High-Performance of a Thick-Walled Polyamide Composite Produced by Microcellular Injection Molding

Lightweight moldings obtained by microcellular injection molding (MIM) are of great significance for saving materials and reducing energy consumption. For thick-walled parts, the standard injection molding process brings some defects, including a sink mark, warpage, and high shrinkage. Polyamide 66 (PA66)/glass fiber (GF) thick-walled moldings were prepared by MuCell® technology. The influences of moldings thickness (6 and 8.4 mm) and applied nitrogen pressure (16 and 20 MPa) on the morphology and mechanical properties were studied. Finally, the microcellular structure with a small cell diameter of about 30 μm was confirmed. Despite a significant time reduction of the holding phase (to 0.3 s), high-performance PA66 GF30 foamed moldings without sink marks and warpage were obtained. The excellent strength properties and favorable impact resistance while reducing the weight of thick-walled moldings were achieved. The main reason for the good results of polyamide composite was the orientation of the fibers in the flow direction and the large number of small nitrogen cells in the core and transition zone. The structure gradient was analysed and confirmed with scanning electron microscopy (SEM) images, X-ray micro computed tomography (micro CT) and finite element method (FEM) simulation.

Using P(Pressure)-T(Temperature) Path to Control the Foaming Cell Sizes in Microcellular Injection Molding Process

Microcellular injection molding technology (MuCell) using supercritical fluid (SCF) as a foaming agent is one of the important green molding solutions for reducing the part weight, saving cycle time, and molding energy, and improving dimensional stability. In view of the environmental issues, the successful application of MuCell is becoming increasingly important. However, the molding process encounters difficulties including the sliver flow marks on the surface and unstable mechanical properties that are caused by the uneven foaming cell sizes within the part. In our previous studies, gas counter-pressure combined with dynamic molding temperature control was observed to be an effective and promising way of improving product quality. In this study, we extend this concept by incorporating additional parameters, such as gas pressure holding time and release time, and taking the mold cooling speed into account to form a P(pressure)-T(temperature) path in the SCF PT diagram. This study demonstrates the successful control of foaming cell size and uniformity in size distribution in microcellular injection molding of polystyrene (PS). A preliminary study in the molding of elastomer thermoplastic polyurethanes (TPU) using the P-T path also shows promising results.

The Microcellular Structure of Injection Molded Thick-Walled Parts as Observed by In-Line Monitoring

The aim of the study was to detect the influence of nitrogen pressure on the rheological properties and structure of PA66 GF30 thick-walled parts, produced by means of microcellular injection molding (MIM), using the MuCell® technology. The process was monitored in-line with pressure and temperature sensors assembled in the original injection mold. The measured data was subsequently used to evaluate rheological properties inside an 8.4 mm depth mold cavity. The analysis of the microcellular structure was related to the monitored in-line pressure and temperature changes during the injection process cycle. A four-times reduction of the maximum filling pressure in the mold cavity for MIM was found. At the same time, the holding pressure was taken over by expanding cells. The gradient effect of the cells distribution and the fiber arrangement in the flow direction were observed. A slight influence of nitrogen pressure on the cells size was found. Cells with a diameter lower than 20 µm dominate in the analyzed cases. An effect of reduction of the average cells size in the function of distance to the gate was observed. The creation of structure gradient and changes of cells dimensions were evaluated by SEM images and confirmed with the micro CT analysis.