High efficiency slime water settlement is very important for ensuring washing water recycling in coal preparation plants. In order to improve the sedimentation of coal slime water, an iron ion-based coagulant was prepared by titanium ion complexation action using titanium sulfate as a main raw material, Fe3+ and NaH2PO3 as a stabilizer and NaHCO3 as an alkalizing agent. The particle size distribution of coal slime was measured, and the sedimentation test for coal slime water was carried out with PAM, polyaluminum chloride and polymerized titanium ferric sulfate (PTFS), respectively. Then, coal slime water sedimentation was investigated at different PAM dosages and polyaluminum chloride or coal slime water of PTFS with various molar ratios of PAM and ferrotitanium. The results showed that PAM and polyaluminum chloride could not make coal slime settle down, and PTFS showed a poor settlement effect. When polyaluminum chloride and PTFS were used together with PAM, it produced a molecular weight of 3 million respectively. Polyaluminum chloride needs 6.66 × 10−10 mol of PAM, PTFS needs 0.66 × 10−10 mol of PAM and the effect of sedimentation is improved. When the molar ratio of PTFS was 1:7, polymerization performance was effective. The sedimentation effect of PTFS was better than that of polymeric aluminum chloride coagulant usually used in coal preparation plants, especially when combined with flocculant, and high efficiency was reached. The surface potential and surface free energy of coal slime particles before and after adding coagulant were measured and analyzed by XDLVO theory to explain the action mechanism of PTFS coagulant. Experimental results demonstrated that PTFS can significantly improve the sedimentation of coal slime water, save the dosage of PAM and increase economic benefit.
Effect of the Polymerized Titanium Ferric Sulfate (PTFS) Coagulant on Sedimentation of Coal Slime Water