AbstractA film of Sr0.35Ba0.65TiO3 (SBT) has been grown in situ by pulsed laser deposition on (001) LaAlO3 single crystal. From X-ray diffraction studies the sample is found to be in single phase and well oriented. Raman spectrum of the SBT film shows bands around 178, 219, 296, 513, 571 and 741 cm”. The spectrum is similar to that found in SBT ceramic material, but the frequencies of the phonons are shifted. This can be explained if the film is under stress due to the presence of defects. The bands at 296 and 741cm−1 correspond to the B1 and A1(LO) normal modes of the BaTiO3 (BT) system, and they are representative of the BT tetragonal phase, which at first glance appears to contradict earlier structural symmetry assignment for SBT(x=0.35) film at room temperature. Micro-Raman measurements from different regions of the film indicate that the SBT film is homogeneous. The bands at 296 and 741 cm−1 are broader in comparison to those in BT single crystal and SBT ceramic material. Temperature dependent halfwidths of these modes suggest strong contribution of defects. Temperature dependent results are discussed in terms of anharmonic contributions involving three and four phonon processes as well as defects. Also, the orthorhombic and rhombohedral phase transitions are discussed. Finally, SEM/EDAX and FT-IR techniques have been used for the structural characterization.