Effect of Heat Treatment on the Physic-Mechanical Characteristics of Eucalyptusurophylla S.T. Blake

Eucalyptus plantations wood have great potential application in high quality solid wood product. In order to improve the overall characteristics, heat treatments (HT) were carried out using Eucalyptus urophylla S.T. Blake wood at 150, 170 and 190 °C, for 2 and 4 h, separately. The effects of HT on physical and mechanical properties, wood color, dimensional stability and chemical change were investigated. The results indicate that: Mass loss (ML) of wood at a moderate temperature of 150 °C was small, but increased remarkably when temperature exceeds 170 °C. A maximum ML of 5.83% was observed at 190 °C/4 h; the velocity of water vapor adsorption and equilibrium moisture content (EMC) of HT wood decreased significantly, and varied considerably with treating severity; absolute dry density of HT wood decreased, presenting a similar tendency with ML, but the reduction was greater than ML; HT reduced the tangential and radial swelling ratio and swelling coefficients of wood, and improved the dimensional stability by 71.88% at 190 °C; modulus of rupture (MOR) and modulus of elasticity (MOE) of HT wood varied significantly in severer conditions, but there were no obvious changes in a moderate conditions at 150 °C; there was a slight color change at 150 °C, but wood color became more dark and uniform with treating severity; HT decreased the relative content of hydroxyl groups in wood components, improving wood dimensional stability. Color change of wood may be caused by variations of chromophoric groups and its own structure of lignin due to HT. Moderate temperature HT at 150 °C improved dimensional stability and color uniform of wood, but without reducing mechanical stress. This is a practical HT condition for Eucalyptus urophylla S.T. Blake.

Large-Area Fabrication of Structurally Colored and Humidity Sensitive Composite Nanofilm via Ultrasonic Spray-Coating

Intelligent structural colors have received extensive attention in recent years due to their diverse applications. However, the large-area, uniform, and cost-effective fabrication of ultra-thin structural color films is still challenging. Here, for the first time, we design and employ an ultrasonic spray-coating technique with non-toxic, green nano-silica and polyvinylpyrrolidone as raw materials, to prepare structural color films on silicon wafers. Due to the addition of polyvinylpyrrolidone, the coffee-ring effect during droplet drying is suppressed and uniform composite films are formed. We further perform a detailed study of the influence of various processing parameters including silica/polyvinylpyrrolidone concentration, substrate temperature, nozzle-to-substrate distance, and number of spray-passes on film roughness and thickness. By increasing the number of spray-passes from 10 to 30, the film thickness from 120 to 340 nm is modulated, resulting in different colors, and large-area and uniform colors on commercial round silicon wafers with 15 cm diameter are achieved. The silica/polyvinylpyrrolidone composite films show strong hydrophilicity and are sensitive to humidity changes, leading to quickly tunable and reversible structural colors. Quartz crystal microbalance with dissipation demonstrates water vapor adsorption and condensation on the nanofilm when increasing environmental humidity. Thereby, ultrasonic spray-coating as a novel film fabrication technique provides a feasible scheme for large-area preparation of intelligent structural colors.

Polyaniline/Biopolymer Composite Systems for Humidity Sensor Applications: A Review

The development of polyaniline (PANI)/biomaterial composites as humidity sensor materials represents an emerging area of advanced materials with promising applications. The increasing attention to biopolymer materials as desiccants for humidity sensor components can be explained by their sustainability and propensity to absorb water. This review represents a literature survey, covering the last decade, which is focused on the interrelationship between the core properties and moisture responsiveness of multicomponent polymer/biomaterial composites. This contribution provides an overview of humidity-sensing materials and the corresponding sensors that emphasize the resistive (impedance) type of PANI devices. The key physicochemical properties that affect moisture sensitivity include the following: swelling, water vapor adsorption capacity, porosity, electrical conductivity, and enthalpies of adsorption and vaporization. Some key features of humidity-sensing materials involve the response time, recovery time, and hysteresis error. This work presents a discussion on various types of humidity-responsive composite materials that contain PANI and biopolymers, such as cellulose, chitosan and structurally related systems, along with a brief overview of carbonaceous and ceramic materials. The effect of additive components, such as polyvinyl alcohol (PVA), for film fabrication and their adsorption properties are also discussed. The mechanisms of hydration and proton transfer, as well as the relationship with conductivity is discussed. The literature survey on hydration reveals that the textural properties (surface area and pore structure) of a material, along with the hydrophile–lipophile balance (HLB) play a crucial role. The role of HLB is important in PANI/biopolymer materials for understanding hydration phenomena and hydrophobic effects. Fundamental aspects of hydration studies that are relevant to humidity sensor materials are reviewed. The experimental design of humidity sensor materials is described, and their relevant physicochemical characterization methods are covered, along with some perspectives on future directions in research on PANI-based humidity sensors.