Mitigation of BPD by Pre-Epigrowth High Temperature Substrate Annealing

Basal Plane Dislocations (BPD) intersecting the SiC substrate surface were converted to threading edge dislocations (TED) by high temperature annealing of the substrates in the temperature range of 1750 °C – 1950 °C. Successively, epitaxial growth on annealed as well as non-annealed samples was performed, concurrently, to investigate the effect of the substrate annealing on BPD mitigation in the epilayers. For the 1950 °C/10min anneal, a 3x reduction in BPD density was observed. Additionally, surface roughness measured using atomic force microscopy revealed no degradation in surface morphology of the grown epilayers after annealing.