica fumes or 4 % of fly ash are implemented and the specimen’s practices 750, 400, and 250 micro strain levels respectively. It is recommended to use modified binder with silica fumes and fly ash in asphalt concrete to enhance the fatigue life and stiffness.

scholarly journals Impact of Graphene Oxide on Zero Shear Viscosity, Fatigue Life and Low-Temperature Properties of Asphalt Binder

Materials ◽  
2021 ◽  
Vol 14 (11) ◽  
pp. 3073
Author(s):  
Abbas Mukhtar Adnan ◽  
Chaofeng Lü ◽  
Xue Luo ◽  
Jinchang Wang
Keyword(s):  
Graphene Oxide ◽  
Fatigue Life ◽  
Low Temperature ◽  
Shear Viscosity ◽  
Storage Stability ◽  
Asphalt Binder ◽  
Asphalt Binders ◽  
Test Results ◽  
Zero Shear Viscosity ◽  
Modified Asphalt

This study has investigated the impact of graphene oxide (GO) in enhancing the performance properties of an asphalt binder. The control asphalt binder (60/70 PEN) was blended with GO in contents of 0%, 0.5%, 1%, 1.5%, 2%, and 2.5%. The permanent deformation behavior of the modified asphalt binders was evaluated based on the zero shear viscosity (ZSV) parameter through a steady shear test approach. Superpave fatigue test and the linear amplitude sweep (LAS) method were used to evaluate the fatigue behavior of the binders. A bending beam rheometer (BBR) test was conducted to evaluate the low-temperature cracking behavior. Furthermore, the storage stability of the binders was investigated using a separation test. The results of the ZSV test showed that GO considerably enhanced the steady shear viscosity and ZSV value, showing a significant contribution of the GO to the deformation resistance; moreover, GO modification changed the asphalt binder’s behavior from Newtonian to shear-thinning flow. A notable improvement in fatigue life was observed with the addition of GO to the binder based on the LAS test results and Superpave fatigue parameter. The BBR test results revealed that compared to the control asphalt, the GO-modified binders showed lower creep stiffness (S) and higher creep rate (m-value), indicating increased cracking resistance at low temperatures. Finally, the GO-modified asphalt binders exhibited good storage stability under high temperatures.

scholarly journals Investigation of the Effect of Induction Heating on Asphalt Binder Aging in Steel Fibers Modified Asphalt Concrete

Materials ◽  
2019 ◽  
Vol 12 (7) ◽  
pp. 1067 ◽  
Author(s):  
Hechuan Li ◽  
Jianying Yu ◽  
Shaopeng Wu ◽  
Quantao Liu ◽  
Yuanyuan Li ◽  
...  
Keyword(s):  
Induction Heating ◽  
Asphalt Concrete ◽  
Asphalt Binder ◽  
Steel Fibers ◽  
Asphalt Binders ◽  
Carbonyl Index ◽  
Modified Asphalt ◽  
Concrete Damage ◽  
The Difference ◽  
Binder Aging

Induction heating is a valuable technology to repair asphalt concrete damage inside. However, in the process of induction heating, induced particles will release a large amount of heat to act on asphalt binder in a short time. The purpose of this paper was to study the effect of induction heating on asphalt binder aging in steel fibers modified asphalt concrete. The experiments were divided into two parts: induction heating of Dramix steel fibers coated with asphalt binder (DA) and steel wool fibers modified asphalt concrete. After induction heating, the asphalt binders in the samples were extracted for testing aging indices with Fourier Transform Infrared (FTIR), Dynamic Shear Rheometer (DSR), and Four-Components Analysis (FCA) tests. The aging of asphalt binder was analyzed identifying the change of chemical structure, the diversification of rheological properties, and the difference of component. The experiments showed that the binder inside asphalt concrete began aging during induction heating due to thermal oxygen reaction and volatilization of light components. However, there was no peak value of the carbonyl index after induction heating of ten cycles, and the carbonyl index of DA was equivalent to that of binder in asphalt concrete after three induction heating cycles, which indicated the relatively closed environment inside asphalt concrete can inhibit the occurrence of the aging reaction.

RHEOLOGICAL BEHAVIOUR OF COCONUT SHELL POWDER MODIFIED ASPHALT BINDER

2016 ◽  
Vol 78 (7-3) ◽  
Author(s):  
Rosnawati Buhari ◽  
Nur Fareesya Zabidi ◽  
Mohd Ezree Abdullah ◽  
Siti Khatijah Abu Bakar ◽  
Nurul Hidayah Mohd Kamarudin
Keyword(s):  
Rheological Properties ◽  
Softening Point ◽  
Asphalt Binder ◽  
Rheological Behaviour ◽  
Coconut Shell ◽  
Modified Asphalt ◽  
Modified Asphalt Binder ◽  
Modified Binder ◽  
Coconut Shell Powder ◽  
Shell Powder

The objectives of this study were to determine the blending parameters of coconut shell powder (CSP) modified asphalt binder and to evaluate the rheological properties of CSP modified asphalt binder. CSP of 2%, 4%, 6%, 8% and 10% by weight of asphalt have been incorporated into an unaged 80/100 asphalt mix in order to improve its performance. The influence of the additives on the physical and rheological properties was evaluated with penetration test, softening point, storage stability, dynamic shear rheometer test (DSR), and Field Emission Scanning Electron Microscope (FESEM). The aging of asphalt binders was simulated in a laboratory by using Rotational Thin Film Oven (RTFO). The results showed that the addition of CSP into virgin binder was decreasing the penetration value and increasing the softening point temperature compared to the original binder. On the rheological effect, for unaged modified binder, higher CSP resulted higher G*/sin δ especially at lower temperature compared to the unaged control binder. Besides, for the aged modified binder, stiffness was lower than the control aged binder for all temperature.

Recycled Polyethylene Modified Asphalt Binders and Mixtures: Performance Characteristics and Environmental Impact

2022 ◽  
pp. 036119812110657
Author(s):  
Ibrahim A. Abdalfattah ◽  
Walaa S. Mogawer ◽  
Kevin D. Stuart
Keyword(s):  
Asphalt Binder ◽  
Asphalt Mixture ◽  
Asphalt Mixtures ◽  
Asphalt Binders ◽  
Dry Process ◽  
Modified Asphalt ◽  
Wet Process ◽  
Melted Snow ◽  
Recycled Polyethylene ◽  
Asphalt Paving

This study addresses the effects of recycled polyethylene (RPE) on the performances of both asphalt binders and asphalt mixtures. Whether using RPE in an asphalt mixture might leach harmful chemicals into rainwater or melted snow was also determined. Two processes, wet and dry, were used to formulate the RPE modified asphalt binders and mixtures. In the wet process, RPE was added to asphalt binder. In the dry process, it was added to heated aggregates. RPE from two sources and PG 64-22 virgin asphalt binders from two sources were used in this study. In conclusion, RPE improved the rutting resistance of the asphalt binders and asphalt mixtures. However, it had adverse effects on their resistance to intermediate-temperature and non-load associated cracking. The dry process could produce a mixture with a higher RPE dosage compared with the wet process using one virgin asphalt binder but not the other; thus, the virgin asphalt binder source was a significant factor for the dry process. Based on an embryotoxicity test, it was found that RPE can be used by the asphalt paving industry without creating any significant environmental risks.

High-temperature performance of gilsonite-modified asphalt binder and asphalt concrete

2016 ◽  
Vol 34 (21) ◽  
pp. 1783-1789 ◽  
Author(s):  
Aliasghar Akbari Nasrekani ◽  
Koorosh Naderi ◽  
Mostafa Nakhaei ◽  
Nader Mahmoodinia
Keyword(s):  
High Temperature ◽  
Asphalt Concrete ◽  
Asphalt Binder ◽  
Modified Asphalt ◽  
Temperature Performance ◽  
Modified Asphalt Binder

PHYSICAL PROPERTIES AND STORAGE STABILITY OF GEOPOLYMER MODIFIED ASPHALT BINDER

2016 ◽  
Vol 78 (7-2) ◽  
Author(s):  
Ahmad Nazrul Hakimi Ibrahim ◽  
Nur Izzi Md. Yusoff ◽  
Norliza Mohd Akhir ◽  
Muhamad Nazri Borhan
Keyword(s):  
Physical Properties ◽  
Storage Stability ◽  
Permanent Deformation ◽  
Asphalt Binder ◽  
Asphalt Binders ◽  
Modified Asphalt ◽  
Modified Asphalt Binder ◽  
Potential Alternative ◽  
Modified Binder ◽  
And Storage

This study was conducted to investigate the physical properties and storage stability of the 80/100 penetration grade asphalt modified with geopolymer. In this research, fly ash and alkali activators, namely sodium silicate (Na2SiO3) and sodium hydroxide (NaOH), were used as geopolymer components. The penetration, Ring and Ball softening point, ductility, and viscosity tests were conducted to determine the physical properties of geopolymer modified asphalt (GMA). Five samples of asphalt binders with varying percentages of geopolymer, namely 0, 3, 5, 7 and 9%, by weight of asphalt binder were studied. Results show that geopolymer has good compatibility with asphalt binder. The addition of geopolymer into asphalt binder resulted in improved permanent deformation resistance of the modified binder compared to that of the conventional asphalt. In conclusion, geopolymer could be considered as a potential alternative in the modification of the properties of asphalt binder.

Evaluation of Permanent Deformation of BRA Modified Asphalt Paving Mixtures Based on Dynamic Creep Test Analysis

2016 ◽  
Vol 16 ◽  
pp. 69-81 ◽  
Author(s):  
Muhammad Karami ◽  
Ainalem Nega ◽  
Ahdyeh Mosadegh ◽  
Hamid Nikraz
Keyword(s):  
Creep Test ◽  
Permanent Deformation ◽  
Asphalt Binder ◽  
Asphalt Mixture ◽  
Asphalt Mixtures ◽  
Modified Asphalt ◽  
Nominal Size ◽  
Dynamic Creep ◽  
Asphalt Paving ◽  
Modified Binder

The main objective this study is to evaluate the permanent deformation of buton rock asphalt (BRA) modified asphalt paving mixtures using dynamic creep test so that long term deformation behavior of asphalt mixtures can be characterized. The dynamic creep test was conducted on unmodified and BRA modified asphalt mixture using UTM25 machine. Asphalt cement of C170 from a regional supplier in Western Australia was used as the base asphalt binder for unmodified asphalt mixture; and BRA modified asphalt mixtures were made by substituting the base asphalt with 10, 20, and 30% (by weight of total asphalt binder) natural binder continuing granular BRA modified binder. The granular (pellets) BRA modified binder with a diameter of 7-10 mm was produced and extracted according the Australia Standard. Crushed granite was taken from a local quarry of the region; and dense graded for both unmodified and BRA modified asphalt mixture with the nominal size of 10 mm was used. The results of this analysis showed that BRA modified had a good performance as compared with unmodified asphalt mixtures, and increase in the content modified binder to 10%, 20%, and 30% resulted in decrease of the total permanent strain.

Sign in / Sign up

Export Citation Format

Share Document