ABSTRACTWith extremely disordered atomic structures, a glass possesses a thermal conductivity k that approaches the theoretical minimum of its composition, known as the Einstein’s limit.1 Depending on the material composition and the extent of disorder, the thermal conductivity of some glasses can be down to 0.1-0.3 W/m∙K at room temperature,2,3 representing some of the lowest k values among existing solids. Such a low k can be further reduced by the interfacial phonon scattering within a nanocomposite that can be used for thermal insulation applications. In this work, nanocomposites hot pressed from the mixture of glass nanopowder (GeSe4 or Ge20Te70Se10) and commercial SiO2 nanoparticles, or pure glass nanopowder, are investigated for the potential k reduction. It is found that adding SiO2 nanoparticles will instead increase k if the measured k values for usually porous nanocomposites are converted into those for the corresponding solid (kSolid) with Eucken’s formula. In contrast, pure glass nano-samples always show kSolid data significantly reduced from that for the starting glass. For a pure GeSe4 nano-sample, kSolid would beat the Einstein’s limit for its composition.
Rigid Polyurethane Foams Modified with Biochar