A nonlinear ultrasonic modulation approach for the detection and localisation of contact defects

Abstract This article reports the microstructure evolution in TP347HFG austenitic steel during the aging process. The experiments were carried out at 700°C with different aging time from 500 to 3,650 h. The metallographic results show that the coherent twin and incoherent twin are existed in the original TP347HFG grains, while they gradually vanished with the increase of the aging time. After aging for 500 h, a lot of fine, dispersed particles precipitated from the matrix, but they disappeared after aging for 1,500 h. When the aging time extend to 3,650 h, the precipitates appeared apparently coarse in TP347HFG steel, which include the M23C6 and σ phase; besides, the micro-hardness of TP347HFG also changes during the aging, which was closely related to the effect of dispersion strengthening and solution strengthening. The results of the nonlinear ultrasonic measurement reveal that the β′ of TP347HFG steel was also changed with the aging time. It first increased at 0–500 h, then reduced later, and increased finally at 1,500–3,650 h. The variation of β′ in TP347HFG was influenced by a combined effect of the twin microstructure and the precipitate phase, which indicate that the nonlinear ultrasonic technique can be utilized to characterize the microstructure evolution in TP347HFG.

Download Full-text

Evaluation of Damage Process of a Coating by Using Nonlinear Ultrasonic Method

Coatings ◽

10.3390/coatings11040440 ◽

2021 ◽

Vol 11 (4) ◽

pp. 440

Author(s):

Chunguang Xu ◽

Lei He ◽

Shiyuan Zhou ◽

Dingguo Xiao ◽

Pengzhi Ma

Keyword(s):

Tensile Stress ◽

Order Parameter ◽

Evaluation Method ◽

Early Stage ◽

Ultrasonic Method ◽

Nonlinear Coefficient ◽

Damage Index ◽

Second Order ◽

External Loading ◽

Nonlinear Ultrasonic

During the service or external loading of the surface coating, the damage accumulation may develop in the coating or at the interface between the substrate and the coating, but it is difficult to measure directly in the early stage, so the acoustic nonlinear parameters are used as the early damage index of the coating. In this paper, the nonlinear wave motion equation is solved by the perturbation method and the new relationship between the relative ratio of second-order parameter and third-order parameter was derived. The nonlinear ultrasonic testing system is used to detect received signals during tensile testing of for the specimen with Al2O3 coatings. It is found that when the stress is less than 260 MPa, the appearance of the coating has no obvious change, but the nonlinear coefficients measured by the experiment increase with the increase of the tensile stress. By comparing the curves of nonlinear coefficients and stress respectively, the fluctuation of curves the second-order nonlinear coefficient A2 and the relative nonlinear coefficient β′ to stress is relatively small, and close to the linear relationship with the tensile stress, which indicates that the two parameters of the specimen with Al2O3 coatings are more sensitive to the bonding conditions, and can be used as an evaluation method to track the coating damage.